Influence of tribomechanical milling and activation of primary mixtures on the synthesis of calcium silicate hydrates

• Autorzy: Palubinskaite, D. , Kantautas, A.
• Języki publikacji: EN

Abstrakty

EN

Tobermorite group minerals with double [Al3++Na+] substitution, using non grind row minerals mixture and grind mixtures in the colloidal mill were syntheses. Calcium silicate hydrate synthesis is going on more intense, when dry primary mixtures ground in a colloid mill are taken, because, having the same synthesis conditions, the compositions of higher crystal degree are synthesized. In this case after 24 h tobermorite forms itself. It is thought, that grinding in a colloid mill a mixture of CaO; SiO2 and Al2O3 some activation centres are induced, which later in the process of hydrothermal processing activate the process of synthesis run. It is reasonable to grind in colloid mill the dry component mixtures, used for synthesis of tobermorite, before hydrothermal processing, until optimum. In the research conditions given the tobermorite formed more intense when original surface was less: S = 547 m2/kg. It is not expedient to use mixtures of smaller primary materials, because stabilizing influence of C-S-H(I) on over forming kinesis of tobermorite displayed itself.

Słowa kluczowe

PL

tobermorit; synteza hydrotermalna; mechaniczna obróbka; obróbka mechaniczna; krzemian wapnia

EN

[Na+ + Al3+]- inserted tobermorite; hydrothermal synthesis; mechanical processing

• Czasopismo: Materials Science Poland
• Rocznik: 2006
• Tom: Vol. 24, No. 2/1
• Strony: 395--403
• Opis fizyczny: Bibliogr. 11 poz.

Twórcy

autor

Palubinskaite, D.

autor

Kantautas, A.

• Faculty of Chemical Technology, Kaunas University of Technology, Radvilenu str. 19, 50254 Kaunas, Lithuania,

Bibliografia

• [1] TRETYAKOV J.D., Solid-State Reactions, Moscow, Khimiya, 1985 (in Russian).
• [2] GORSHKOV V.S., SAVELEV V.G., FEDOROV N.F., Physical Chemistry of Silicates and Other Hardly Fusible Compounds, Moscow, Vysshaya Shkola, 1988 (in Russian).
• [3] BUTYAGIN P., Colloids Surf. A: Physicochem. Eng. Aspects, 160 (1999), 107.
• [4] MI G. M., SAITO F., HANADA M., Powder Technology, 93 (1997), 71.
• [5] MARTUSEVIČIUS M, KAMINSKAS R., MITUZAS J. A., Chemical Technology of Binding Materials, Kaunas, Tekhnologiya, 2002 (in Lithuanian).
• [6] BUTT J.M., RASHKOVICH L.N., Hardening of Binding Materials at High Temperatures, Moscow, Stroiizdat, 1965 (in Russian).
• [7] SIAUCIUNAS R., JANICKIS V., PALUBINSKAITE D., IVANAUSKAS R., Ceramics – Silikaty, 48 (2004), 76.
• [8] NOCUŃN-WCZELIK W., Cement Concrete Res., 29 (1999), 1759.
• [9] NELSON E.B., Cement Concrete Res., 7 (1977), 687.
• [10] COLEMAN N. J., Mater. Res. Bull., 40 (2005), 2000.
• [11] NOCUŃ-WCZELIK W., Cement Concrete Res., 27 (1997), 83.