PL
 |
EN
Nowa wersja platformy, zawierająca wyłącznie zasoby pełnotekstowe, jest już dostępna.
Przejdź na https://bibliotekanauki.pl
Preferencje help
Polish version English version Język
Widoczny [Schowaj] Abstrakt
Liczba wyników

Znaleziono wyników: 26

Liczba wyników na stronie
first rewind previous Strona / 2 next fast forward last
Wyniki wyszukiwania
help Sortuj według:

help Ogranicz wyniki do:
first rewind previous Strona / 2 next fast forward last
1
Content available The studies of scale surface produced on outer diffusion layers
100%
Augustyn-Pieniążek J. , Zapała R.
Archives of Foundry Engineering
|
2011
|
tom Vol. 11, iss. 2 spec.
5--8
EN
In this study at attempt was made to examine the scale formed on ferritic-austenitic duplex type steel subjected to previous thermo-chemical treatment. The treatment consisted in diffusion aluminising in a metallising mixture composed of Fe-Al powder. As an activator, ammonium chloride (NH4Cl) added in an amount of 2 wt.% was used. Then, both the base material and samples with the diffusion-deposited surface layers were oxidised at 1000°C in the air. Thus formed scales were identified by light microscopy, SEM and X-ray phase analysis. The aim of the oxidation tests carried out under isothermal conditions was to compare the scale morphology when obtained on untreated substrate material and on the surface layers rich in aluminium.
2
Content available remote Changes of phase morphology in 29%Cr-6%Ni-3%Mo-3% Cu steel castings with varied wall thickness
100%
Kalandyk B. , Augustyn-Pieniążek J.
Archives of Foundry Engineering
|
2008
|
tom Vol. 8, iss. 1 spec.
175--178
EN
The article discusses the effect of wall thickness and temperature of solution treatment on the morphology of phases present in castings made from 29%Cr-6%Ni-3%Mo-3% Cu steel. The presence of acicular precipitates near the casting surface in as-cast condition was stated. The precipitates ceased to exist after the solution treatment, while volume fraction of the alloyed ferrite increased quite obviously. Compared with parallel investigations carried out on cast steel heats with lower concentration of Cr (24-25%), it has been started that high concentrations of Cr and Mo favour the occurrence of a brittle phase σ, both in as-cast condition and after solution treatment.
3
Content available Qualitative Assessment of the Defects in Metal Casting Prosthetic Restorations
100%
Augustyn-Pieniążek J. , Wilkosz K.
Archives of Foundry Engineering
|
2014
|
tom Vol. 14, iss. 4 spec.
7--12
EN
Due to the frequent occurrence of casting defects in the casting process of metal prosthetic elements, studies aiming at identifying the defects and determining their probable causes were performed. The work presents the results of the examinations of the Co-Cr-Mo alloy, brand name Argeloy N.P. Special, used for prosthetic restorations. Macroscopic and microscopic observations were conducted with the use of light and scanning microscopy (SEM). Also, the results of the observations by means of a 3D scanner by GOM ATOS 3 were presented. The performed research made it possible to determine and classify casting defects such as blisters, misruns and interscrystalline cracks. It was stated that a stabilized technological process affects the elimination of the casting defect formation.
4
Effect of the type of abrasive agent on the properties of cast Co-Cr alloys used in prosthetics
100%
Augustyn-Pieniążek J. , Kurtyka P.
Rudy i Metale Nieżelazne Recykling
|
2015
|
tom R. 60, nr 6
262--268
EN
The study presents the results of abrasion resistance tests carried out on alloys from the cobalt-based family, including Remanium 2001 (CoCrMoW) and Wironit LA (CoCrMo). Tests were performed on the Miller apparatus. The abrasive agent was slurry composed of water and silicon carbide particles of different granulations (SiC > 500 μm and SiC ~45 μm). The study included metallographic examinations, measurements of hardness and weight loss recorded in the tested materials after different times of abrasion amounting to 2, 4, 6, 8, 12 and 16 hours. The surfaces of samples subjected to abrasion were additionally examined by SEM. Alloys were characterized by a dendritic structure typical of cast materials. The results have proved the effect of abrasive particle size on the relative weight loss in Remanium 2001 and Wironit LA alloys. They have also proved that, regardless of the size of abrasive particles, the Wironit LA alloy offers better resistance to abrasion than Remanium 2001. This is due to, among others, the geometric features of the dendrite arms.
