New methods of ultramarine pigments synthesis from zeolites
Języki publikacji
Abstrakty
The natural ultramarine (lazurite, lapis lazuli) has been known and valued since the ancient times as semiprecious gem applied for jewelry, artistic works, decoration and painting. In Middle Ages it was used as excellent, but very expensive pigment. At the beginning of the nineteenth century a method of synthesis of artificial ultramarine has been discovered and it soon became a common inexpensive commercial product applied mostly for production of paints and as an optical brightener. The procedure included heating of the substrate mixtures (kaolin, sulfur, sodium carbonate, reducing agent) in kilns at high temperature (800°C). The technology of ultramarine production has not been substantially changed up to now, whereas the law regulations concerning environment protection imposed in the twentieth century could not accept a serious air pollution (SO2, H2S) always accompanying the production process. Therefore, searching for novel, environmentally friendly procedures becomes challenging. Ultramarine is an aluminosilicate with sodalite structure that contains sulfur anion-radicals (mostly •S3-) combined with Na+ cations embedded inside ?-cages. The sulfur radicals play a role of chromophores (•S3- blue, •S3- yellow). Sodalite is a zeolite and the sodalite units (?-cages) are constituents of structure of several zeolites (LTA, FAU, LTN, EMT). The use of zeolitic structures for encapsulation of sulfur anion radicals appeared very promising. The direct introduction of sulfur radicals from aprotic solutions of oligosulfides [27] was not successful but the thermal treatment of zeolites mixed with sulfur radical precursors (NaSn, S + alkalis) resulted in colored products analogous to ultramarine [24-26, 30, 31]. Zeolites A seem the most useful for preparation of sulfur pigments but other zeolites can be applied as well. The products of various colors (yellow, green blue and sometimes pinky) and shades can be obtained by choosing appropriate zeolite, radi-cal precursor, kind and content of alkaline cation in the initial mixture, temperature (400-800°C) and time of treatment. It was found that zeolite structure can be maintained upon the thermal treatment or it can be transformed (mostly towards SOD) under highly alkaline thermal treatment. The sulfur radicals can also be embedded inside smaller than ?-cages (e.g. CAN) which favors a generation of smaller radicals (i.e. •S2-) [39-42]. It is also possible to incorporate the sulfur compounds into zeolites during their crystallization and then a generation of radical upon heating. The sulfur pigments based on non aluminosilicate matrices (e.g. AlPO4-20) can be also obtained [38, 53]. Generally use of zeolites allows to obtain ultramarine-like pigments with broad range of colors under much milder than conventional conditions and with much lower emission of polluting agents.
Czasopismo
Rocznik
Tom
Strony
659-682
Opis fizyczny
bibliogr. 57 poz., tab., wykr.
Twórcy
autor
autor
- Uniwersytet im. A. Mickiewicza w Poznaniu, Wydział Chemii, ul. Grunwaldzka 6, 60-780 Poznań, aljan@amu.edu.pl
Bibliografia
- [1] F. Clement, J.B. Desormes, Annales de Chimie, 1806, 57, 317.
- [2] J. Zeltner, Patent nr 1 Cesarskiego Niemieckiego Biura Patentowego (1877).
- |3] F.M. Jaeger, Trans. Faraday Soc, 1929, 25, 320.
- [4] J.R. Morton, 15o College Ampćre. Grenoble Sept. 1968, Amsterdam 1969. 299.
- [5] Y. Matsunaga, Can. J. Chem., 1959, 37, 994.
- [6] D.M. Gardner. O.K. Frankel, J. Am. Chem. Soc., 1955, 77, 6399.
- [7] A.B. Więckowski, D. Mechandzijew, Prace Kom. Mat. Przyr., 1968, 9, 3.
- [8] A.A. Landman, D. de Waal, S. Afr. J. Chem., 2005, 58, 46.
- [9] W. Koch, J. Natterer, C. Henemann, J. Chem. Phys., 1995, 102, 6159.
- [10] N. Gobeltz, A. Demortier, J.P. Lelieur, A. Lorriaux. C. Duhayon, New J. Chem., 1996, 20,19.
- [11] A. Arieli, D.E.W. Vaughan, and D. Goldfarb, J. Am. Chem. Soc. 2004, 126, 5776.
- [12] F. Seel, HJ. Guttler, Angew. Chem.. 1973, 85. 416
- [13] F. Seel, H.J. Guttler, Angew. Chem. Int. Ed. Engl., 1973. 12. 420.
- [14] F. Seel, Stud. Inorg. Chem., 1984, 5, 67.
- [15] J. Plique, Bl. Soc. Chim., Paris N.S., 1877, 28, 522.
- [16] D. Reinen, G.G. Lindner, Chem. Soc. Rev., 1999, 28, 75.
- [17] R.J.H. Clark, T.J. Dines. M. Kurmoo, Inorg. Chem., 1983, 22, 2766.
- [18] H. Schlaich, G.G. Lindner, J. Feldmann, E.O. Gobel, and D. Reinen, Inorg. Chem., 2000,39,2740.
- [19] G.G. Lindner, K. Witkę, D. Schlaich, D. Reinen. D. Inorg. Chim. Acta, 1966, 252. 39.
