Effect of Lignin on properties NR/SBR blends

100%

Kubačková J. , Hudec I. , Ferenc J.

Elastomery

|

2012

|

tom T. 16, nr 3

5-8

EN

In the present work research conceming the application of calcium lignosulfonate in NR/SBR rubber blends used to coating cords is reported. Commercially available lignosulfonate Borrement CA120 was testedas replacement of carbon black, rubber and the both ofthese components in rangę from O to 30% in real rubber blends. Influence of lignin on cure characteristics, crosslink density, physical-mechanical properties and interface compatibility of lignin and rubber matrix were studied. Increasing of lignin con-tentcauses increase of optimum cure time and decrease of crosslink density of rubber blends where rubber or rubber and carbon black were replaced. In case ofthese blends there was also obsemed significant decline oftensile strength at break ofvulcanizates with lignin content over5%. However, measurements of physical-mechanical properties shown that lignin acts as good replacement of carbon blacks in quite wide rangę of concentrations, because there is minimal change in properties in comparison with lig-nin-free compound. Scanning electron microscopy confirmed very good compatibility between lignin and rubber matrix even at high lignin content.

PL

W przedstawionej pracy opisano badania nad zastosowaniem lignosulfonianu wapnia w mieszankach gumowych używanych do powlekania kordów. Dostępny w handlu lignosulfonian Borrement CA120 był testowany jako zamiennik sadzy, kauczuku lub obu tych składników w zakresie od 0 do 30% w stosowanych w przemyśle mieszankach gumowych. Badano wpływ ligniny na właściwości wulkanizacyjne, gęstość usieciowania i właściwości wytrzymałościowe oraz zdolność jednorodnego mieszania się faz ligniny i osnowy kauczukowej. Zwiększenie zawartości ligniny kosztem kauczuku bądź kauczuku i sadzy powodowało wydłużenie optymalnego czasu wulkanizacji i zmniejszenie gęstości usieciowania mieszanek gumowych. W przypadku tych mieszanek można było także zaobserwować znaczące zmniejszenie wytrzymałości na rozciąganie przy zerwaniu wulkanizatów zawierających ponad 5% ligniny. Jednakże pomiary właściwości wytrzymałościowych dowiodły, że lignina jest dobrym zamiennikiem sadzy w dość szerokim zakresie ilościowym, gdyż ich zmiany w stosunku do mieszanek niezawierających ligniny były niewielkie. Badania SEM potwierdziły bardzo dobre powinowactwo kauczuku i ligniny nawet przy dużym udziale ilościowym tej ostatniej.

2

Badanie i charakterystyka populacji rakow w CHKO BR Vychodne Karpaty

100%

Hudec I. , Kosco J. , Platko J.

Roczniki Bieszczadzkie

|

1994

|

tom 03

151-158

3

Elastomeric magnetic composites – physical properties and network structure

100%

Kruželák J. , Hudec I. , Dosoudil R.

Polimery

|

2012

|

tom T. 57, nr 1

25-32

EN

The two types of magnetic elastomeric composites were prepared by incorporation of ferrite alone as well as ferrite in combinations with carbon black in rubber matrix based on natural rubber. The influence of applied fillers and thermo-oxidative ageing on basic physical and magnetic properties of elastomeric composites was studied. Together with the study of properties, the crosslink density and sulfur crosslink structure of prepared vulcanizates were analyzed. The results of the study showed that ferrite alone as well as in combinations with carbon black affects the evaluated properties in various ways. The presence of magnetic filler leads to an increase value of stress at 300 % elongation (Se300) and hardness of composites, the elongation at break by contrast decreases. The values of tensile strength practically do not change in the presence of applied filler. The values of magnetic properties of vulcanizates significantly increase with increasing of ferrite content. In generally one can say that prepared vulcanizates have suitable magnetic and elastic properties.

PL

Wytworzono dwa rodzaje magnetycznych kompozytów elastomerowych, które otrzymano przez wprowadzenie ferrytu lub ferrytu w połączeniu z sadzą do matrycy z kauczuku naturalnego. Zbadano wpływ użytych napełniaczy i termooksydacyjnego starzenia na podstawowe właściwości fizyczne i magnetyczne kompozytów elastomerowych. Wraz z badaniem właściwości analizowano gęstości sieciowania i struktury wiązań poprzecznych w przygotowanych wulkanizatach. Wyniki badań wykazały, że dodatek samego ferrytu, jak i w połączeniu z sadzą wpływa na badane właściwości w różny sposób. Obecność wypełniacza magnetycznego prowadzi do zwiększenia wartości naprężenia przy wydłużeniu 300 % (Se300) i twardości kompozytów, natomiast wydłużenie przy zerwaniu zmniejsza się. W przypadku wytrzymałości na rozciąganie praktycznie nie obserwuje się jego zmian pod wpływem dodanego wypełniacza. Wartości właściwości magnetycznych wulkanizatów znacznie zwiększają się wraz ze wzrostem zawartości ferrytu. Podsumowując można stwierdzić, że otrzymane wulkanizaty mają dobre właściwości magnetyczne i mechaniczne.