PL
W artykule przestawiono wyniki badań odporności na ścieranie stopów z grupy na osnowie kobaltu Remanium 2001 (CoCrMoW) i Wironit LA (CoCrMo), które wykonano na aparacie Millera. Ośrodek ścierający stanowiła zawiesina złożona z wody i węglika krzemu o różniej granulacji (SiC > 500 μm i SiC ~45 μm). W ramach badań wykonano obserwacje metalograficzne, pomiary twardości oraz zarejestrowano ubytki mas badanych materiałów po poszczególnych czasach ścierania tj. 2, 4, 6, 8, 12 i 16 h. Dodatkowo powierzchnie próbek po ścieraniu poddano obserwacji przy wykorzystaniu SEM. Wykazano, że stopy charakteryzowały się strukturą dendrytyczną typową dla materiałów odlewanych. Stwierdzono również istotną rolę wielkości elementów trących na wartości względnych ubytków mas stopu Remanium 2001 oraz Wironit LA. Pokazano również, że stop Wironit, cechuje się większa odpornością na ścieranie od stopu Remanium 2001, niezależnie od wielkości cząstek ścierających. Efekt ten jest związany między innymi z właściwościami geometrycznymi ramion dendrytów.
5
Content available Corrosion Resistance of Co-Cr-Mo Alloy Used in Dentistry
100%
Łukaszczyk A. , Augustyn-Pieniążek J.
Archives of Metallurgy and Materials
|
2015
|
tom Vol. 60, iss. 1
523--528
EN
The presented paper studies the effect of the casting technology on the corrosion resistance of Co-Cr-Mo alloy. The investigations were conducted on a commercial alloy with the brand name ARGELOY N.P SPECIAL (Co-Cr-Mo) produced by Argen as well as the same alloy melted and cast by the lost wax casting method performed by a dental technician. The corrosion behavior of the dental alloys in an artificial saliva was studied with the use of the following electrochemical techniques: open circuit potential and voltammetry. After the electrochemical tests, studies of the surface of the examined alloys were performed by means of a scanning electron microscope with an X-ray microanalyzer. The results of the electrochemical studies show that the dependence of the corrosion resistance on the microstructure associated with the recasting process is marginal. The results of the electrochemical studies of the considered alloy clearly point to their good corrosion resistance in the discussed environment.
PL
Zbadano wpływ technologii odlewania na odporność korozyjną stopu Co-Cr-Mo. Badaniom poddano stop komercyjny o nazwie handlowej ARGELOY N.P SPECIAL (Co-Cr-Mo) firmy Argen oraz ten sam stop przetopiony i odlany przez technika dentystycznego metodą traconego wosku. Zachowanie korozyjne badanego stopu w środowisku sztucznej śliny zostało zbadane przy użyciu technik elektrochemicznych: pomiaru potencjału bezprądowego, woltamperometrii cyklicznej. Po przeprowadzeniu badań elektrochemicznych wykonano badania powierzchni badanego stopu przy pomocy elektronowego mikroskopu skaningowego z mikroanalizatorem rentgenowskim. Wyniki badań elektrochemicznych wskazują, że na odporność korozyjną oraz mikrostrukturę stopu proces powtórnego odlania wpływa jedynie w niewielkim stopniu. Wyniki badań elektrochemicznych rozpatrywanego stopu wskazują jednoznacznie na ich dobrą odporność korozyjną w rozpatrywanym środowisku.
6
Content available Badania materiałowe i korozyjne konwencjonalnych stopów Co-Cr-Mo-W przeznaczonych na odlewy konstrukcji szkieletowych w protetyce dentystycznej
80%
Augustyn-Pieniążek J. , Łukaszczyk A. , Loch J.
Engineering of Biomaterials
|
2015
|
tom Vol. 18, no. 130
2--9
PL
Podstawowe cechy jakimi powinny charakteryzować się materiały stosowane na protezy szkieletowe w stomatologii to biotolerancja w środowisku tkanek i płynów ustrojowych oraz duża odporność na korozję wżerową i szczelinową. Ważna jest również stabilność zespołu określonych własności fizyczno-mechanicznych (wysoka wytrzymałość, odpowiednia ciągliwość, twardość i odporność na ścieranie) oraz jednorodność składu chemicznego W pracy przedstawiono wyniki badań konwencjonalnych stopów odlewniczych Co-Cr-Mo-W stosowanych do wykonywania odlewów szkieletów protez ruchomych, koron i mostów w protetyce dentystycznej. Badania wykonano na czterech stopach Co-Cr-Mo-W o różnej zawartości Mo, W oraz innych domieszek. W pracy dokonano analizy mikrostruktury stopów z zastosowaniem mikroskopu świetlnego oraz elektronowego mikroskopu skaningowego. Dodatkowo wykonano pomiary mikrotwardości metodą Vickersa oraz badania odporności korozyjnej. Dla każdego z badanych stopów Co-Cr-Mo-W wykreślono zależność potencjału stacjonarnego w funkcji czasu oraz wykonano badania woltamperometryczne w środowisku sztucznej śliny. Przeprowadzone obserwacje metalograficzne pozwoliły stwierdzić, że analizowane materiały charakteryzowały się budową dendrytyczną typową dla stopów odlewanych. Mikrostruktura ta jest chemicznie niejednorodna, złożona z austenitycznej osnowy składającej się z roztworu stałego kobaltu oraz chromu w rdzeniowej strukturze dendrytycznej. Stopy charakteryzowały się wysoką twardością. Wzrost mikrotwardości jest silnie determinowany występowaniem wydzieleń węglikowych M23C6, które zapewniają dużo silniejsze umocnienie stopu. Analizowane stopy wykazywały zbliżone przebiegi krzywych polaryzacji. Zachowanie elektrochemiczne stopów Co-Cr-Mo-W w dużej mierze zależy od zawartości w stopie chromu i molibdenu, pierwiastków, które przyczyniają się do pasywacji stopów.
