PL
 |
EN
Nowa wersja platformy, zawierająca wyłącznie zasoby pełnotekstowe, jest już dostępna.
Przejdź na https://bibliotekanauki.pl
Preferencje help
Polish version English version Język
Widoczny [Schowaj] Abstrakt
Liczba wyników

Znaleziono wyników: 6

Liczba wyników na stronie
first rewind previous Strona / 1 next fast forward last
Wyniki wyszukiwania
help Sortuj według:

help Ogranicz wyniki do:
first rewind previous Strona / 1 next fast forward last
1
Podłączenie filtracyjo-kompensacyjnego rozdzielacza dla sieci wysokiego napięcia
100%
Novy Z. , Žila D.
Zeszyty Naukowe. Elektryka / Politechnika Opolska
|
2002
|
tom Vol. 280, z. 51
525-530
EN
This report shows what are the possibilities for a construction of ststic and automated compensator of power factor in a tension level 6kV. Two of the main features are: a higher compatibility with a feeding network, and a higher compatibility with a network with connected appliances. The example of a compact filtration and compensating switchboard, awarded on AMPER 2001 fairs, will be presented.
2
Content available remote Deformation behavior of bulk TRIP steel
80%
Zrnik J. , Muransky O. , Novy Z. , Slama P.
Journal of Achievements in Materials and Manufacturing Engineering
|
2015
|
tom Vol. 68, nr 2
59--63
EN
Purpose: Experimental verification of various thermo-mechanical (TM) processing schedules, with aim to modify the structure characteristics using press forging of Si-Mn TRIP (Transformation Induced Plasticity) steel, was described. Design/methodology/approach: High strength and ductility of TRIP steels is attributed to the TRIP effect resulting from the strain induced martensitic transformation of the retained austenite in the multiphase (ferrite, bainite, martensite) microstructure. In order to rationalize the retained austenite (RA) volume fraction in steel microstructure, several TM schedules were employed at experiment where different austenite conditioning was considered. Findings: The various multiphase structure characteristics were then resulting after TM processing of steel, where different volume fractions of ferrite, bainite and RA were received in the steel. The modification of structural characteristics of steel then influenced the deformation behavior and mechanical properties TRIP steel. Research limitations/implications: The present work also focused on monitoring of RA transformation during incremental mechanical straining using in-situ neutron diffraction technique. Originality/value: This non-convenient experimental method was used to characterize the kinetics of RA transformation and its stability during consecutive straining.
3
Content available remote Carbide spheroidisation in 100CrMnSi6-4 bearing steel by controlled rolling
80%
Dlouhy J. , Hauserova D. , Novy Z.
Archives of Materials Science and Engineering
|
2014
|
tom Vol. 68, nr 2
87--92
EN
Purpose: This article describes influence of thermomechanical treatment parameters on microstructure and mechanical properties of 100CrMnSi6-4 bearing steel. Design/methodology/approach: Steel properties after accelerated carbide spheroidisation enables machining and cold forming as well as after conventional soft annealing. Apparently, structure after accelerated carbide spheroidisation is significantly finer than after long duration soft annealing – in terms of carbide particles and grain size. That enhances steel hardness and homogeneity of the structure in final state after hardening. Findings: Presented experiment deals with accelerated carbide spheroidisation of 100CrMnSi6-4 bearing steel during final stage of hot rolling. Main purpose is to achieve microstructure consisting of globular carbides and ferritic matrix directly after hot forming. Research limitations/implications: The combination of a suitable forming temperature, an appropriate amount of deformation and a possible reheating lead to globular carbide formation during austenite decomposition instead of cementite lamellae. Originality/value: Experiment results are promising for quenching and tempering in comparison with structure after conventional soft annealing with coarser. Finer ASR structure retains finer austenite grain at quenching temperature and higher dispersion strengthening.
4
Content available Effect of Heating Rate on Accelerated Carbide Spheroidisation (ASR) in 100CrMnSi6-4 Bearing Steel
80%
Hauserova D. , Dlouhy J. , Novy Z.
Archives of Metallurgy and Materials
|
2014
|
tom Vol. 59, iss. 3
1199--1203
EN
Typical processing routes for bearing steels include a soft annealing stage, the purpose of which is to obtain a microstructure containing globular carbides in ferritic matrix. A newly developed process called ASR cuts the carbide spheroidisation times several fold, producing considerably finer globular carbides than conventional soft annealing. The present paper explores the effect of the heating rate and temperature on the accelerated carbide spheroidisation process and on the resulting hardness. Accelerated spheroidisation was achieved by thermal cycling for several minutes around various temperatures close to the transformation temperature at various heating rates applied by induction heating.
PL
Proces obróbki stali łożyskowych obejmuje wyżarzanie zmiękczajace, którego celem jest uzyskanie mikrostruktury zawierającej kuliste węgliki w osnowie ferrytycznej. Nowo opracowana obróbka zwana ASR polega na wielokrotnym przerywaniu procesu sferoidyzacji, co prowadzi do wytworzenia węglików kulistych o znacznie mniejszych rozmiarach w porównaniu do tych, jakie powstają w konwencjonalnym procesie wyżarzania zmiękczającego. Niniejsza praca analizuje wpływ szybkości grzania i temperatury na proces przyspieszonej sferoidyzacji węglików i na uzyskana twardość. Przyspieszona sferoidyzacje węglików uzyskano dzięki zastosowaniu cyklicznych zmian temperatury trwających kilka minut wokół określonych temperatur bliskich temperaturze przemiany za pomocą grzania indukcyjnego z różnymi prędkościami.
5
Content available remote Influence of pulsatory forming on mechanical properties of stainless steel
70%
Kvackaj T. , Sokolova L. , Vlado M. , Vrchovinsky V. , Novy Z.
Archives of Civil and Mechanical Engineering
|
2004
|
tom Vol. 4, no 3
93-101
EN
Pulsatory forming of metal materials (stress cycling) is a non-conventional forging method based on the application of a variable pulsation frequency during the metal-forming process. This paper presents initial results of pulsatory forming performed with a pulsator at the Department of Metal Forming, Technical University of Kosice. The basic mechanical characteristics as well as geometrical and microstructural parameters ofCrl8Nil0 steel after pulsatory forming were analyzed.
PL
Formowanie cykliczne materiałów metalicznych jest niekonwencjonalną metoda kucia opartą na zmiennej frekwencji cyklicznego obciążania w procesach kształtowania metali. Przedstawiono wstępne wyniki kształtowania cyklicznego przy użyciu pulsatora zainstalowanego na Wydziale Kształtowania Metali Politechniki w Koszycach. Przeanalizowane podstawowe właściwości mechaniczne oraz geometryczne i mechaniczne parametry stali Crl8Ni 10 po kształtowaniu cyklicznym. Kształtowanie prowadzono w stałej temperaturze 850 C po wstępnym nagrzaniu stali do temperatury I 100 C. Zaobserwowano także, że cykliczne odkształcanie zwiększa niejednorodność odkształceń oraz powoduje zmniejszenie rozmiarów ziaren, zapewniając jednocześnie dobre właściwości plastyczne badanego materiału, konieczne do jego prawidłowego kształtowania.
6
Content available Effect of Heating Rate on Accelerated Carbide Spheroidisation (ASR) in 100CrMnSi6-4 Bearing Steel
41%
Hauserova D. , Dlouhy J. , Novy Z.
|