Influence of synthesis conditions on molecular weight as well as mechanical and thermal properties of poly(hexamethylene 2,5-furanate)

100%

Paszkiewicz S. , Irska I. , Walkowiak K. , Zubkiewicz A.

|

2021

|

tom T. 66, nr 10

527--531

EN

Poly(hexamethylene 2,5-furanate) (PHF) was obtained by melt polycondensation. The process was carried out at temperatures of 230, 235 and 240°C. It has been shown that the selection of the optimal parameters of the synthesis process leads to the obtaining of biomaterials of high molecular weight, and thus better mechanical and thermal properties. The relationship between the molecular weight and the mobility of polymer chains, and consequently the temperature of phase changes and mechanical properties, was determined.

PL

Poli(2,5-furanian heksametylenowy) (PHF) otrzymano metodą polikondensacji w stanie stopionym. Proces prowadzono w temperaturze 230, 235 i 240°C. Wykazano, że dobór optymalnych parametrów procesu syntezy prowadzi do otrzymania biomateriałów o dużej masie cząsteczkowej, a tym samym lepszych właściwościach mechanicznych i termicznych. Określono zależność między masą cząsteczkową a ruchliwością łańcuchów polimerowych, a w konsekwencji temperaturą przemian fazowych i właściwościami mechanicznymi.

2

Wpływ recyklatowego pyłu EPDM na właściwości mechaniczne mieszanek kauczukowych

100%

Pypeć K. , Piesowicz E. , Paszkiewicz S. , Irska I.

|

tom T. 100, nr 11

1071--1076

PL

Przedstawiono wyniki opisujące możliwość wykorzystania recyklatowego pyłu EPDM o frakcji 0,0-0,180 mm jako zamiennika napełniaczy mineralnych do wytwarzania mieszanek elastomerowych o korzystnych właściwościach użytkowych. Opracowane mieszanki zawierały w składzie 15, 20, 25, 30, 35% mas. pyłu EPDM. Przeanalizowano ich właściwości przetwórcze oraz parametry wytrzymałościowe w porównaniu z mieszankami zawierającymi standardowo wykorzystywane napełniacze mineralne.

EN

Powdered recyclate waste from the production of EPDM rubber of variable grain size (0.0-0.85 mm) was added to the blends with virgin rubbers in the amts. of 15, 20, 25, 30 or 35% by mass. The processing properties of the blends as well as phys. chem. and mech. parameters of obtained elastomers (d, Mooney viscosity, tensile strength, hardness, abrasion) were analyzed and compared with parameters of elastomers based on standard mineral fillers. Lower values of the mech. strength of the elastomers were obsd. with the use of EPDM-R fines but they did not differ significantly from the values for the mixts. contg. the mineral filler. EPDM recyclate dust with a grain size of 0.0-0.18 mm can be applied as a substitute for mineral fillers for the production of elastomer mixts. with favorable performance properties.

3

Wpływ zawartości octanu winylu w materiałach izolacyjnych na ich właściwości mechaniczne oraz ognioodporność

75%

Paszkiewicz S. , Piesowicz E. , Irska I. , Kozłowski Ł. , Wysocki S. , Siemiński J.

|

2019

|

tom T. 98, nr 7

1153--1157

PL

Przedstawiono wyniki badań dotyczących wykorzystania napełnionych wodorotlenkiem glinu i zmodyfikowanych kopolimerem EVA izolacyjnych materiałów kablowych o różnej zawartości octanu winylu (28% i 40%). Stwierdzono, że wzrost zawartości octanu winylu w materiale powodował zmniejszenie twardości oraz zwiększenie nasiąkliwości materiału, przy jednoczesnym polepszeniu odporności na zużycie ścierne oraz poprawie ognioodporności. Zwiększenie zawartości octanu winylu powodowało również obniżenie wartości modułu sprężystości przy rozciąganiu oraz wytrzymałości na rozciąganie, równocześnie powodując wzrost wydłużenia względnego przy zerwaniu.

EN

Eight ethylene-vinyl acetate copolymers (EVA) with a mass content of vinyl acetate 28% and 40%, resp. were mixed together up to 15% and then blended with low d. polyethylene, a plasticizer and a filler to produce cable insulating materials. Hardness, tensile strength, tensile modulus and abrasion resistance as well as absorbability and fire resistance of the cable materials were detd. in accordance with the relevant stds. Increasing a share of EVA with a higher content of vinyl acetate in the insulation mixt. resulted in a decrease in hardness, tensile modulus, tensile strength and abrasion resistance, as well as in an increase of water absorption and fire resistance.