EN
The basic characteristics of skeletal prosthetic materials used in dentistry are: biotolerance with tissues and body fluids, as well as high pitting and crevice corrosion resistance. Also important are such characteristics as: high strength, adequate ductility, hardness and abrasion resistance, as well as homogeneity of the chemical composition. The work presents the results of the studies of conventional Co-Cr-Mo-W casting alloys used in the production of frame casts of removable dentures, crowns and bridges in dental prosthetics. The studies were performed on four Co-Cr-Mo-W alloys of different contents of Mo, W and other additives. The work analyzes the alloys microstructures with the use of a light microscope and a scanning electron microscope. Additionally, hardness measurements were made by means of the Vickers method and corrosion resistance tests were conducted. For each examined Co-Cr-Mo-W alloy, the open circuit potential as a function of time was determined and voltamperometric tests were performed in artificial saliva. The microstructure of the examined alloys was of the dendrite type. This microstructure was chemically inhomogeneous and consisted of an austenitic matrix formed by a solid cobalt solution and chromium in the core dendritic structure. The investigated alloys were characterized by high hardness. The increase in the microhardness was depended on the presence of carbide precipitates M23C6, which provide a much stronger reinforcement of the alloy. The analyzed materials exhibited a similar progress of the polarization curves. The electrochemical corrosion of Co-Cr-Mo-W alloys was depended on the content of chromium and molybdenum, which largely contributed to alloy passivation.
7
Model kinetyki wydzielania węglikoazotków w stalach mikrostopowych
80%
Adrian H. , Augustyn-Pieniążek J. , Marynowski P. , Matusiewicz P.
Hutnik, Wiadomości Hutnicze
|
2014
|
tom Vol. 81, nr 4
208--214
PL
W artykule przedstawiono model kinetyki wydzielania węglikoazotku M(C, N) w stali mikrostopowej zawierającej dodatek Ti, Nb lub V. Model jest oparty na klasycznej teorii zarodkowania (ogólny model Kampmanna i Wagnera [1]) i pozwala obliczać rozkład wielkości wydzieleń w austenicie lub ferrycie w warunkach izotermicznego wytrzymywania stali przy temperaturze Tw, poddanej wcześniej przesycaniu o wysokiej temperaturze Tp. Opisano opracowany program komputerowy CarbNit_kinet oraz przedstawiono przykład wyników obliczeń dla stali zawierającej 0,2 %C, 0,01 %N i 0,15 %V.
EN
Model of kinetics of carbonitride M(C, N) precipitation in HSLA steel containing microalloying element Ti, Nb or V is presented. The model is based on classical theory of nucleation (general model of Kampmann and Wagner [1]). It enables to calculate the size distribution of carbonitrides precipitation in austenite or ferrite during isothermal holding at temperature Tw of microalloyed steel after previous heating at high austenitising temperature Tp. An example of application of developed computer program, CarNit_kinet for carbonitride precipitation in steel containing 0.2 %C, 0.01 %N and 0.15 %V is presented.
8
Content available Structure and Mechanical Properties of Al-Li Alloys as Cast
80%
Augustyn-Pieniążek J. , Rzadkosz S. , Adrian H. , Choroszyński M.
|
|
nr 2
9
Charakterystyka warstw tlenkowych powstałych na staliwie Cr-Ni modyfikowanym Ce podczas wysokotemperaturowego utleniania
80%
Zapała R. , Augustyn-Pieniążek J. , Kalandyk B.