4

Surface modification of polyester reinforcing materials by plasma

100%

Hudec I. , Amir I. , Černák M.

|

2010

|

tom Nr 12

97-100

EN

In this work, plasma treatment technique for modification of polyester cords was studied. As result of plasma treatment new morphology of surface layer with different chemical structure and roughness was investigated. These changes may have substantial contribution into increasing of adhesion strength of such treated polyester cords to rubber compound.

PL

Celem pracy było zbadanie wpływu cieczy jonowych na stabilność termiczną i palność gumy. W badaniach wykorzystano następujące ciecze jonowe: tri(pentafluoroetylo)-trifluorofosforan triheksylo(tetradecylo)fosfonowy, tetrafluoroboran l-butylo-2,3-dimetylo-imidazoliowy oraz tri(pentafluoroetylo)trifluorofosforan tetrametylo-amoniowy (Sigma Aldrich), za pomocą których modyfikowano powierzchnię krzemionki, którą następnie napełniano kauczuk, lub spęczniano powierzchnię gumy. Wbrew oczekiwaniom, modyfikacja powierzchni cząstek napełniacza za pomocą cieczy jonowej nie podnosi w istotny sposób stabilności termicznej (T5, T50) ani też wartości wskaźnika tlenowego (Ol) gumy z jego udziałem. Trochę lepiej przedstawia się sytuacja w przypadku powierzchniowej modyfikacji gumy za pomocą cieczy jonowych. Podjęto próby wyjaśnienia tej nieoczekiwanej sytuacji (w literaturze przedmiotu można znaleźć szereg doniesień o uniepalnianiu materiałów, np. drewna, za pomocą cieczy jonowych), badając stopień modyfikacji powierzchni napełniaczy i warstwy wierzchniej gumy oraz morfologię napełnionych wulkanizatów.

5

Centre for applied research of environmentally friendly polymer materials

100%

Bakos D. , Hudec I. , Alexy P. , Bugaj P.

|

2010

|

tom Nr 12

9-12

EN

The Centre is established by the Slovak University of Technology and financed by both the EEA and Norwegian Financial Mechanism. The Centre has three goals - help transfer results from basic science to technology applications, improve education in field of polymers from renewables and to support SMEs (Small and Medium Enterprises) in the field of packaging materials production.

6

Elastomeric composites filled with magnetic hard fillers

100%

Kruželák J. , Hudec I. , Dosoudil R.

|

tom T. 15, nr 1

9-15

EN

In this work elastomeric magnetic materials were prepared by incorporation of strontium ferrite as magnetic filler in rubber compounds based on natural as well as butadiene rubber. The focus of the work is aimed at a preparation of elastomeric magnetic composites and evaluation of magnetic filler influence on curing characteristics, physical-mechanical and magnetic properties of prepared composites. The study is also dedicated to the cross-link density and sulfur cross-link structure of vulcanizates. The results achieved by the study point out the possibilities of preparation of elastomeric magnetic composites by the processes generally used in rubber technology. The prepared materials have suitable magnetic and elastic properties.

PL

W przedstawionej pracy otrzymano materiały o właściwościach, magnetycznych uzyskiwanych przez dodatek napełniacza magnetycznego - żelazianu (III) strontowego (ferrytu strontowego) - do mieszanek gumowych zawierających kauczuk naturalny, jak również butadienowy. Badania koncentrują się na przygotowaniu elastomerowych kompozytów magnetycznych i ocenie wpływu napełniacza magnetycznego na charakterystykę wulkanizacji oraz na właściwości mechaniczne i magnetyczne tych kompozytów. Dotyczą także gęstości usieciowania i struktury wiązań siarkowych w wulkanizatach. Uzyskane w trakcie badań wyniki wykazują możliwości wytwarzania elastomerowych kompozytów magnetycznych w procesach powszechnie stosowanych w technologii gumy. Uzyskane materiały mają odpowiednie właściwości magnetyczne i elastyczne.

