Effect of holes in overlap on the load capacity of the single-lap adhesive joints made of EN AW-2024-T3 aluminium alloy

100%

Zielecki W. , Burnat K. , Kubit A. , Katrňák T.

tom Vol. 21, nr 4(70)

112--121

The paper presents the results of experimental research aimed at determining the possibilities of strengthening structural adhesive joints. Techniques to improve the strength of adhesive joints was to make holes in the front part of the adherends in order to make the joint locally more flexible in the area of stress concentration at the joint edges. The tests were carried out for the lap joints of EN AW-2024-T3 aluminum alloy sheets, which were bonded with Loctite EA3430 epoxy adhesive. Static tests were carried out on the basis of the tensile/shear test. It has been shown that the applied structural modifications allow for an increase in the strength of the joint, in the best variant, an increase in strength of 14.5% was obtained. In addition, it has been shown that making holes in the adherends allows to reduce the spread of strength results.

Effect of Nanofillers on the Mechanical Properties of Vinyl Ester Resin Used as a Carbon Fiber Reinforced Polymer Matrix

88%

Kubit A. , Bucior M. , Kluz R. , Ochałek K. , Burnat K.

2022

tom Vol. 16, no 4

10--21

This article presents the results of research aimed at determining the influence of selected nanofillers of vinyl ester resin on the mechanical properties of the cured resin. The influence of the resin with nanofillers as a matrix on the properties of the unidirectional CFRP composite was also investigated. Graphite, silicon oxide and titanium dioxide nanopowders were used as resin nanofillers. Each of the fillers was considered in two different contents, i.e. 1 wt.% and 2 wt.%. The variants with such nanofillers content were compared with the unfilled reference variant. The uniaxial tensile strength tests of the resin samples were carried out, showing the possibility of increasing the strength by 19.35% for the variant 1 wt.% of silica nanopowder content. For CFRP composites, the possibility of increasing the strength in the three-point bending test by 25.57% due to the use of a matrix reinforced with graphite nanopowder with a content of 1 wt.% was demonstrated. Based on the analysis of fracture surfaces performed using SEM microscopy, it was shown that the fillers used lead to a significant improvement in the adhesion of the matrix to the composite fibers.