Multiple MAG Repair Welding of Steel S1100QL with the Removal of Defective Fragments of Welds Using Mechanical Treatment

• Autorzy: Turyk, E. , Łomozik, M.

Warianty tytułu

PL

Wielokrotne spawanie naprawcze metodą MAG stali S1100QL, z usuwaniem wadliwej części spoiny za pomocą obróbki mechanicznej

• Języki publikacji: EN PL

Abstrakty

EN

The research discussed in the article involved the performance of tests assessing the effect of a one-time and four-time repair welding thermal cycle on mechanical properties of 18 mm thick butt joints made of toughened steel S1100QL. The tests also involved the determination of mechanical properties of a production joint and joints subjected to mechanical treatment-based repair, involving the use of the MAG method (138) and metallic flux-cored wire STEIN-MEGAFIL 1100 M. It was ascertained that the mechanical properties of the joints subjected to mechanical treatment-based repair were similar to those of the joints subjected to repair welding involving the removal of a defective part using arc-air gouging.

PL

Przeprowadzono badania wpływu jedno- i czterokrotnego oddziaływania cyklu cieplnego spawania naprawczego na własności mechaniczne złączy doczołowych blach o grubości 18 mm ze stali ulepszonej cieplnie gatunku S1100QL. Określono własności mechaniczne złącza produkcyjnego oraz złączy naprawianych z użyciem obróbki mechanicznej, wykonywanych metodą MAG drutem elektrodowym proszkowym o rdzeniu metalicznym (proces 138) gatunku STEIN-MEGAFIL 1100 M. Stwierdzono, że własności mechaniczne złączy naprawianych z użyciem obróbki mechanicznej są zbliżone do odpowiednich własności złączy po spawaniu naprawczym z usuwaniem wadliwej części spoiny za pomocą żłobienia elektropowietrznego.

Słowa kluczowe

PL

spawanie naprawcze; stal; S1100QL; właściwości mechaniczne złączy spawanych

EN

repair welding; Steel S1100QL; mechanical properties of joints

• Czasopismo: Biuletyn Instytutu Spawalnictwa w Gliwicach
• Rocznik: 2018
• Tom: Vol. 62, No. 5
• Strony: 65--71
• Opis fizyczny: Bibliogr. 7 poz., rys., wykr., tab.

Twórcy

autor

Turyk, E.

• Professor extraordinary – Instytut Spawalnictwa, Welding Technologies Department

autor

Łomozik, M.

• Professor extraordinary – Instytut Spawalnictwa, Testing of Materials Weldability and Welded Constructions Department

Bibliografia

• [1] Łomozik M., Turyk E.: Mechanical Properties of Welded Joints in Steel S1100QL after Multiple Repair Welding (Własności mechaniczne złączy spawanych stali S1100QL po wielokrotnym spawaniu naprawczym). Biuletyn Instytutu Spawalnictwa, 2018 r., no. 3, doi: 10.17729/ebis.2018.3/1.
• [2] Data sheet 2017 Strenx 1100. Prospekt firmy SSAB. https://venturiacciai.it/wp-content/uploads/2017/03/STRENX-1100-Data-Sheet.pdf, accessed on 14.06.2018
• [3] Drahtzug Stein wire & welding. Seamless flux-cored wire STEIN-MEGAFIL 1100 M. http://www.anapol.ee/images/fsrv/dokumendid/Datasheets/DRAHTZUG/Megafil_1100M.pdf, accessed on 22.08.2017
• [4] Welding Hardox and Weldox. SSAB. http://www.damatech.com/en/files/default/damatech/pdf-EN/11%20Hardox%20plate%20welding%20-%20ENG.pdf. accessed on 10.06.2018
• [5] Welding parameters: STEIN-MEGAFIL 1100M. DRAHTZUG STEIN.
• [6] MEGAFIL Welding parameters – guidance values: metal-cored wires. ITW Welding Europe Corporation.
• [7] Łomozik M., Turyk E.: Badania wpływu spawania naprawczego stali ulepszonych cieplnie o granicy plastyczności powyżej 900 MPa na własności mechaniczne i mikrostrukturę złączy. Sprawozdanie z pracy badawczej no. Hb-109. Instytut Spawalnictwa, Gliwice, 2017

Uwagi

PL

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2019).

PL

Wersja polska artykułu w wydaniu papierowym s. 49-56.

Identyfikatory

DOI

10.17729/ebis.2018.5/6