7

Strontium ferrite filled rubber composites based on EPDM

100%

Kruželák J. , Dosoudil R. , Hudec I.

Elastomery

|

2017

|

tom T. 21, nr 3

147--158

EN

Strontium ferrite was compounded with ethylene-propylene-diene monomer rubber (EPDM) to prepare rubber magnetic composites. Traditional sulfur as well as peroxide curing system were applied for cross-linking of the rubber matrices. The main objective of the work was to investigate the influence of magnetic filler content and type of curing system on the cross-linking, magnetic and physical-mechanical properties of the prepared composites. The results of the study revealed that EPDM based magnetic composites can be efficiently prepared by applying of both, sulfur and peroxide curing systems. Slightly higher values of tensile strength were found to have composites cured with peroxide curing system, what can be attributed to the suitable combination of dicumyl peroxide and co-agent (i.e. ethylene glycol dimethacrylate). The application of strontium ferrite into both type composites leads to a significant improvement of the remanent magnetic induction.

PL

Do kauczuku etylenowo-propylenowo-dienowego (EPDM) wprowadzono ferryt strontu w celu uzyskania magnetycznych kompozytów gumowych. Do wulkanizacji mieszanek kauczukowych użyto zarówno tradycyjnych siarkowych, jak i nadtlenkowych zespołów sieciujących. Głównym celem pracy było zbadanie wpływu zawartości magnetycznego napełniacza oraz rodzaju zespołu wulkanizującego na właściwości magnetyczne i fizyko-mechaniczne otrzymanych materiałów kompozytowych. Wyniki uzyskanych badań potwierdziły możliwość efektywnego otrzymywania kompozytów gumowych zarówno poprzez wulkanizację siarkową, jak i nadtlenkową. Nieznacznie większą wytrzymałość na rozciąganie kompozytów usieciowanych za pomocą nadtlenkowego zespołu wulkanizującego można przypisać odpowiedniej kombinacji nadtlenku dikumylu i koagenta (tzn. dimetakrylanu glikolu etylenowego). Zastosowanie ferrytu strontu w obu rodzajach kompozytów przyczyniło się do znacznego zwiększenia szczątkowej indukcji magnetycznej.

8

Influence of corn starch on properties of rubber compounds

100%

Vanova P. , Hudec I. , Knazeova A.

|

tom [R.] 19, nr 3 (153)

283--285

EN

At the present time rubber industry and markets of polymer they are obliged be searching of the new renewable resources for their products. Hence, research is focused on application and function of renewable natural sources, for example lignin, starch, cellulose in the last years. The present work was focused on the study of the influence of corn starch as a filler on properties of rubber blends based on NBR. The main goal was to find suitable amount of used corn starch in combinations with other additives of rubber compounds in order to support biodegradability and to reduce the cost of final products. The study is dedicated to the evaluation of starch content on curing characteristics and physical-mechanical properties and the observation of fillers dispersion in the rubber matrix. The corn starch was applied in natural form, and also after subsequent drying. The achieved results point out the possibilities of preparation of rubber compounds with applied corn starch in various concentration.

9

New apparatus for Chip-Chunk resistance testing

88%

Manas D. , Mizera A. , Manas M. , Stoklasek P. , Hudec I.

Elastomery

|

2017

|

tom T. 21, nr 3

167--172

EN

Wear is a phenomenon which can never be completely eliminated. It is present everywhere in all aspects of life. While the problem of wear in metal materials has been described in detail, the problem of wear in rubber products requires further investigation. Tire production is the largest sector in products made of rubber. Their wear is an important factor both for producers and users. Producers aim to produce tires with better resistance to wear than those of their competitors, while users look for a tire with the best resistance of wear. Wear is usually considered in terms of abrasion, which is defined as the loss of material that results from mechanical action on a rubber surface. Abrasion resistance is a complicated phenomenon and is dependent on many things, residence, stiffness, thermal stability, resistance to cutting and tearing, etc. and different applications require these properties in widely varying proportions. Aim of this article is to introduce the reader to the wear of off-road tires which are used in harsh terrain conditions such as quarries, construction sites or forests. For the study of such a type of wear referred to as Chip-Chunk effect improved equipment has been designed, built and verified in praxis.

