Effect of the retrogression and reageing heat treatment on mechanical properties, dislocation structure, susceptibility to stress corrosion cracking and fracture mode of the AlZn5Mg1 alloy.

• Autorzy: Chrzanowski, J. , Gazda, A. , Warmuzek, M. , Jezierska, E. , Zieliński, A.
• Konferencja: XVIth Physical Metallurgy and Materials Science Conference on Advanced Materials & Technologies AMT'2001, Gdańsk-Jurata, 16-20 September 2001
• Języki publikacji: PL

Abstrakty

EN

The time-to-failure, RRA and fracture energy was measured in Slow Strain Rate Test in air and seawater, and dislocation structure and fracture mode examined with the transmission and scanning electron microscopes for the AlZn5Mg1 alloy. The observed change in the alloy behaviour was attributed to change in its microstructure.

PL

Czas do zniszczenia, przewężenie i energia zniszczenia stopu AlZn5Mg1 mierzone były w trakcie powolnego rozciągania w wodzie morskiej i powietrzu, a struktura dyslokacyjna i przełomy analizowane metodami mikroskopii elektronowej. Obserwowane zmiany zachowania się stopu przypisano zmianom jego mikrostruktury.

Słowa kluczowe

PL

pękanie korozyjne naprężeniowe; zniszczenie; energia przełomu; rodzaj przełomu; woda morska; powietrze; struktura dyslokacyjna; własności mechaniczne; nawrót; obróbka cieplna; starzenie; stop

EN

stress corrosion cracking; failure; fracture energy; fracture mode; sea water; air; dislocation structure; mechanical properties; retrogression; reageing; alloy

• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2001
• Tom: R. XXII, nr 4
• Strony: 253-254
• Opis fizyczny: Bibliogr. 5 poz., tab., rys.

Twórcy

autor

Chrzanowski, J.

• Technical University of Gdańsk, Poland

autor

Gazda, A.

• Institut of Foundry, Polish Academy of Sciences, Kraków, Poland

autor

Warmuzek, M.

• Institut of Foundry, Polish Academy of Sciences, Kraków, Poland

autor

Jezierska, E.

• Technical University of Warsaw, Poland

autor

Zieliński, A.

• Technical University of Gdańsk, Poland

• Technical University of Gdańsk

Bibliografia

• [1] Zieliński A.: Niszczenie wodorowe metali nieżelaznych i ich stopów Gdańskie Towarzystwo Naukowe, Gdańsk, 1999.
• [2] Braun R.: Environmentally assisted cracking of aluminium alloys in chloride Solutions, Proceedings of ICAA-6, Aluminium Alloys, Vol. 1 (1998)153.
• [3] Talianker M., Cina B.: Retrogression and Reaging and the dislocations of 7000-type aluminium alloys. Metall. Trans. A, 20 A (1989) 2087.
• [4] Katoh Y., Tomita K., Sakaguchi M., Nakazawa Y.: Effect of RRA treatment on SCC susceptibility of Al.l.IMg-l.0Si-0.5Cu alloy, Proceedings of ICAA-6, Aluminium Alloys, Vol. 3 (1998) 1687.
• [5] Nakai M., Eto T.: New retrogression and reaging process for high strength and high stress corrosion resistance 7050 aluminum alloys. Proceedings of ICAA-6, Aluminium Alloys, Vol. 3 (1998) 1621.