Phase diagram of the Ti-V-C system at 1000 and 1200 C

• Autorzy: Picha, R. , Kroupa, A. , Brož, P.

Warianty tytułu

PL

Wykres fazowy układu Ti-V-C w temperaturze 1000 oraz 1200 st. C

• Języki publikacji: EN

Abstrakty

EN

The ternary Ti-V-C system was studied experimentally at 1000 and 1200°C. Phase diagram data for this system and relevant subsystems has been collected and theoretical assessment was caried out. New thermodynamic parameters in Hillert-Staffansson model were assessed. Experimental results, both own and taken from literature were compared with calculated phase diagrams in order to support and verify suggested data. Reasonable agreement was obtained between the calculation and the experiments.

PL

Zbadano doświadczalnie układ Ti-V-C w temperaturach 1000 oraz 1200°C. Zebrano i krytycznie opracowano dane dotyczące tego układu oraz składowych układów podwójnych. Określono parametry termodynamiczne w modelu Hillerta-Staffanssona. W celu weryfikacji danych porównano obliczony wykres fazowy z rezultatami badań własnych i z literatury. Stwierdzono dobrą zgodność pomiędzy rezultatami z obliczeń oraz z badań.

Słowa kluczowe

PL

wykres fazowy; model Hillerta-Staffanssona; Ti-V-C

EN

phase diagram; Hillert-Staffansson model; Ti-V-C

• Czasopismo: Archives of Metallurgy
• Rocznik: 2001
• Tom: Vol. 46, iss. 2
• Strony: 139-144
• Opis fizyczny: Bibliogr. 13 poz., rys., tab.

Twórcy

autor

Picha, R.

• Department of Theor. and Phys.,Chemistry, Masaryk University, Brno, Czech Republic

autor

Kroupa, A.

• Institute of Physics of Materials, Brno, Czech Republic

autor

Brož, P.

• Department of Theor. and Phys.,Chemistry, Masaryk University, Brno, Czech Republic

Bibliografia

• [1] V.N. Eremenko, L. A. Tret'yachenko, Poroshk. Metall. 6, 27 (1964).
• [2] L. A. Tret'yachenko, V.N. Eremenko, Trudy Soveshch. po Metallkhim., Metalloved. i Primeneniyu Titana i ego Splavov, 6th ed., Nauka, Moscow 75, 1965.
• [3] L.A. Tret'yachenko, V.N. Eremenko, Izv. Akad. Nauk SSSR, Neorg. Mater. 3, 2009 (1967).
• [4] T.F. Fedrov, L. V. Gorshkova, E. T. G ladyshevsky, Izv. Akad. Nauk SSSR 4, 128 (1966).
• [5] E. Rudy, U.S. Air Force Tech. Doc. Report AFML-TR-69-117, Part VII, 1969.
• [6] M. Enomoto, J. of Phase Equilibria 17, 237 (1996).
• [7] M. Hillert, L.I. Staffansson, Acta Chemica Scand. 24. 3618 (1970).
• [8] B. Sundman, B. Jansson, J.O. Andersson, CALPHAD 9, 153 (1985).
• [9] A.T. Dinsdale, CALPHAD 15, 317 (1991).
• [10] K.C. Hari Kumar, P. Wollants, L. Delaey, CALPHAD 18, 71 (1993).
• [11] W. Huang, Metallkd. 82, 703 (1991).
• [12] L. Dumitrescu, submitted for Zeit. fur Metallkd.
• [13] R. Picha, A. Kroupa, P. Broz, J. Bursik, G. Weatherly, To be published.