Phase transformations in ULCB_Mn steel cooled from (alpha+gamma) range.

• Autorzy: Kolan, C. , Lis, A. K.
• Konferencja: XVIth Physical Metallurgy and Materials Science Conference on Advanced Materials and Technologies AMT'2001, Gdańsk-Jurata, 16-20 September, 2001
• Języki publikacji: PL

Abstrakty

EN

The aim of the investigation was to establish the conditions for dual-phase microstructure formation which consists of bainite-martensite (BM) islands in ferrite matrix of ultra low carbon bainitic steel (ULCB_Mn) bearing about 3.7% Mn. The kinetic of austenite formation during the heating up at rate V5-8=0.6K/s process was determined to establish the temperature of intercritical annealing for a predetermined austenite content. The phase transformations of newly formed austenite within (alpha+beta) range during continuous cooling at a rate V8-5=0.6/30 K/s were studied. The intercritical annealing simulations were conducted for the commercially produced cold-rolled material. The influence of annealing temperature at (alpha+gamma) range and the volume fraction of BM islands formed during cooling down on the mechanical properties of sheets of 04G4Ti steel was established.

PL

Celem badań było ustalenie warunków tworzenia się dwoistofazowej struktury złożonej z wysp bainityczno-martenzytycznych (BM) w osnowie ferrytycznej stali ULCB_Mn zawierającej około 3.7% Mn. Dla określenia temperatury międzykrytycznego wyżarzania oraz ilości nowopowstałego austenitu wyznaczono kinetykę przemiany alfa->gama dla V5-8=0.6K/s. Badano przemiany fazowe nowoutworzonego austenitu w zakresie (alfa+gama) dla warunków ciągłego chłodzenia w zakresie szybkości V8-5=0.6/30 K/s. Przeprowadzono symulację międzykrytycznego wyżarzania taśm zimnowalcowanych produkowanych przemysłowo. Określono wpływ temperatur wyżarzania w zakresie dwufazowym (alfa+beta) i różnej ilości wysp BM powstałych przy chłodzeniu na własności mechaniczne taśm ze stali 04G4Ti.

Słowa kluczowe

PL

przemiana fazowa; stal ULCB_Mn; struktura dwoistofazowa; wyżarzanie; chłodzenie; właściwości mechaniczne; symulacja; kinetyka; własności mechaniczne przy rozciąganiu; skład chemiczny

EN

phase transformation; ULCB_Mn steel; dual-phase microstructure; annealing; cooling; mechanical properties; simulation; kinetics; tensile properties; chemical composition

• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2001
• Tom: R. XXII, nr 4
• Strony: 458-461
• Opis fizyczny: Bibliogr. 6 poz., tab., rys.

Twórcy

autor

Kolan, C.

• Technical University of Częstochowa

autor

Lis, A. K.

• Technical University of Częstochowa

Bibliografia

• [1] Mould P. R., Skena C. C.: Struaure and properties of cold-rolled ferrite-martensite (duaii-phase) steel sheets, Fornable HSLA and Dual Phase steels, wyd. The Metallurgical Society of AIME, New York, 1979, pp. 181-204.
• [2] Ciszewski B, Przetakiewicz W.: Nowoczesne Materiały w Technice, Warszawa 1993, Wyd. Bellona, pp. 21.
• [3] Hartman G, Heckelmann I., Menne M: HSZ 220 and 260 Steel with exellent stretch formability, Steels and Materials for Power Plants, Euromat’99, Vol. 7, WILEY-VCH, Germany, 2000, pp 198-201.
• [4] Lis A. K., Kolan C.: Quantification of dual-phase microstiuctures of ULCB_Mn steel after thermomedunical rolling. Proceedings International Conference on „The Quantitative Description of Materials Microstructure QMAT’97’, Warsaw, 1997, Poland, pp 371-376.
• [5] Kolan C., Lis A.K.; Matematycmy opis przemian przy nagrzewaniu i chłodzeniu bardzo niskowęglowych sali manganowych, XXVIII Szkoła Inżynierii Materiałowej, AGH, Szczawnica – Kraków, 2000, pp. 29-34.
• [6] Kolan C., Lis A.K.: Modelowanie kompozytową struktury i własności stali ULCB_Mn, Nowe technologie i osiągnięcia w metalurgii i inżynierii materiałowej, Wyd. Wydziału Metalurgii i Inżynierii Materiałowej Politechniki Częstochowskiej, Częstochowa, 2000, pp. 272-278