Inżynieria Materiałowa
|
2012
|
tom Vol. 33, nr 1
37--41
PL
W pracy badano wpływ Ce w staliwie chromowo-niklowym na korozję wysokotemperaturową. W artykule przedstawiono wyniki badań kinetyki utleniania stopu w temperaturze: 820, 930 i 1000°C oraz charakterystykę morfologii powierzchni zgorzeliny utworzonej na staliwie Cr-Ni. Badania warstwy produktów korozji powstałych podczas izotermicznego utleniania obejmowały obserwacje mikroskopowe (SEM), mikroanalizę rentgenowską (EDS) oraz pomiary rentgenograficzne za pomocą rentgenowskiej dyfrakcyjnej analizy fazowej z zastosowaniem dyfrakcji w geometrii Bragg-Brentano. Stwierdzono, że materiał dla wszystkich wartości temperatury badań utleniał się w przybliżeniu zgodnie z prawem parabolicznym. Powstała zgorzelina była zwarta i ciągła dla niższej temperatury utleniania. W badanych zgorzelinach za pomocą dyfrakcyjnej analizy fazowej zidentyfikowano następujące fazy: Cr2O3, MnCr2O4, (Cr, Fe)2O3, SiO2 i CrNbO4.
EN
The effect of Ce on the behaviour of cast chromium-nickel steel subjected to high temperature corrosion was investigated. The work also includes studies of the kinetics of oxidation of the alloy at temperatures of 820, 930 and 1000°C and the characteristics of the surface morphology of the scale formed on the Cr-Ni cast steel. Examinations of the layer of corrosion products formed during isothermal oxidation included microscopic observations (SEM), X-ray microanalysis (EDS), and X-ray diffraction phase analysis in Bragg-Brentano geometry. It was found that for all the test temperatures, the material was oxidized roughly in accordance with parabolic law. The resulting scale was compact and continuous at lower oxidation temperatures. The analysis of the recorded diffraction patterns allowed detection in the examined scale the presence of the following phases: Cr2O3 MnCr2O4, (Cr, Fe)2O3, SiO2 and CrNbO4.
10
Content available Structure and mechanical properties of Al-Li alloys as cast
80%
Augustyn-Pieniążek J. , Adrian H. , Rzadkosz S. , Choroszyński M.
Archives of Foundry Engineering
|
2013
|
tom Vol. 13, iss. 2
5--10
EN
The high mechanical properties of the Al-Li-X alloys contribute to their increasingly broad application in aeronautics, as an alternative for the aluminium alloys, which have been used so far. The aluminium-lithium alloys have a lower specific gravity, a higher nucleation and crack spread resistance, a higher Young’s module and they characterize in a high crack resistance at lower temperatures. The aim of the research planned in this work was to design an aluminium alloy with a content of lithium and other alloy elements. The research included the creation of a laboratorial melt, the microstructure analysis with the use of light microscopy, the application of X-ray methods to identify the phases existing in the alloy, and the microhardness test.
11
Content available Selected properties and tribological wear alloys Co-Cr-Mo and Co-Cr-Mo-W used in dental prosthetics
80%
Augustyn-Pieniążek J. , Kurtyka P. , Sulima I. , Stopka J.
Archives of Metallurgy and Materials
|
2015
|
tom Vol. 60, iss. 3A
1569--1574
EN
The presented work provides the results of the abrasive wear resistance tests performed on Co-Cr-Mo and Co-Cr-Mo-W alloys with the use of the Miller’s apparatus. The analyzed alloys underwent microstructure observations as well as hardness measurements, and the abraded surfaces of the examined materials were observed by means of electron scanning microscopy. The performed examinations made it possible to state that the Co-Cr alloys characterized in a high hardness, whereas the changes in the mass decrement were minimal, which proved a high abrasive wear resistance.
PL
W prezentowanej pracy przedstawiono wyniki badań zużycia ściernego stopów, Co-Cr-Mo i Co-Cr-Mo-W przy użyciu aparatu Millera. Analizowane stopy poddano obserwacjom mikrostruktury, pomiarom twardości i mikrotwardości, a ścierane powierzchnie badanych materiałów obserwacji przy wykorzystaniu elektronowej mikroskopii skaningowej. Przeprowadzone badania pozwoliły na stwierdzenie, że stopy, Co-Cr charakteryzowały się wysoką twardością i mikrotwardością, zaś zmiany ubytku masy były bardzo minimalne, co świadczy o wysokiej odporności na ścieranie.
12
Content available remote Deformation and recrystalization textures in single phase Ag-Cd alloys
80%
Ratuszek W. , Kowalska J. , Augustyn-Pieniążek J. , Chruściel K.
