Comparative Analysis of the Influenceofthe Kind and Amount of Two Ferromagnetic Nanoadditives on the Structural Properties of Precursor Polyacrylonitrile Fibres

• Autorzy: Boguń, M. , Mikołajczyk, T. , Szparaga, G. , Kurzak, A. , Wójcik, M.

Warianty tytułu

PL

Analiza porównawcza wpływu ilości i rodzaju ferromagnetycznego nanododatku na strukturę oraz właściwości prekursorowych włókien poliakrylonitrylowych

• Języki publikacji: EN

Abstrakty

EN

A comparative analysis of the influence of two different ferromagnetic nanoadditives on the rheological properties of polyacrylonitrile spinning solutions in DMF, as well as on the porous structure and tensile strength properties of nanocomposite fibresobtainedfromthesesolutions, was carried out. A ferromagnetic commercial product of the company Sigma-Aldrich and a product manufactured at the AGH University of Science and Technology, Krakow, Poland were used in this study. The influenceoftheamountofbothtypesofnanoadditives inserted into the fibrematrixontheirstructureandtensilestrengthpropertieswas determined. The uniformity of distribution of the nanoadditive on the fibresurfacewasestimated on the basis of SEM + EDS investigations.

PL

Przeprowadzono analizę porównawczą wpływu dwóch różnych ferromagnetycznych nano dodatków (produktu handlowego firmy Sigma-Aldrich oraz produktu otrzymanego w AGH Kraków) na właściwości reologiczne roztworów poliakrylonitrylu w DMF-ie, strukturę porowatą i właściwości wytrzymałościowe włókien nano kompozytowych uzyskanych z tych roztworów. Określono wpływ ilości obu typów nanododatków wpro­wadzanych do tworzywa włókien na ich strukturę i właściwości wytrzymałościowe. W oparciu o badania SEM+EDS oceniono równomierność rozłożenia nano dodatku na powierzchni włókien.

Słowa kluczowe

PL

włókna prekursorowe; poliakrylonitryl; nanododatek; ferromagnetyczny dodatek; wytrzymałość; struktura porowata

EN

precursor fibres; polyacrylonitrile; nanoadditive; ferromagnetic; tenacity; porous structure

• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2008
• Tom: Vol. 16, no. 5 (70)
• Strony: 48--53
• Opis fizyczny: Bibliogr. 17 poz., rys., tab.

Twórcy

autor

Boguń, M.

• Department of Man-Made Fibres, Faculty of Material Technologies and Textile Design, Technical University of Lodz, Poland, 116 Żeromskiego Street 90-924 Lodz, Poland, tel. (+48) (0-42) 631 33 59 fax. (+48) (0-42) 637 20 40,

autor

Mikołajczyk, T.

• Department of Man-Made Fibres, Faculty of Material Technologies and Textile Design, Technical University of Lodz, Poland, 116 Żeromskiego Street 90-924 Lodz, Poland tel. (+48) (0-42) 631 33 59 fax. (+48) (0-42) 637 20 40

autor

Szparaga, G.

• Department of Man-Made Fibres, Faculty of Material Technologies and Textile Design, Technical University of Lodz, Poland, 116 Żeromskiego Street 90-924 Lodz, Poland tel. (+48) (0-42) 631 33 59 fax. (+48) (0-42) 637 20 40

autor

Kurzak, A.

• Department of Man-Made Fibres, Faculty of Material Technologies and Textile Design, Technical University of Lodz, Poland, 116 Żeromskiego Street 90-924 Lodz, Poland tel. (+48) (0-42) 631 33 59 fax. (+48) (0-42) 637 20 40

autor

Wójcik, M.

• Department of Biomaterials, Faculty of Materials Engineering and Ceramics, AGH University of Science and Technology, Krakow, Poland
• Department of Man-Made Fibres Faculty of Material Technologies and Textile Design Technical University of Lodz 116 Żeromskiego Street 90-924 Lodz, Poland tel. (+48) (0-42) 631 33 59 fax. (+48) (0-42) 637 20 40

Bibliografia

• 1. Sinha Ray, S.:Okamoto, M. Prog Polym Sci 28, 2003, 1539.
• 2. Zhang, Z.; Zhang, L.; Wang, S.; Chen, W.; Lei, Y. Polymer 42, 2001, 8315.
• 3. Liu, Z.T.; Lu, D.S.; Guo, Z.Y. Appl Catal A 118, 1994, 163.
• 4. Hong, Y.; Li, D.; Zheng, J.; Zou, G. Nanotechnology 17, 2006, 1986.
• 5. Deki, S.; Nabika, H.; Akamatsu, K.; Mizuhata, M.; Kajinami, A.; Tomita, S.; Fujii, M.; Hayashi, S. Thin Solid Films 408, 2002, 59.
• 6. Šafařik, I.; Šafařikovǻ, M Monatshefte für Chemie 2002, 133, 737.
• 7. Kriz, C.B.; Radevik, K.; Kriz, D. Anal Chem 68, 1996, 1966.
• 8. Yeh, T.C.; Zhang, W.G.; Ildstad, S.T.; Ho, C. Magnet Reson Med 1995, 33, 200.
• 9. Bulte, J.W.M.; de Cuyper, M.; Despres, D.; Frank, J.A. J Magn Magn Mater 194, 1999, 204.
• 10. Brusentsov, N.A.; Gogosov, V.V.; Brusentsova, T.N.; Sergeev, A.V.; Jurchenko, N.Y.; Kuznetsov, A.A.; Kuznetsov, O.A.; Shumakov, L.I. J Magn Magn Mater 225, 2001, 113.
• 11. Jordan, A.; Scholz, R.; Maier-Hauff, K.; Johannsen, M.; Wust, P.; Nadobny, J.; Schirra, H.; Schmidt, H.; Deger, S.; Loening S.; Lanksch, W.; Felix, R. J Magn Magn Mater 225, 2001, 118.
• 12. Boguń, M.; Mikołajczyk, T. “PAN Nanocomposite Fibres Including a System of Two Nano-additions in their Fibre Matter” J Appl Polym Sci – w druku.
• 13. Boguń, M. “New Generation Precursor PAN Fibres Containing Ceramic Nanoaddition” Doctoral Thesis, Technical University of Lodz, 2007.
• 14. Mikołajczyk, T.; Boguń, M.; Kurzak, A.; Wójcik, M.; Nowicka, K. Fibres Text East Eur 15(3), 2007,19.
• 15. Mikołajczyk, T.; Janowska, G.; Wójcik, M.; Boguń, M.; Kurzak, A. “Influenceof the Amount of Ferromagnetic Addition on the Rheological Properties of Spinning Solutions, the Structure, the Strength and Thermal Properties of Polyacrylonitrile Fibres” J Appl Polym Sci – w druku.
• 16. Mikołajczyk, T.; Boguń, M. Fibres & Textiles in Eastern Europe13(1), 2005, 28.
• 17. Ferguson, J.; Kembłowski, Z. ,,Reologia stosowana płynów”, Wydawnictwo Marcus sc, Łódź, 1995.