Multiphase sintering of iron-copper-iron boride cermets.

• Autorzy: Nowacki, J. , Wysiecki, M.

Warianty tytułu

PL

Spiekanie reakcyjne cermetali żelazo-miedź-borek żelaza.

• Języki publikacji: EN

Abstrakty

EN

Multiphase sintering of a mixture of iron, copper and boron powder of a concentration of 5-15 wt. of copper and 9 wt. of boron has been analyzed. The powder mixture was milled, pressed and sintered in a vacuum at temperature of 1100 stopni C (1373 K) and time of 30-180 min. Multiphase sintering process leads to the formation of the iron-copper boride (FeCu)2B grains of hardness of 1700 HV0.1 seated in the eutectic mixture Cu-B (alpha +beta) of hardness 600-700 HV0.1, and a porosity of 0.5-3%, depending on the sintering conditions. The combination of such components results in promising mechanical properties of sinters: high hardness and satisfactory ductility.

PL

Analizowano proces spiekania reakcyjnego mieszaniny proszku żelaza z domieszką 5-15% miedzi i 9% boru. Wytworzono cermetale żelazo-borek żelaza Fe-Cu-(FeCu)2B, w których borek (FeCu)2B, o twardości około 1700 HV, jest osadzony w mieszaninie eutektycznej Cu-B (alfa + beta) o twardości 600-700 HV. Skład ten zadecydował o dużej twardości (1450 HV), stałej w całym przekroju spieku, i dobrej ciągliwości. W czasie spiekania występują procesy cząstkowe: dyfuzja boru do żelaza w fazie stałej, utworzenie się fazy ciekłej - eutektyki Cu-B (alfa + beta), dyfuzja boru i żelaza do fazy ciekłej oraz boru i miedzi z fazy ciekłej do żelaza.

Słowa kluczowe

PL

spiek; borki żelaza; cermetal

EN

sinters; iron borides; cermets

• Czasopismo: Postępy Technologii Maszyn i Urządzeń
• Rocznik: 1998
• Tom: vol. 22, nr 2
• Strony: 89-98

Twórcy

autor

Nowacki, J.

autor

Wysiecki, M.

• Technical University of Szczecin [Politechnika Szczecińska],