Archives of Metallurgy and Materials
|
2005
|
tom Vol. 50, iss. 2
423-433
EN
Deformation and recrystallization textures were examined in pure Ag and Ag with 10, 15, 20 and 30 wt.% Cd additions. The materials were cold-rolled up to 90% of deformation and subsequently annealed within the range of temperatures 170-310°C for 20, 60 and 120 min in dependence on the chemical composition. The influence of alloy addition on the texture development was investigated due to the fact that the electron density coeffcient increases, while the stacking fault energy (SFE) decreases with the increasing content of Cd. The texture after deformation could be described by a limited &alpha fibre <110> ND with main component {110}<225> and a weak &gamma fibre {111}. After annealing the &alpha fibre became weak and extended, the maximum of the orientation distribution function (ODF) value shifted towards the {110<110> orientation and the &gamma fibre decayed. New components appeared: a limited {113g fibre and {430}<340>, {412}<548>, {523}<638> orientations. Although the cadmium addition did not affect much the deformation texture, its influence on recrystallization texture was more pronounced. The relationship between deformation and annealing textures was described by the 35-40° rotation around <111> poles, for oriented growth or by the rotation about the (2n-1) x 60° angle around <111> poles, for twinning. The orientations formed during further annealing can be described by the 22-30° rotation angle around <111> poles of the previous textures. Small volume of twinned areas was observed in the microstructure after large deformation. The formation of twins during annealing and their selective growth indicated that they played an important role in the recrystallization process.
PL
Przedmiot badań stanowiło srebro i jego stopy Ag-Cd (10, 15, 20 i 30% masowych Cd). Materiał walcowano na zimno do 90% odkształcenia i następnie wyżarzano w zakresie temperatur 170-310°C (w zależności od składu chemicznego) przez czas 20, 60 i 120 minut. Badano wpływ dodatku stopowego na rozwój tekstury, wraz ze wzrostem zawartosci kadmu wzrasta stężenie elektronów (e/a) natomiast energia błedu ułozenia (EBU) maleje. Teksturę po odkształceniu opisuje ograniczone włókno &alpha (<110>II KW) z główną składową {110}<225> i słabe włókno &gamma {111}. W wyniku wyżarzania włókno &alpha ulega osłabieniu i rozciągnięciu, maksimum orientacji przesuwa sie w kierunku orientacji {110}<110>, zanika włókno &gamma, pojawiają się nowe składowe np. ograniczone włókno {113}< uvw> i orientacje {430}<340>, {412}<548>, {523}<638>. Dodatek stopowy Cd nie wpłynął istotnie na teksturę odkształcenia, natomiast wyraźniejszy był wpływ kadmu w przypadku tekstury rekrystalizacji. Relacje pomiędzy orientacjami wystepującymi w teksturze odkształcenia a orientacjami tekstury rekrystalizacji można opisać obrotem o kąt około 40° wokół biegunów <111> i obrotem (2n-1) L 60° wokół biegunów <111>- relacja bliźniacza, zaś orientacje powstałe w dalszym etapie wyżarzania obrotami o kąty 22- 30° wokół biegunów <111> uprzednio powstałych orientacji. W mikrostrukturze po dużych stopniach odkształcenia obserwuje się niewielką ilość obszarów zbliźniaczonych na tle pasm ścinania. Tworzenie się bliźniaków w czasie wyżarzania a następnie selektywny wzrost wskazują na ich istotną rolę w procesie rekrystalizacji.
13
Content available remote Skład fazowy i mikrostruktura warstwy wierzchniej na podłożu stali austenitycznej 18-8 po laserowej modyfikacji
80%
Augustyn-Pieniążek J. , Skrzypek S. , Goły M.
Czasopismo Techniczne. Mechanika
|
2009
|
tom R. 106, z. 2-M
91-98
PL
W artykule przedstawiono wyniki badań stopowych warstw wierzchnich na podłożu ze stali austenitycznej X10CrNi18-8. Analizowane warstwy otrzymano w wyniku laserowego przetapiania podłoża z naniesioną warstwą proszku Fe-Al. Wykonano dyfrakcyjną analizę fazową, obserwacje mikrostruktury otrzymanych warstw wzbogaconych w fazy międzymetaliczne z układu Fe-Al oraz pomiary mikrotwardości. Uzyskane podczas laserowego przetapiania warstwy charakteryzują się silnie rozdrobnioną mikrostrukturą. Znaczny wzrost mikrotwardości w odniesieniu do podłoża był efektem powstania związków międzymetalicznych w analizowanej warstwie wierzchniej. Maksymalna wartość mikrotwardości wynosiła ok. 490 [mi]HV[40].
