Content available Casting Quality Improvement by Gating System Optimization
100%
Bruna M. , Galčík M.
Archives of Foundry Engineering
|
2021
|
tom Vol. 21, iss. 1
132--136
EN
One of the main reason for decreased internal homogeneity of aluminium alloy castings is reoxidation. The resulting products of reoxidation are doubled oxides, so called "bifilms". Submitted paper deals with optimization of gating system design in order to reduce reoxidation processes taking place in mold cavity. Experimental work compares and evaluates three gating systems designs based on non-pressurized and naturally pressurized principles. Unconventional spin trap extension of runner was used in third design. Among the evaluated aspects were: mechanical properties, hot tearing index, visual inspection of average porosity amount, numerical simulation of velocity, turbulence and oxide amount. Paper aim is also to clarify the reoxidation phenomenon by visualization with the aid of ProCAST numerical simulation software. Results of mechanical properties and hot tear index clearly confirmed the positive effect of the naturally pressurized gating system with applied element for velocity reduction.
2
Content available Casting Quality Improvement by Gating System Optimization
85%
Bruna M. , Galčík M. , Bruna M. , Galčík M.
|
3
Content available Effect of Strontium Inoculation on Hot Tearing in Aluminium Alloys
80%
Bolibruchová D. , Bruna M. , Pastirčák R. , Major-Gabryś K.
Archives of Metallurgy and Materials
|
2018
|
tom Vol. 63, iss. 4
1837--1842
EN
Main aim of submitted work is evaluation and experimental verification of inoculation effect on Al alloys hot-tear sensitivity. Submitted work consists of two parts. The first part introduces the reader to the hot tearing in general and provides theoretical analysis of hot tearing phenomenon. The second part describes strontium effect on hot tearing susceptibility, and gives the results on hot tearing for various aluminium alloys. During the test, the effect of alloy chemical composition on hot tearing susceptibility was also analyzed. Two different Al-based alloys were examined. Conclusions deals with effect of strontium on hot tearing susceptibility and confirms that main objective was achieved.
4
Content available Effect of Filter Thickness on Reoxidation and Mechanical Properties of Aluminium Alloy AlSi7Mg0.3
80%
Bruna M. , Remišová A. , Sládek A.
|
|
tom Vol. 64, iss. 3
1100--1106
EN
The melt cleaning is an important aspect in the production of high-quality aluminum castings. Specifically inclusions within the melt and an excessively high hydrogen content lead to defects and undesired porosity in the castings. Although it is possible to reduce the amount of hydrogen and oxidic inclusions by purge gas treatment and the use of melting salts, it is impossible toremove oxides (bifilms) created during filling of gating system. Paper deals with the effects of melt quality and the placement of a filter in the filling system on Al-7%Si-Mg alloy mechanical properties. Three different filters were used: (a) rectangular ceramic pressed filter with 3 mm thickness (b) cubical pressed ceramic filter with thickness 10 mm (c) cubical pressed ceramic filter with thickness 22 mm. The results showed that the highest tensile strength values were obtained from the filter with thickness of 22 mm. Numerical simulation analysis of the filling process showed that velocity reduction by filter is the major phenomenon affecting the mechanical properties. Another evaluated aspect during experiments was capability of filters to retain old bifilms. For this purpose multiply remelted alloy was prepared and analyzed. Results showed that filter efficiency increases with decreasing melt quality as a result of possibility to retain "old” bifilms better than small and thin "new” bifilms.
5
Content available Effect of Strontium Inoculation on Hot Tearing in Aluminium Alloys
60%
Bolibruchová D. , Bruna M. , Pastirčák R. , Major-Gabryś K.
|
|