Fracture toughness of 19Mn5 steel pipe welded joints materials

100%

Daunys M. , Krasauskas P. , Dundulis R.

Acta Mechanica et Automatica

2009

tom Vol. 3, no. 4

24-27

This paper presents an investigation of Ignalina NPP reactor’s main circulated circuit (MCC) pipeline welded joints materials fracture toughness properties. Standard compact C(T)-1T specimens containing “V” and “K” – type welds were cut off from the various MCC pipe’s zones, produced from the 19Mn5 steel pipe and welded by electrodes UTP-068HH, YONI-13/55 and CT-36. Critical J – integraf JIc values were defined Rusing J–R curve test method, which results on determination of J – integral values as a function of crack extension ?a. The investigation enables to calculate critical crack length ?amax and ?ac sizes and J – integral JIc, Jmax and JPmax values, which are used to predict safe service lifetime of the cracked pipelines.

Fracture toughness of welded joints materials in ignalina NPP steam pipelines

100%

Daunys M. , Krasauskas P. , Dundulis R.

Zeszyty Naukowe Politechniki Białostockiej. Mechanika

2001

tom Z. 24

115--122

The paper presents an investigation of fracture toughness of welded joint metals in Ignalina NPP steam pipelines DU-300 and DU-630. Main metal steels 08X18N10T and 16GS, weld metal welded by manual and automatic arc method using the wire SV-0419N11M3 and electrodes EA-100/10U or EA-100/10T, weld metal welded by manual arc method using the wire SV-08GS2 and electrodes UONI13/55 and heat affected zone metal of welded joint of steel 08X18N10T were investigated. In compact specimens sharp fatigue cracks were initiated and using fracture compliance testing method crack resistance curves, J integral versus crack length (J-R curve), limit values of stable crack extension Damax and critical values of JIc integral were obtained.

W pracy opisano badania odporności na pękanie połączeń spawanych w rurociągach parowych wykonanych z Ignaliny NPP. W próbkach kompaktowych wyinicjowano pęknięcia zmęczeniowe i sporządzono dla nich krzywe J - R. Określono także graniczną wartość długości szczeliny Damax oraz krytyczną wartość całki J (JIc).