EN
Alloyed surface layers on X10CrNi18-8 austenitic substrate were presented in this work. The alloyed surface layers after laser melting with powder layer contained Fe-Al intermetalic compounds were analized. Investigated layers were enriched with intermetallic phases from Fe-Al system. X-ray diffraction phase analysis, optical microscopy and microhardness measurements were used to explain relation between phase composition, microstructure and some properties. Laser treatment caused refinement of alloyed ferrite and austenite microstructure and additionally some ordered intermetalic phases. Formed in surface layers intermetallic compounds caused meaningfully increase of microhardness to 490 [mi]HV[40] in comparison with substrate 200 [mi]HV[40].
14
Content available Właściwości ścierne stopów Co-Cr w zawiesinie ceramika-sztuczna ślina
80%
Augustyn-Pieniążek J. , Kurtyka P. , Stopka J.
Engineering of Biomaterials
|
2014
|
tom Vol. 17, no. 127
7--15
PL
Publikacja zawiera wyniki badań odporności na ścieranie stopów Co-Cr-Mo i Co-Cr-Mo-W przeprowadzonych na aparacie Millera. W celu oceny podatności na zużycie ścierne w naturalnych warunkach pracy w/w stopów, badania prowadzono w specjalnie zasymulowanym środowisku, składającym się z ceramicznego proszku Dentyna oraz roztworu sztucznej śliny o pH równym 6,7. W ramach badań przeprowadzono obserwacje mikrostruktury przy wykorzystaniu mikroskopu świetlnego stosując kontrast interferencyjno--różniczkowy (kontrast Nomarskiego), wykonano pomiary twardości, zaś powierzchnie po procesie ścierania poddano obserwacji przy wykorzystaniu elektronowej mikroskopii skaningowej. Na postawie przeprowadzonych badań stwierdzono, że stopy Co-Cr-Mo i Co-Cr-Mo-W charakteryzują się wysoką twardością około 400-450 HV10 i minimalnym ubytkiem masy w procesie ścierania. Cechy te świadczą o wysokiej odporności na ścieranie badanych stopów w środowisku proszek ceramiczny-sztuczna ślina. Dodatkowo stwierdzono również, że trzy z badanych stopów Remanium 2001, Colado CC oraz Heraenium P w odróżnieniu od stopu Wironit LA, posiadają przystanki na krzywych ubytku masy w czasie związane z różnicami twardości materiału osnowy β-Co, wydzieleń węglikowych oraz ramion dendrytów. W przypadku stopu Wironit LA obserwowano równomierne zużycie materiału na całej powierzchni. Stwierdzono również, że pomimo różnic w mechanizmach ścierania pomiędzy stopem Wironit LA I Remanium 2001 wielkość ubytku masy jest dla nich na podobnym poziomie, jednak jest ona znacznie niższa niż dla pozostałych dwóch badanych stopów Colado CC ora Heraenium P.
EN
The publication contains the results of the abrasion resistance tests carried out on Co-Cr-Mo and Co-Cr--Mo-W alloys using Miller apparatus. To assess the susceptibility to abrasive wear of the above mentioned alloys under natural operating conditions, tests were carried out in a specially simulated environment, consisting of a ceramic Dentine powder and artificial saliva solution with pH of 6.7. The scope of studies included the examinations of microstructure performed by light microscopy using differential interference contrast (Nomarski contrast), measurements of hardness, and SEM examinations of surfaces after the abrasion process. The results of these studies enabled formulating the conclusion that alloys from the Co-Cr-Mo and Co-Cr-Mo-W systems are characterised by high hardness of about 400-450 HV10 and minimum weight loss in the process of abrasion. These features prove high abrasive wear resistance of the examined alloys in the environment of ceramic powder and artificial saliva. Additionally, it was also found that three of the tested alloys, i.e. Remanium 2001, Colado CC and Heraenium P, unlike the Wironit LA alloy, show time-related arrests on the weight loss curves caused by different hardness values of the β-Co matrix, carbide precipitates and dendrite arms. The Wironit LA alloy was observed to wear evenly across the whole surface. It was also found that, despite differences in abrasion mechanism operating in the Wironit LA and Remanium 2001 alloys, the magnitude of weight loss has been similar and, at the same time, much lower than for the other two alloys tested, i.e. Colado CC and Heraenium P.
15
Struktura i własności stopów dentystycznych na bazie kobaltu stosowanych do wykonywania protez szkieletowych
80%
Augustyn-Pieniążek J. , Łukaszczyk A. , Szczurek A. , Sowińska K.
