Otrzymywanie i właściwości termoelektryczne CoSb3 typu p i n

100%

Wojciechowski K. T. , Leszczyński J.

|

tom Vol. 46, nr 2-3

35-36

PL

Opisano otrzymywanie polikrystalicznych próbek CoSb₃ typu p i n domieszkowanego Sn i Te. Wykonano badania strukturalne, analizę składu oraz pomiary właściwości termoelektrycznych. Określono optymalne zawartości domieszek w celu uzyskania maksymalnej wartości współczynnika etektywności termoelektrycznej ZT.

EN

Polycrystalline p and n doped CoSb₃ materials with various contents of Sn and Te have been obtained. Structural, phase analysis and thermoelectric properties have been investigated. Optimal contents of impurities for maximum figure of merit ZT have been determined.

2

Zastosowanie metody 3-ω do pomiaru przewodnictwa cieplnego materiałów litych oraz warstw

80%

Wojciechowski K. T. , Mania R. , Mars K. , Zybała R.

|

tom Vol. 48, nr 10

61-63

PL

Technologie mikroelektroniczne wymagają opracowania metod pomiaru przewodnictwa cieplnego materiałów otrzymywanych w postaci cienkich warstw nanoszonych na metaliczne lub ceramiczna podłoża. Metoda 3-omega pozwala na wykonanie dokładnych pomiarów przewodnictwa cieplnego materiałów litych oraz warstw w kierunku prostopadłym do podłoża. Opisano opracowaną metodę oraz układ pomiarowy. Metoda została sprawdzona na różnego typu materiałach monokrystalicznych, polikrystalicznych oraz warstwach w zakresie przewodnictwa cieplnego 0,2...140 Wm-1K-1.

EN

Technology in microelectronics requires the development of methods of measuring thermal conductivities of materials in the form of films deposited on the substrate. The 3-omega provides accurate measurements of values of thermal conductivity of bulk materials and films in normal-to-plane direction. The paper describes developed method and experimental setup. The method was successfully verified on various polycrystalline materials, single crystals and layers over the thermal conductivity range from 0.2 to 140 Wm-1 K-1.

3

DLC layers prepared by the PVD magnetron sputtering technique

80%

Wojciechowski K. T. , Zybala R. , Mania R. , Morgiel J.

Journal of Achievements in Materials and Manufacturing Engineering

|

2009

|

tom Vol. 37, nr 2

726-729

EN

magnetron sputtering technique. Design/methodology/approach: DLC layers were fabricated by the reactive pulsed magnetron sputtering method in the mixture of Ar and methane (CH4). The gas pressure during sputtering process ranged from 0.3 to 0.7 Pa. The DLC layers were deposited on selected thermoelectric, ceramic and metallic substrates. Microstructure of obtained DLC layers were characterised by TEM and SEM microscopy. Raman spectroscopy was also used to characterise the different forms of carbon in the films. Findings: Structural investigations showed amorphous character of the produced layers and the lack of presence of nano-crystalline diamond phase both in layers obtained at 35 °C and in higher temperatures. Raman spectroscopy studies confirmed the dominant share of sp2 hybridization in the C - C and the presence of C – H bonds. Obtained layers are characterized by high electrical resistivity. Practical implications: Microstructure and high resistivity of DLC layers, prepared by magnetron technique, give prospective of their applications e.g. in microelectronics. Originality/value: Microstructure and high resistivity of DLC layers, prepared by magnetron technique, give perspectives for their applications e.g. in microelectronics.

4

Application of DLC layers in 3-omega thermal conductivity method

80%

Wojciechowski K. T. , Zybala R. , Mania R.