PL

Zużycie to zjawisko, którego nigdy nie da się całkowicie wyeliminować. Występuje ono we wszystkich aspektach życia. Chociaż problem zużywania się materiałów metalowych został szczegółowo opisany, problem zużycia wyrobów gumowych wymaga dalszego badania. Produkcja opon jest największym sektorem wyrobów z gumy. Ich zużycie jest ważnym czynnikiem zarówno dla producentów, jak i użytkowników. Producenci starają się produkować opony o większej odporności na zużycie niż ich konkurenci, natomiast użytkownicy szukają opony o najlepszej odporności na zużycie. Zużycie jest zazwyczaj rozpatrywane pod kątem ścieralności, określanej jako utrata materiału, która jest wynikiem oddziaływania mechanicznego na powierzchnię gumy. Odporność na ścieranie jest zjawiskiem skomplikowanym i zależy od wielu rzeczy, lokalizacji, sztywności, trwałości termicznej, odporności na rozcięcia i rozdarcia itp., a różne zastosowania wymagają różnego zestawu tych właściwości. Celem tego artykułu jest wprowadzenie czytelnika w zagadnienie zużycia opon terenowych, które są użytkowane w trudnych warunkach, takich jak kamieniołomy, place budowy czy lasy. W celu zbadania takiego typu zużycia, określanego jako efekt chip-chunk, zaprojektowano, zbudowano i zweryfikowano w praktyce udoskonalone urządzenie opisane w tej pracy.

10

Antioxidant properties of lignin in rubber blends

75%

Kubačková J. , Ferenc J. , Hudec I. , Šutý Š. , Jablonský M. , Annus J. , Pret'o J.

|

tom T. 17, nr 3

21--27

EN

The present work studied the antioxidant properties of different lignin samples in carbon black filled NR/SBR blends. The commercial calcium lignosulfonate and two types of lignins with different botanical origin which were isolated from black liquors using diluted sulfuric acid were used. The lignin samples were characterized in terms of the elemental analysis and FTIR spectroscopy. The content of phenolic hydroxyl groups of each sample was determined using UV spectroscopy. Efficiency of these "natural stabilizers" was compared with common used rubber stabilizer N-isopropyl-N'-phenyl-p-phenylene diamine (IPPD). Rubber vulcanizates with addition of chosen stabilizers were submitted to accelerated diermo-oxidative aging for 72 and 168 hours and the mechanical properties of prepared vulcanizates before and after agingwere measured. The obtained results showed that lignin exhibits stabilizing effect in tested rubber blends and its effect is comparable with conventional antioxidant IPPD. However, it was revealed that stabilizing effect depends greatly on total content of phenolic hydroxyl groups. Moreover, the amount of phenolic structures significantly influences antioxidant properties of lignins in mixtures with IPPD.

PL

W niniejszej pracy badano właściwości przeciwutleniające różnych próbek ligniny w napełnionych sadzą mieszankach NR/SBR. Do badań użyto komercyjnego lignosulfonianu wapnia oraz dwóch rodzajów ligniny o różnym pochodzeniu botanicznym, wyizolowanych z ługu posiarczynowego za pomocą rozcieńczonego kwasu siarkowego. Próbki ligniny scharakteryzowano metodami analizy elementarnej i spektroskopii FTIR. Zawartość grup hydroksylowych pochodzących z fenolu w każdej z próbek określono za pomocą spektroskopii UV. Skuteczność tych „naturalnych stabilizatorów" porównywano z efektywnością powszechnie stosowanego w mieszankach gumowych stabilizatora - N-izopropylo-N'-fenylo-p-fenylenodiaminy (IPPD). Zwulkanizowane próbki zawierające dodatek wybranych stabilizatorów poddano przyśpieszonemu starzeniu termooksydacyjnemu w ciągu 72 i 168 h oraz zmierzono ich właściwości mechaniczne przed i po starzeniu. Uzyskane wyniki dowodzą, że w przypadku badanych mieszanek gumowych lignina działa stabilizująco, zaś pod względem skuteczności jest porównywalna z konwencjonalnym przeciwutleniaczem - IPPD. Okazało się także, że efekt stabilizujący ligniny zależy w dużym stopniu od całkowitej zawartości fenolowych grup hydroksylowych. Co więcej, ilość struktur fenolowych znacząco wpływa na właściwości przeciwutleniające ligniny w mieszaninach z IPPD.

11

Study of thermo-mechanical degradation of biodegradable polymers using oscillation rheometry

75%

Pavlačková M. , Alexy P. , Tomanová K. , Bugaj P. , Hudec I. , Bakoš D.

|

2010

|

tom Nr 12

283-286

EN

This work is focused on study of possibilities to determine thermo - mechanical degradation during melt processing of biopolymers. The oscillation rheometry was found as the simple method which is able indicates the first stages of degradation process. Polylactide acid was used as bio-polymer substance in comparison to PE and PCL.