Inżynieria Materiałowa
|
2013
|
tom Vol. 34, nr 2
116--120
PL
W pracy przedstawiono wyniki badań materiałów metalowych stosowanych W protetyee dentystycznej do wykonywania m.in. protez szkieletowych. Materiał do badań stanowiły dwa stopy odlewnicze: Co-Cr-Mo i Co-Cr-W-Mo. Przeprowadzono obserwacje mikrostruktury z zastosowaniem mikroskopii świetlnej oraz elektronowej mikroskopii skaningowej (SEM) oraz wykonano mikroanalizę składu chemicznego (EDS) wybranych obszarów zgładów. Na przekrojach próbek wykonano pomiary mikrotwardości sposobem Vickersa. W pracy zaprezentowano również badania odporności korozyjnej przeprowadzone w roztworze sztucznej śliny. Mikrostruktura badanych stopów Co-Cr miała budowę dendrytyczną. W obszarach międzydendrytycznych występowały cząstki wydzieleń Wzbogaconych W takie pierwiastki, jak: Nb, Mo i Si - w przypadku stopu Co-Cr- -Mo oraz Mo i W stop Co-Cr-W-Mo. W osnowie dendrytycznej dominowały Co i Cr. Obszary międzydendrytyczne Wykazywały większą twardość W porównaniu z osnową. Badane materiały wykazywały zbliżoną odporność korozyjną w środowisku sztucznej śliny. Z otrzymanych wartości potencjału bezprądowego oraz na podstawie szerokiego obszaru pasywacji tych stopów można wnioskować o ich dużej odporności korozyjnej w badanym środowisku.
EN
In the paper, the results of investigations of metallic materials used in dentistry for the production of frame dentures are presented. The investigations were carried out using two casting alloys: Co-Cr-Mo and Co-Cr-W-Mo. The specimen microstructures were investigated by light microscopy and scanning electron microscope (SEM) equipped with an X-ray microanalyzer (EDS). The microhardness oft he cross-sections of the specimens was measured. The microstructure of the specimens was of the dendritic type, characteristic for cast alloys. The hardness of the interdendritic areas was higher in comparison to the dendritic matrix because of the M23C6 type carbides. In addition, the corrosion resistance of the cast alloys in an artificial saliva solution was investigated. The results of the open circuit potential method and wide area passivation (Cyclic Voltammetry) of the alloys revealed high corrosion resistance in the investigated alloys.
16
Content available remote Corrosion resistance of titanium alloys in the artificial saliva solution
80%
Loch J. , Krawiec H. , Łukaszczyk A. , Augustyn-Pieniążek J.
Journal of Achievements in Materials and Manufacturing Engineering
|
2016
|
tom Vol. 74, nr 1
29--36
EN
Purpose: The purpose of this article was to characterize the corrosion behaviour and compare two biomedical titanium alloys (Ti-6Al-4V and Ti-10Mo-4Zr) in an artificial saliva solution (MAS) containing lactic acid and hydrogen peroxide (H2O2) used in dentistry. The addition of these two compounds simulate the situation, where the alloy is implanted in the human body and hydrogen peroxide is generated by the inflammatory reaction and lactic acid is release by bacterial in the oral cavity. Design/methodology/approach: In this studies were used following electrochemical techniques: Open Circuit Potential (OCP), Linear Sweep Voltamperometry (LSV), Chronoamperometry at constant potential and Electrochemical Impedance Spectroscopy (EIS). Electrochemical impedance spectra were carried out at the 0.5 V vs. Ag/AgCl potential. The EIS data were fitted using the ZViev software. Findings: The results presented in the work demonstrate that the titanium alloys have a good corrosion resistance. The corrosion behaviour was determined by surface condition of alloys and presence different chemical compounds in the solution. For Ti-10Mo-4Zr titanium alloy in MAS with different concentration of hydrogen peroxide in anodic domain it was seen more clearly. Research limitations/implications: In the future passive films of both titanium alloys will be investigated by: X-ray photoelectron spectroscopy (XPS) and scanning electron spectroscopy (SEM). Originality/value: The corrosion behaviour of biomedical titanium alloy contains molybdenum and zirconium selected as safe alloying elements for human body is presented and compared to commercial Ti-6Al-4V alloy. The corrosion resistance of the titanium alloys was investigated in the artificial saliva solution with addition of lactic acid and hydrogen peroxide.
17
Content available Microstructure and corrosion resistance characteristics of Cr-Co-Mo alloys designed for prosthetic materials
80%
Augustyn-Pieniążek J. , Łukaszczyk A. , Zapała R.
Archives of Metallurgy and Materials
|
2013
|
tom Vol. 58, iss. 4
1281--1285
EN
The work presents the results of microscopic tests of two alloys: Co-Cr-Mo and Co-Cr-W-Mo, together with a quantitative local analysis of the chemical composition, with the use of an electron microprobe X-ray analyzer EDS. Corrosion resistance tests were also performed on the alloys, in the artificial saliva environment. The microstructure of the examined alloys was of the dendrite type. An eutectic consisting of alloy carbides and a cobalt austenite was observed in the interdendritic spaces. The dendritic matrix was a solid solution of chromium, molybdenum and carbon in cobalt (γCo), and the precipitates present in the interdendritic spaces were rich with Cr and Mo - in the case of Co-Cr-Mo - and with W and Mo - in the case of Co-Cr-W-Mo. The analyzed materials exhibited a similar progress of polarization curves. The obtained currentless potential values and the wide passivation area of those alloys made it possible to conclude their high corrosion resistance in the examined environment.