Journal of Achievements in Materials and Manufacturing Engineering

|

2009

|

tom Vol. 37, nr 2

512-517

EN

Purpose: The 3-omega method is a unique measuring technique which can be applied for thermal conductivity measurements of bulk materials and layers. In order to measure thermal conductivity of semiconducting and metallic materials (e.g. thermoelectric materials) it is necessary to separate the sensor from the substrate by a dielectric layer. The layer should exhibit thermal conductivity .s comparable or greater than thermal conductivity of characterised materials, as well as good, electrically insulating properties. Design/methodology/approach: The DLC layers were prepared via the magnetron sputtering technique. The reactive sputtering process was carried out in the mixture of Ar and methane (CH4) work gases at the pressure ranging from 0.3 to 0.7 Pa. The layers were deposited on glass and selected thermoelectric materials. The temperature of substrate was controlled in range from 35 oC to 500 oC depending on type of the substrate material. The thickness of received DLC layers was in range from 0.2 to 2 žm. Findings: In order to estimate the accuracy of the modified 3-omega method thermal conductivity measurement results were compared to results of measurements without additional DLC layers and independent data obtained by the laser-flash method. Analysis of experimental results of test measurements show that application of 300 nm thick DLC insulating films allow for characterization of materials exhibiting . < 1.2Wm-1K-1 with the accuracy better than 9%. Research limitations/implications: Results of investigations indicate that prepared DLC layers satisfy requirements of 3-omega method and do not influence significantly on precision and accuracy of thermal conductivity measurements. Originality/value: We have developed the new method of preparation of diamond-like carbon (DLC) layers which satisfy requirements of the 3-omega technique. The layers can be applied for thermal properties measurements of selected thermoelectric materials.

5

Otrzymywanie wybranych materiałów termoelektrycznych metodą krystalizacji kierunkowej i ich charakterystyka

80%

Schmidt M. , Zybała R. , Wojciechowski K. T.

|

tom T. 62, nr 1

56-59

PL

Celem pracy było otrzymanie monokryształów związków AgSbSe2, Ag0,9Sb1,1Se2 oraz BiSbTe3 metodą Bridgmana. Materiały otrzymywano dwoma wariantami metody różniącymi się wytwarzanym gradientem temperatur w obszarze frontu krystalizacji. Obserwacje mikrostrukturalne oraz składu chemicznego przeprowadzono skaningowym mikroskopem elektronowym (SEM) z analizatorem dyspersji energii promieniowania rentgenowskiego (EDS) oraz za pomocą emisyjnej spektroskopii atomowej (AES). Badania jednorodności właściwości termoelektrycznych przeprowadzono za pomocą mikrosondy Seebecka w temperaturze pokojowej. Stwierdzono, że współczynnik Seebecka dla materiału AgSbSe2 zmienia się monotonicznie w zakresie od 250 do 1000 μVK-1. Dla związku Ag0,9Sb1,1Se2 współczynnik Seebecka wynosi od -500 do -750 μVK-1. Monokryształy BiSbTe3 cechują się małymi zmianami wartości współczynnika Seebecka w przedziale od 200 do 280 μVK-1.

EN

The aim of this work was to prepare single crystals of AgSbSe2, Ag0,9Sb1,1Se2 and BiSbTe3 by the Bridgman method. Materials were prepared by means of two variants of this method, differing in temperature gradients in the area of the crystallization front. Microstructural and chemical analysis were done using Scanning Electron Microscope (SEM) with Energy-Dispersive X-ray Spectroscopy (EDS) and Atomic Emission Spectroscopy (AES). Analysis of homogeneity of thermoelectric properties was carried out using the Seebeck microprobe at room temperature. It was found that the Seebeck coefficient for AgSbSe2 changed monotonically in the range from 250 to 1000 μVK-1. For Ag0,9Sb1,1Se2, the Seebeck coefficient is in range from -500 to -750 μVK-1. Single crystals of BiSbTe3 exhibit small changes of the Seebeck coefficient in the range from 200 to 280 μVK-1.

6

Charakterystyka właściwości cieplnych warstw ochronnych metodą 3-omega

61%

Zybała R. , Wojciechowski K. T. , Kucza W. , Gajerski R. , Godlewska E. , Mania R.

|

2009

|

tom Vol. 50, nr 9

22-24

PL

Przedmiotem pracy są badania przewodnictwa cieplnego powłok ochronnych, dla stali wysokogatunkowej oraz materiałów termoelektrycznych, które pełnią jednocześnie funkcje barier termicznych TBC (Thermal Barrier Coatings). Badania przewodnictwa cieplnego powłok wykonano metodą 3-omega. Stwierdzono, że otrzymane powłoki charakteryzują się bardzo dobrymi właściwościami izolacyjnymi. Najniższe przewodnictwo cieplne (0,8 Wm ⁻ K ⁻) zmierzono dla powłok wykonanych na bazie przemysłowych farb wykonanych z żywic fenylometylo siloksanowych odpornych termicznie do 700*C.

EN

The paper deals with thermal conductivity of protective layers for highperformance steel and thermoelectric materials, which also have function of thermal barrier coatings TBC. Measurements of thermal conductivity were made by a 3-omega method. It has been found, that the investigated coatings exhibit very good insulating properties. The lowest thermal conductivity (0,8 Wm ⁻¹ K ⁻¹) was measured for the coatings based on commercial available paint, polysiloxane resin, thermally stable up to 700*C.