Admixturing of waste nickel hydroxide to ceramical building materials

• Autorzy: Osińska, M. , Stefanowicz, T.

Warianty tytułu

PL

Odpadowy wodorotlenek niklu jako dodatek do ceramicznych materiałów budowlanych

• Języki publikacji: EN

Abstrakty

EN

Clay destined for bricks production was admixtured with 1, 2, 3 and 10% (d.s.) of nickel hydroxide (the often electroplating sludge component). The burnt-out ceramic brick samples were examined for physical and mechanical properties and for nickel leaching. Samples admixtured within the range of 1-3% did not differ by physical and mechanical properties, while those admixtured with 10% of Ni(OH)2 (non-washed of salts) lost approx. 50% of their initial compressive strength. Nickel concentrations in leachates at water-to-ceramics ratio 10:1 with ceramics admixtured with 10% of Ni(OH)2 (at leaching time 48 h) were below the permissible level. Nickel hydroxide stabilization in ceramics within 1-10% admixtures is considered to be effective and in line with law requirements.

Słowa kluczowe

PL

utylizacja odpadów pogalwanicznych; ceramika budowlana; wodorotlenek niklu

EN

electroplating waste utilization; ceramics; nickel hydroxide

• Czasopismo: Polish Journal of Applied Chemistry
• Rocznik: 2001
• Tom: Vol. 45, nr 3-4
• Strony: 109-116
• Opis fizyczny: Bibliogr. 17 poz., tabl 2, rys. 2

Twórcy

autor

Osińska, M.

• Poznań University of Technology, Institute of Chemistry and Technical Electrochemistry, Piotrowo str. 3, 60-965 Poznań, Poland

autor

Stefanowicz, T.

• Poznań University of Technology, Institute of Chemistry and Technical Electrochemistry, Piotrowo str. 3, 60-965 Poznań, Poland,

Bibliografia

• [1] M.J. CULLINANE Jr., L.W. JONES, P.O. MALONE, Handbook for Stabilization/Solidification of Hazardous Waste, EPA/540/2-86/001, Cincinnati, OHIO, June (1986).
• [2] J. BUDILOVSKY, The Economyst of Lithuania (3), 61, (1991).
• [3] Cerificates issued by Building Research Institute in Warsaw - Świadectwa nr Og-193/91 i Og-222/91wydane przez Instytut Techniki Budowlanej w Warszawie, (1991).
• [4] http:/www.igo.katowice.pl/bazy/techkraj/tk249.htm.
• [5] T. STEFANOWICZ, M. OSIŃSKA, Archiwum Ochrony Środowiska, vol. 24, nr 4, 175 (1998).
• [6] T. STEFANOWICZ, M. DUDKA, M. OSIŃSKA, Chemik, LI, nr 6, 155, (1998).
• [7] T. STEFANOWICZ, M. OSIŃSKA, S. NAPIERALSKA-ZAGOZDA, Arch. Ochr. Śród., vol. 26, nr 34,137, (2000).
• [8] T. STEFANOWICZ, M. SŁOWIK, M. OSIŃSKA, Chemik, LIV, nr 5, 111, (2001).
• [9] T. STEFANOWICZ, M. OSIŃSKA, E. KOSTKA, Ekologia i Technika, nr 3, (2001).
• [10] M. PINTA, Absorpcyjna spektrometria atomowa, PWN, Warszawa, (1977).
• [11] Dziennik Ustaw 1991, nr 116 z dn. 5.XI. 1991, poz. 503, Rozporządzenie Ministra Ochrony Środowiska, Zasobów Naturalnych i Leśnictwa - załącznik nr 2.
• [12] Polska Norma PN-70/B-12016. Wyroby ceramiki budowlanej. Badania techniczne.
• [13] Polska Norma PN-70/B-12001. Cegła pełna wypalana z gliny - zwykła.
• [14] Norma: "Technische Verordnung über Abfalle", (TVA) As.1991 vom 10 Dezember 1990, Der Schweizerische Bundesrat.
• [15] Polska Norma PN-Z-15009. Odpady stałe - Przygotowanie wyciągu wodnego.
• [16] Rozporządzenie Ministra Gospodarki z dnia 21.X.1998 "w sprawie szczegółowych zasad usuwania, wykorzystywania i unieszkodliwiania odpadów niebezpiecznych", Dz.U. nr 145, poz. 942.
• [17] Rozporządzenie Ministra Ochrony Środowiska, Zasobów Naturalnych i Leśnictwa z dnia 5.XI. 1991 "w sprawie klasyfikacji wód oraz warunków, jakim powinny odpowiadać ścieki wprowadzane do wód i do ziemi", Dz.U. 1991 nr 116, poz. 503.