PL
W pracy przedstawiono wyniki badań mikroskopowych dwóch stopów: Co-Cr-Mo i Co-Cr-W-Mo wraz z ilościową analizą punktową składu chemicznego przy wykorzystaniu mikroanalizatora rentgenowskiego EDS. W ramach pracy wykonano również badania odporności korozyjnej stopów w środowisku sztucznej śliny. Mikrostruktura badanych stopów miała budowę dendrytyczną. W przestrzeniach międzydendrytycznych występowała eutektyka składająca się z węglików stopowych i austenitu kobaltowego. Osnowę dendrytyczną stanowił roztwór stały chromu, molibdenu i węgla w kobalcie (γCo), zaś wydzielenia występujące w obszarach międzydendrytycznych były bogate w Cr i Mo - w przypadku stopu Co-Cr-Mo oraz W i Mo - w przypadku stopu Co-Cr-W-Mo. Analizowane materiały wykazywały zbliżone przebiegi krzywych polaryzacji. Z otrzymanych wartości potencjału bezprądowego oraz na podstawie szerokiego obszaru pasywacji tych stopów można wnioskować o ich wysokiej odporności korozyjnej w badanym środowisku.
18
Content available Corrosion Resistance and Microstructure of Recasting Cobalt Alloys Used in Dental Prosthetics
80%
Loch J. , Krzykała A. , Łukaszczyk A. , Augustyn-Pieniążek J.
Archives of Foundry Engineering
|
2017
|
tom Vol. 17, iss. 2
63--68
EN
The work presents the results of the studies of Co-Cr-Mo casting alloys used in the production of frame casts of removable dentures, crowns and bridges in dental prosthetics. The studies were performed on four Co-Cr-Mo alloys of different contents of Mo, W and other additives. Electrochemical tests were performed, which aimed at examining the corrosion resistance of the alloys and observing the alloy structure after chronoamperometric tests with the potential in the area of the occurrence of the passive layer breakpoint. The alloy microstructure images after chronoamperometric tests show the presence of non-uniformly distributed general corrosion. Moreover, a project of cobalt alloy casting was elaborated using a ceramic mold casting. Additionally, analysis of the obtained microstructure was performed. The microstructure of the examined alloys was of the dendrite type. This microstructure was chemically inhomogeneous and consisted of an austenitic matrix formed by a solid cobalt solution and chromium in the core dendritic structure.
19
Content available remote Charakterystyka zdolności chłodzącej wybranych olejów hartowniczych
80%
Adrian H. , Augustyn-Pieniążek J. , Franek J. , Osika M.
Utrzymanie Ruchu
|
2013
|
tom Nr 2
38--41
PL
Szerokie zastosowanie olejów hartowniczych w praktyce hartowania wynika z ich szczególnej zdolności chłodzenia, która zapewnia zmniejszenie występowania odkształceń i pęknięć hartowniczych chłodzonych w nich przedmiotów.
20
Obliczanie własności mechanicznych stali konstrukcyjnych po hartowaniu i odpuszczaniu
80%
Adrian H. , Adrian A. , Augustyn-Pieniążek J. , Głowacz E.
Hutnik, Wiadomości Hutnicze
|
2012
|
tom Vol. 79, nr 4
232--237
PL
W pracy przedstawiono sposób obliczania twardości oraz własności wytrzymałościowych (Re, Rm), plastycznych (A, Z) oraz udarności niskostopowych stali konstrukcyjnych po hartowaniu i odpuszczaniu na podstawie znajomości składu chemicznego i parametrów obróbki cieplnej. Przeprowadzono badania doświadczalne i obliczenia własności dla dwóch gatunków stali do ulepszania cieplnego: 40Cr8 i 34CrMo4. Dla obliczeń opracowano program komputerowy, Quench. Uzyskano zadowalającą zgodność wyników obliczeń z danymi eksperymentalnymi.
EN
The method and data for calculation of the mechanical properties of quenched and tempered structural steels using the chemical composition and heat treatment parameters are presented. The method of calculation was experimentally verified using two structural steels: 40Cr8 and 34CrMo4. For calculations the computer program, Quench, was developed. A satisfied agreement of calculated and experimental mechanical properties of heat treated steels was obtained.
first rewind previous Strona / 2 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.