Modification of a Polylactide Fibre Surface

• Autorzy: Jantas, R. , Połowiński, S. , Stawski, D. , Szumilewicz, J.

Warianty tytułu

PL

Modyfikacja powierzchni włókien polilaktydowych

• Języki publikacji: EN

Abstrakty

EN

The properties of polylactide (PLA) fibres were modified by incorporating carboxyl groups into the fibre surface by grafting acrylic acid (AA) or by the entrapment of poly(acrylic acid) (PAA) to the fibre surface. The presence of a PAA layer was confirmed by IR spectrometry. The number of carboxyl groups incorporated into the top layer of the modified fibres was determined by potentiometric titration. The fibres containing carboxyl groups in their top layer were further treated by the Layer-by-Layer method to deposit basic polyelectrolytes such as poly(allylamine hydrochloride) (PAH) or poly(dimethylaminoethyl methacrylate) (PDAMA) alternately with the layers of acidic polyelectrolyte, i.e. PAA. The presence of successive deposited layers was confirmed by electric charge measurements. The modification performed resulted in changes in the properties of PLA fibres, such as dyeability, water sorption and thermal resistance.

PL

Modyfikowano właściwości włókien polilaktydowych (PLA), wprowadzając grupy karboksylowe na powierzchni włókien metodą szczepienia kwasem akrylowym (AA) lub metodą zakleszczania poli(kwasu akrylowego) (PAA). Obecność warstwy poli(kwasu akrylowego) potwierdzono metodą spektrometrii w podczerwieni. Wprowadzaną ilość grup karboksylowych w warstwie wierzchniej modyfikowanych włókien oznaczano metodą miareczkowania potencjometrycznego. Na włókna z pierwszą warstwą zawierającą grupy karboksylowe nakładano metodą Layer-by-Layer warstwy polielektrolitów zasadowych takich jak chlorowodorek poli(alliloaminy) (PALL) albo poli(metakrylan dimetyloaminoetylu) (PDAMA) naprzemian z warstwami polielektrolitu kwasowego tj. poli(kwasu akrylowego). Potwierdzono obecność kolejnych nakładanych warstw badaniami ładunku elektrycznego. Zaobserwowano zmiany szeregu właściwości takich jak: zdolność do wybawień, sorpcja wody, odporność termiczna.

Słowa kluczowe

PL

włókna polilaktydowe; szczepienie; pułapkowanie; osadzanie warstw po warstwie

EN

polylactide fibres; grafting; entrapment; layer by layer deposition

• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2010
• Tom: Vol. 18, no. 4 (81)
• Strony: 87--91
• Opis fizyczny: Bibliogr. 25 poz., tab., rys.

Twórcy

autor

Jantas, R.

• Department of Physical Chemistry of Polymers, Technical University of Łódź, ul. Żeromskiego 116, 90-924 Łódź, Poland

autor

Połowiński, S.

• Department of Physical Chemistry of Polymers, Technical University of Łódź, ul. Żeromskiego 116, 90-924 Łódź, Poland

autor

Stawski, D.

• Department of Physical Chemistry of Polymers, Technical University of Łódź, ul. Żeromskiego 116, 90-924 Łódź, Poland

autor

Szumilewicz, J.

• Department of Physical Chemistry of Polymers, Technical University of Łódź, ul. Żeromskiego 116, 90-924 Łódź, Poland,

Bibliografia

• 1. S. Gogolewski, M. Jovanovic, S.M. Perren, J.G. Dillon, M.K. Hughes, J. Biomed. Mater. Res. 27 1135 (1993).
• 2. D. Eling, S. Gogolewski, A.J. Pennings, Polymer 23 1587 (1982) i 24 175 1(1983).
• 3. S. Gogolewski, A. J. Pennings, J. Appl. Polym. Sci., 28 1045 (1983).
• 4. J.W. Leenslag, S. Gogolewski, A.J. Pennings, J. Appl. Polym. Sci., 29 2829 (1984).
• 5. L.J. Sumning, H. Garreau, M. Vert. J. Mater. Sci. Mater. In Med. 1 198 (1990).
• 6. S. Li, H. Garreau, M. Vert, J. Mater. Sci. Mater. In Med. 1 123 (1990).
• 7. M. Källrot, U. Edlund, A-S. Albertsson, Biomaterials 27 1788 (2006).
• 8. U. Edlund, M. Källrot, A-C Albertsson, J. Am. Chem. Soc. 127 8865 (2005.)
• 9. N.P. Desai, J.A. Hubbell, Macromolecules, 25, 226 (1992)
• 10. R.A.Quirk, M.C.Davies, S.Tendler, and K.Shakesheff, Macromolecules 33, 258 (2000).
• 11. H. Zhu, J. Shen, Macromol. Rapid Commun.,23, 819 (2002).
• 12. C. Kaiyong, Y. Kangde, Y. Zhiming, L. Xiuqiong, Acta Biomaterialia 3 597 (2007).
• 13. L. Xiaohua,, W. Youngjun, P.X. Ma, J. Biomed.Mater.Res., Part A 74, 84 (2005).
• 14. G. Decher and J. Schlenoff (EDS.),“Multilayer Thin Films”, 2003 Wiley-VCH Weinheim
• 15. S. Połowiński, J. Appl. Polym. Sci. 103, 1700 (2005).
• 16. M. Arslan, Yiğitoğlu, O. Şanh, H. I. Ǜnal, Polym. Bull. 51, 237 (2003).
• 17. C.H. Bamford, K.G. Al. Lamee, Polymer 35, 284 (1994).
• 18. J. Bucheńska, J. Appl. Polym. Sci., 61, 567 (1996).
• 19. S. Połowiński, Polimery, 52, 37 (2007).
• 20. S. Połowiński, Fibers Textiles in Eastern Europe 13(6) 50 (2005).
• 21. R. Jantas, S. Połowiński, Fibers Textiles in Eastern Europe 15 (2) 97 (2007).
• 22. S. Brzeziński, D. Kowalczyk, S. Połowiński, Fibers Textiles in Eastern Europe 17(1) 87 (2009).
• 23. J. Seo, J. Lutkenhaus, J. Kim, P. Hammond, K. Char, Macromolecules 40, 4028 (2007).
• 24. J. Yuan, W. Xing., G. Gu, Wu, Dyes and Pigments 76, 463 (2008).
• 25. S. Yılmaztürk, H. Deligöz, M. Yılmazoĝlu, H. Damyan, F. Öksüzömer, S. Naci Koç, A. Durmuş, A. Gürkaynak, Journal of Membrane Science 343, 137 (2009).