Nanostructure and Thermal Behaviour of Isotactic Polypropylene

• Autorzy: Janicki, J.

Warianty tytułu

PL

Nanostruktura i właściwości termiczne izotaktycznego polipropylenu

• Języki publikacji: EN

Abstrakty

EN

The nonisothermal melting and crystallisation process of isotactic polypropylene was investigated by time-resolved simultaneous small-angle X-ray scattering (SAXS) and wide-angle X-ray diffraction methods with synchrotron radiation. It was found that the nanostructure of the iPP investigated depends on thermal conditions. The nanostructure can be described based on parameters determined from one-dimensional correlation function analysis. It was shown that real-time synchrotron investigation is an appropriate method for describing changes of supermolecular structure parameters during crystallisation and melting process. Changes of long period values, degree of crystallinity, invariant, thickness of crystalline lamellae and thickness of amorphous layers during heating and cooling on wide range of temperature were discussed.

PL

Nieizotermiczne topnienie i proces krystalizacji izotaktycznego polipropylenu badano metodą oznaczenia równoczesnego rozkładów czasowych niskokątowego rozproszenia promieniowania rentgenowskiego (SAKS) oraz metodą szerokokątowej dyfrakcji promieniowania rentgenowskiego z promieniowania synchrotronowego. Stwierdzono, że nanostruktura badanego izotaktycznego polipropylenu zależy od warunków termicznych. Nanostruktura może być opisana na podstawie parametrów wyznaczonych z analizy funkcyjnej korelacji liniowej. Wykazano, że badania synchrotronowe w czasie rzeczywistym są odpowiednią metodą dla opisania parametrów nadmolekularnej struktury podczas krystalizacji i procesu topnienia. Przeprowadzono dyskusję na temat zmian długiego okresu, stopnia krystalizacji, niezmienników, grubości krystalicznych lameli i grubości warstw amorficznych podczas grzania i chłodzenia w szerokim zakresie temperatur.

Słowa kluczowe

PL

polipropylen izotaktyczny; nanostruktura; właściwości termiczne; krystalizacja topnienia; rozpraszanie promieniowania rentgenowskiego pod małym kątem; dyfrakcja rentgenowska szerokokątna

EN

isotactic polypropylene; nanostructure; thermal behaviour; melting crystallisation; small-angle X-ray scattering; wide-angle X-ray diffraction

• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2002
• Tom: Vol. 8, no. 1 (36)
• Strony: 62--65
• Opis fizyczny: Bibliogr. 21 poz., wykr., wz.

Twórcy

autor

Janicki, J.

• Technical Academy of Bielsko-Biała, Textile Institute, ul. Willowa 2, 43-309 Bielsko-Biala, Poland

Bibliografia

• 1.J. Bicerano, Rev. Macromol. Chem. Phys., C38, 391 (1998).
• 2.J. Garbarczyk, Macromol. Chem., 186, 2145 (1985).
• 3.C.C. Hsu, P.H. Geil, H. Miyaji, K. Asai, J. Polym. Sci., Polym. Phys. Ed., 24, 2379 (1986).
• 4.R.L. Miller, Polymer 1, 135 (1960).
• 5.B. Lotz, J.C. Wittmann, J. Polym. Sei., Polym. Phys. Ed., 24, 1541 (1986).
• 6.Strobl G., Eur. Phys. J. E3, 165 (2000).
• 7.B. Lotz, Polymer 39, 4561 (1998).
• 8.A. J. Ryan, J. L. Stanford, W. Bras, T. M. Nye, Polymer, 38, 759 (1997).
• 9.Z.G. Wang et al.. Polymer 42 7561 (2001).
• 10.V.B.F. Mathot, Thermochimica Acta, 1, 355 (2000).
• 11.V.B.F. Mathot, "Calorimetry and Thermal Analysis of Polymers", Hanser Publishers, München (1994).
• 12.httplwww.utk.edul/—athas
• 13.B. Wunderlich, Pure Appl.Chem., 67, 1019 (1995).
• 14.B. Goderis, H. Reynaers, M. H. J. Koch, V.B.F. Mathot, J. Polym. Sci. Polym. Phys. 37, 1715 (1999).
• 15.C. G. Vonk, G. Kortleve, Kolloid - Z.Z,. Polymer, 220, 19 (1967).
• 16.J. T. Koberstein, B. Morra, R. S. Stein, J. Appl. Cryst., 13, 34 (1980).
• 17.W. Ruland, Colloid and Polymer Sci., 255, 417 (1977).
• 18.B. Goderis, M. Peeters, V.B.F. Mathot, M. H. J. Koch, W. Bras, A. J. Ryan, H. Reynaers, J. Polym. Sci. Polym. Phys. Ed. 38, 1975 (2000).
• 19.M.H.J. Koch, J. Bordas, Nucl. Instrum. and Methods, 208, 461 (1985).
• 20.C. J. Boulin, R. Kempf, A. Gabriel, M.H.J. Koch, Nucl. Instrum. and Methods, A357, 178 (1995).
• 21.J. Janicki, "Nanostructure and thermal properties of selected polymer materials", D.Sc. Dissertation, Ed. Technical University of Łódź, Bielsko-Biala Branch, 2001 (in Polish).