Influence of anti-foaming admixture and polycarboxylic superplasticizer type on fresh and hardened properties of self-compacting mortar

• Autorzy: Łaźniewska-Piekarczyk, B.
• Języki publikacji: EN

Abstrakty

EN

Research results proved, that some type of superplasticizers (SP) show air-entraining functioning. In order to counteract the excessive air-content in self-compacting mortar the anti-foaming admixtures (AFA) can be applied. Verification of the influence of type, amount and introduction manner of AFA and two type of polycarboxylic SP on air-entrainment, rheological properties and stability of the self-compacting mortar are described in the paper. The research results showed, that the SP and AFA type influence significantly investigated properties of fresh mortars. The hardened properties of the mortars were also investigated. Research results showed, that the AFA type does not influence significantly compressive strength of mortars. The compressive strength of mortars incorporating AFA is similar to mortar with “non air entraining” SP. Moreover, AFA increases significantly the flexural strength of mortar. SEM (Scanning Electron Microscopy) research results showed clearly that admixtures type influence significantly SCC microstructure and values of porosity structure parameters investigated according to EN 480-11.

PL

Wyniki badań wykazały, że niektóre rodzaje superplastyfikatorów (SP) wykazują się działaniem napowietrzającym. W celu przeciwdziałania powstania nadmiernej zawartości powietrza w samozagęszczalnej zaprawie można stosować domieszki przeciwpieniące (AFA). Podjęto badania celem weryfikacji wpływu rodzaju, ilości oraz sposobu dozowania AFA oraz dwóch rodzajów polikarboksylowych SP na napowietrzenie, właściwości reologiczne i odporność na segregację samozagęszczalnych zapraw. Rezultaty badań dowodzą, że rodzaj AFA i SP wpływa istotnie na badane właściwości świeżej zaprawy. Badano także właściwości stwardniałych zapraw. Wyniki badań wykazały, że rodzaj AFA nie wpływa znacząco na wytrzymałość na ściskanie zapraw. Wytrzymałość zaprawy wykonanej z udziałem AFA jest podobna do wytrzymałości zaprawy wykonanej z „nienapowietrzającego” SP. Ponadto wyniki badań dowiodły, że AFA bardzo istotnie wpływa na wytrzymałość na zginanie zapraw. Wyniki analizy SEM udowodniły, że rodzaj domieszki ma zasadnicze znaczenia dla mikrostruktury SCC i wartości parametrów struktury porowatości według EN 480-11.

Słowa kluczowe

PL

antypieniące domieszki; superplastyfikator; urabialność; wytrzymałość na ściskanie

EN

anti-foaming admixtures; superplasticizer; workability; compressive strength

• Czasopismo: Architecture Civil Engineering Environment
• Rocznik: 2010
• Tom: Vol. 3, no. 4
• Strony: 61-72
• Opis fizyczny: Bibliogr. 17 poz.

Twórcy

autor

Łaźniewska-Piekarczyk, B.

• Faculty of Civil Engineering, Silesian University of Technology, Akademicka 5, 44-100 Gliwice, Poland,

Bibliografia

• [1] European Project Group (2005); The European guidelines for self-compacting concrete: specification, production and use. http://www. efnarc. org/ pdf/SCCGuidelinesMay2005.pdf. Available from Internet: 17.01.2010
• [2] Kamal H., Khayat and Joseph Assaad; Air-Void Stability in Self – Consolidating Concrete. ACI Materials Journal, V.99, No.4, July-August 2002; p.408-416
• [3] Khayat K. H.; Optimization and performance of the air-entrained, self-consolidating concrete. ACI Materials Journal, Vol.97, No.5, 2000
• [4] Kobayashi M., Nakakuro E., Kodama K., Negami S.; Frost resistance of superplasticized concrete, ACI SP-68: 1981; p.269-282
• [5] Kucharska L.; Traditional and modern water reducing concrete admixtures, Cement, Wapno, Beton, No.2, 2000; p.46-61 (in Polish)
• [6] Kurdowski W.; Chemistry of building materials. Uczelniane Wydawnictwa Naukowo-Techniczne AGH, Kraków 2003 (in Polish)
• [7] Łaźniewska-Piekarczyk B.; The influence of SP on porosity structure characteristic and durability of SCC. Konferencja Dni Betonu, Tradycja i Nowoczesność, 13-15 Oct. 2008; p.567-576 (in Polish)
• [8] Łaźniewska-Piekarczyk B.; The surface tension of cement paste and its effect on air bubbles formation. 6th International Conference AMCM’2008 Analytical Models and Concepts in Concrete and Masonry Structures, Łódź, 2008; p.229-230 (abstract with paper in CD)
• [9] Litvan G.; Air entrainment in the presence of SP. ACI Journal, Vol. 80, No. 4, 1983; p.326-331
• [10] Młodecki J, Stebnicka I.; Admixtures for concrete. COIB, Warszawa, 1996 (in Polish)
• [11] Mosquet M.; The New generation admixtures. Budownictwo Technologie Architektura, 2003 (In Polish)
• [12] Sakai E., Kasuga T., Sugiyama T, Asaga K., Daimon M.; Influence of superplasticizers on the hydration of cement and the pore structure of hardened cement. Cement and Concrete Research 36, 2006; p.2049-2053
• [13] Szczeniowski Sz.; Eksperimental physics. Part 2., PWN, Warszawa, 1982 (in Polish)
• [14] Szwabowski J., Łaźniewska-Piekarczyk B.; The increase of air content in SCC mixes under the influence of carboxylate SP. Cement-Wapno-Beton, No.4, 2008; p.205-215
• [15] Szwabowski J.; Rheology of cement binder mix. Wydawnictwo Politechniki Śląskiej, Gliwice, 1999 (In Polish)
• [16] Szwabowski J.; The rheology of self-compacting concrete. IV Sympozjum Naukowo-Techniczne “Reologia w technologii betonu”, Gliwice, June 2002; p.61-76 (in Polish)
• [17] Szwabowski J., Łaźniewska B.; Air-entrainment problem in self-compacting concrete. Journal of Civil Engineering and Management International Research and Achievements, Vilnius, Technika, Vol.15, No 2, 2009; p.137-147