- [20] E.F. Beleński, J.W. Ryskin, Chemia i Technologia pigmentów, Goschimizda, Moskwa (1949).
- [21] Ch. Baerlocher, W.M. Meier, D.H. Olson. Atlas of zeolite framework types, Elsevier (2001).
- [22] J. Singer, Z. Anorg. Chem., 1932, 204, 232.
- [23] C.A. Kumins, A.E. Gessler, Ind. Eng. Chem., 1953, 45, 567.
- [24] C.A. Kumins, Patent U.S. 2 544 695 (1951).
- [25] I. Ishida, Y. Fujimura. K. Fujiyoshi, M. Wakamatsu, The Ceramic Society of Japan, 1983, 91, 53.
- [26] I. Ishida, Y. Fujimura, K. Fujiyoshi, M. Wakamatsu, The Ceramic Society of Japan, 1982, 90, 326.
- [27] I. Ishida, Y Fujimura, K. Fujiyoshi, Y. Satoh, M. Wakamatsu, The Ceramic Society of Japan, 1984, 92, 579.
- [28] S. Kowalak, M. Stróżyk, M. Pawłowska, M. Miluśka, W. Przystajko, J. Kania, Colloids and Surface A, 1995, 101, 179.
- [29] M.T. Weller. G. Wong, C.L. Adamson, S.M. Dodd, J.J. Roe. J. Chem. Soc. Dalton Trans.. 1990. 593.
- [30] D.E.W. Vaughan, Stud. Surf. Sci. Catal., 2007, 170A, 193.
- [31] S. Kowalak, M. Stróżyk, M. Pawłowska, M. Miluśka, J. Kania, Stud. Surf. Sci. Catal., 1997.105A, 237.
- [32] A. Jankowska, S. Zeidler, S. Kowalak, Proc. of XII Zeolite Forum, Polańczyk, Polish Zeolite Association, Kraków. Poland, 2006.
- [33] A.B. Więckowski, Z. Stuglik, Z. Stróżyk. S. Kowalak, Mol. Phys. Rep.. 2000. 28, 25.
- [34] S.E. Tarling, P. Barnes, L.A. Mackay, J. Appl. Crystallogr. 1984, 17, 96.
- [35] N. Gobeltz, A. Demortier, J.P. Lelieur, C. Duhayon, J. Chem. Soc. Faraday Trans., 1998, 94, 2257.
- [36] S. Kowalak, A. Jankowska, and S. Łączkowska, Stud. Surf. Sci. Catal., 2005, 158A, 215.
- [37] S. Kowalak, A. Jankowska, S. Łączkowska, Catal. Today, 2004, 90, 167.
- [38] R.M. Barren E.A.D. White, J. Chem. Soc, 1952, 2. 1561.
- [39] A. Jankowska. Rozprawa doktorska. Wydział Chemii UAM, Poznań (2004).
- [40] F. Hund. Z. Anorg. Allg. Chem., 1984, 509, 153.
- [41] G.G. Lindner, W. Massa, D. Reinen, J. Solid State. Chem.. 1995, 117, 386.
- [42] S. Kowalak, A. Jankowska, S. Zeidler, A.B. Więckowski, J. Solid State Chem., 2007, 180, 1119.
- [43] S. Kowalak, A. Jankowska, Polish J. Chem., 2008, 82, 131.
- [44] S. Kowalak, A. Jankowska, Micropor. Mesopor. Mater., 2008, 110, 570.
- [45] A. Jankowska, E. Mikołajska, S. Kowalak, Proc. of XIV Zeolite Forum, Kocierz, Polish Zeolite Association, Kraków, Poland, 2007.
- [46] S. Kowalak, A. Jankowska, E. Mikołajska, Proc. of Second International Symposium. Varna, Bułgaria 2007.
- [47] S. Kowalak, A. Jankowska, Micropor. Mesopor. Mater., 2003, 61, 213.
- [48] D.W. Breck, Zeolite Molecular Sieves, J. Wiley, Int. Publ., New York (1974).
- [49] G. Pergo, G. Bellusi, C. Cormo. M. Taramoss. F. Buonamo, A. Esposito, Stud. Surf. Sci. Catal., 1986,28,129.
- [50] R.M. Barrer and J.S. Raitt. J. Chem. Soc, 1954. 4641.
- [51] D.G. Booth, S.E. Dann, M.T. Weller, Dyes and Pigments, 2003, 58, 73.
- [52] S. Kowalak, M. Stróżyk, J. Chem. Soc. Faraday Trans., 1996, 92, 1639.
- [53] M. Ogawa, F. Saito. Chem. Lett., 2004, 33,1030.
- [54] S. Kowatak, A. Jankowska, N. Pietrzak, M. Stróżyk, Stud. Surf. Sci. Catal., 2001, 363.
- [55] G.M. Johnson. P.J. Mead, M.T. Weller, Micropor. Mesopor. Mater., 2000, 38, 445.
- [56] D.E.W. Vaughan, Stud. Surf. Sci. Catal., 2007,170A, 193.
- [57] S. Kowalak, A. Jankowska, E. Baran, Chem. Commun., 2001, 575
Typ dokumentu
Bibliografia
Identyfikatory
Identyfikator YADDA
bwmeta1.element.baztech-article-BUS5-0011-0026