The sorption of copper ions by gyrolite in alkaline solution

• Autorzy: Bankauskaite, A. , Baltakys, K.
• Języki publikacji: EN

Abstrakty

EN

Sorption of copper ions by synthetic pure gyrolite (CaO/SiO2 = 0.66; 96 h; 200 °C) in alkaline solutions was examined. When the initial concentration of Cu2+ ions is 1 g/dm3, the cation exchange capacity of the gyrolite is 100 mg Cu2+/g after 360 min of sorption at 25 °C. It has been proved that the cation exchange capacity of gyrolite depends on the concentration of copper ions in the Cu(NO3)2 solution, because a fivefold increase of the concentration (from 1.0 to 5.0 g/dm3) reduces the duration of the ion exchange reaction by a factor of three (from 15 min to 5 min). In solutions with higher initial concentrations of Cu2+ ions (10.0 and 20.0 g/dm3), the sorption proceeds more intensively and all the copper ions are adsorbed in 1 min. It should be noted that the cation exchange reactions are reversible in alkaline solution, because nearly 90% of the copper ions are adsorbed in a physical process, while the remaining part of the cation exchange process takes place in a chemical reaction. Furthermore, the crystal structure of gyrolite is stable in alkaline solution. The products of sorption were characterized by X-ray diffraction, thermogravimetry-differential scanning calorimetry and Fourier-transform infrared spectroscopy methods.

Słowa kluczowe

EN

gyrolite; cation exchange; calcium silicate hydrate; X-ray diffraction

• Czasopismo: Materials Science Poland
• Rocznik: 2009
• Tom: Vol. 27, No. 3
• Strony: 899--908
• Opis fizyczny: Bibliogr. 25 poz.

Twórcy

autor

Bankauskaite, A.

autor

Baltakys, K.

• Department of Silicate Technology, Kaunas University of Technology, Radvilenu 19, LT - 50270 Kaunas, Lithuania

Bibliografia

• [1] HAK-SU K., Ministerial Conference on Environment and Development in Asia and the Pacific 2000 Pollution and Waste, Japan (2000).
• [2] ZHANG Q.R., DU W., PAN B.C., PAN B.J., ZHANG W.M., ZHANG Q.J., XU Z.W., ZHANG Q.X., J. Hazard. Mater., 152 (2008), 469.
• [3] NABI S. A., NAUSHAD MU., INAMUDDIN, J. Hazard. Mater., 142 (2007), 404.
• [4] NABI S.A., SHALLA A. H., KHAN A. M., GANIE S. A., Coll. Surf. A: Physicochem. Eng. Aspects, 302 (2007), 241.
• [5] NABI S. A., NAUSHAD MU., Coll. Surf. A: Physicochem. Eng. Aspects, 293 (2007), 175.
• [6] WANG S., WU H., J. Hazard. Mat., 136 (2006), 482.
• [7] KASPERAVICIUTE V., BALTAKYS K., SIAUCIUNAS R., Ceram. Sil., 52 (2008), 95.
• [8] LABHESTWAR N., SHRIVASTAVA O. P., J. Mater. Sci., 24 (1989), 4359.
• [9] KOMARNENI S., ROY D. M., J. Mater. Sci., 24 (1985), 2930.
• [10] KOMARNENI S., ROY D. M., Nature, 221 (1983), 647.
• [11] KOMARNENI S., TSUJI M., J. Am. Ceram. Soc., 72 (1989), 1668.
• [12] MICHIHIRO M., MASAKI I., TAKASHI S., HIROYUKI K., TAKESHI M., J. Com. Am. Cer. Soc., 73 (1990), 3524.
• [13] SABRY A., EL-KORASHY S.A., Monats. Chemie, 133 (2002), 333.
• [14] AL-WAKEEL E. I., EL-KORASHY S. A., EL-HEMALY S. A., RIZK M. A., J. Mater. Sci., 36 (2001), 2405.
• [15] SIAUCIUNAS R., JANICKIS V., PALUBINSKAITE D., IVANAUSKAS R., Ceram. Sil., 48 (2004), 76.
• [16] SHRIVASTAVA O. P., KOMARENI S., Cem. Concr. Res., 24 (1994), 573.
• [17] KOMARNENI S., ROY R., ROY D. M., Cem. Concr. Res., 12 (1982), 773.
• [18] TSUJI M., KOMARNENI S., J. Mat. Sci., 4 (1989), 698.
• [19] EL-KORASHY S. A., AL-WAKEEL E. I., EL-HEMALY S. A., RIZK M. A., Egypt. J. Chem., 45 (2002), 723.
• [20] MERLINO S., Mineral. Mag., 52 (1988), 377.
• [21] MEYER J. W., JAUNARAJS K. L., Am. Mineral., 46 (1961), 913.
• [22] SHAW S., HENDERSON C. M. B., CLARK S. M., Am. Mineral., 87 (2002), 533.
• [23] EL-KORASHY S. A., AL-WAKEEL E. I., EL-HEMALY S. A., RIZK M. A., Egypt. J. Chem., 46 (2003), 27.
• [24] BALTAKYS K., SIAUCIUNAS R., J. Mater. Sci., 41 (2006), 4799.
• [25] BALTAKYS K., SIAUCIUNAS R., Cem. Concr. Res., 34 (2004), 2029.