Evaluation of protective properties of concretes made of cements with calcareous fly ash with respect to reinforcing steel

• Autorzy: Śliwka, A. , Domagała, K.

Warianty tytułu

PL

Ocena właściwości ochronnych względem stali zbrojeniowej betonów na cementach zawierających popioły wapienne

• Języki publikacji: EN PL

Abstrakty

EN

The studies on the protective properties of concrete made of cements containing calcareous fly ash are presented in the paper. The aim of the studies carried out by electrochemical methods was to determine the susceptibility of reinforcing steel corrosion, protected by the analysed concretes, as well as to define the rate of reinforcement corrosion installed in the loaded and cracked samples , subjected additionally to the action of chloride solution. The obtained results were compared with the values of Portland cement concrete, considered as reference. The results showed that the addition of up to 50% calcareous fly ash do not reduce the protective properties of concretes with respect to reinforcing steel , while the use of fly ash together with blast furnace slag leads to the deterioration of reinforcement.

PL

W artykule przedstawiono badania właściwości ochronnych betonu wykonanego na cementach zawierających lotne popioły wapienne. Badania prowadzone metodami elektrochemicznymi miały na celu określenie podatności korozyjnej stal i zbrojeniowej , chronionej analizowanymi betonami, oraz wyznaczenie szybkości korozji zbrojenia umieszczonego w obciążonych i zarysowanych elementach próbnych pod wpływem chlorków. Uzyskane wyniki porównywano z poziomem odniesienia, który stanowiły wartości pomierzone w seri i referencyjnej z betonu na cemencie portlandzkim. Badania wykazały, że zastosowanie w cemencie do 50% lotnych popiołów wapiennych nie powoduje pogorszenia właściwości ochronnych betonów względem stali zbrojeniowej. Natomiast zastosowanie oprócz lotnych popiołów wapiennych żużla wielkopiecowego prowadzi do zwiększenia podatności korozyjnej zbrojenia.

Słowa kluczowe

PL

gęstość prądu korozyjnego; podatność korozyjna; pomiary elektrochemiczne; popioły wapienne; szybkość korozji

EN

calcareous fly ash; corrosion current; orrosion current density; corrosion rate; corrosion susceptibility; electrochemical measurements

• Czasopismo: Roads and Bridges - Drogi i Mosty
• Rocznik: 2013
• Tom: Vol. 12, no. 2
• Strony: 237-250
• Opis fizyczny: Bibliogr. 15 poz., rys., tab.

Twórcy

autor

Śliwka, A.

autor

Domagała, K.

• Politechnika Śląska w Gliwicach, Katedra Konstrukcji Budowlanych,

Bibliografia

• [1] Montemor M.F., Simoes A.M., Salta M.M.: Effect of fly ash on concrete reinforcement corrosion studied by EIS. Cement and Concrete Composites, 22,3,2000,175 -185
• [2] Montemor M.F., Cunha M.P., Ferreira M.G., Simoes A.M.: Corrosion behaviour of rebars in fly ash mortar exposed to carbon dioxide and chlorides. Cement and Concrete Composites, 24, 1, 2002, 45 - 53
• [3] Hossain K.M.A., Lachemi M.: Corrosion resistance and chloride diffusivity of volcanic ash blended cement mortar. Cement and Concrete Research, 34, 4, 2004, 695 - 702
• [4] AmpaduK.O., ToriiK.: Chloride ingress and steel corrosion in cement mortars incorporating low-quality fly ashes. Cement and Concrete Research, 32, 6, 2002, 893 - 901
• [5] Saraswathy V., Muralidharan S., Thangavel K., Sriniva san S.: Influence of activated fly ash on corrosion-resistance and strength of concrete. Cement and Concrete Composites, 25, 7, 2003, 673 - 680
• [6] Jiang L., Liu Z., YeY.: Durability of concrete incorporat ing large volumes of low-quality fly ash. Cement and Concrete Research, 34, 8, 2004, 1467 - 1469
• [7] Kayali O., Zhu B.: Chloride inducted reinforcement corrosion in lightweight aggregate high-strength fly ash concrete. Construction and Building Materials, 19,4, 2005, 327 – 336
• [8] Pacewska B., Bukowska M., Wilińska I., Swat M.: odification of the properties of concrete by a new pozzolan. A waste catalyst from the catalytic process in a fluidized bed. Cement and Concrete Research, 32, 1,2002, 145 - 152
• [9] Brandt A.M. (red.): Zastosowanie popiołów lotnych z kotłów fluidalnych w betonach konstrukcyjnych. Studia z Zakresu Inżynierii nr 72, IPPT PAN, Warszawa, 2010
• [10] PN-86/B-01810 Antykorozyjne zabezpieczenia w budownictwie. Własności ochronne betonu w stosunku do stali zbrojeniowej. Badania elektrochemiczne [11] Wieczorek G.: Korozja zbrojenia inicjowana przez chlorki lub karbonatyzację otuliny. Dolnośląskie Wydawnictwo Edukacyjne, Wrocław, 2002
• [12] Wieczorek G., Sokalska A.: Modelowanie ciekłego środowiska korozyjnego w betonach skażonych chlorkami . Ochrona przed Korozją, 5, 1977, 132 - 136
• [13] DIN 488-1:2006 Reinforcingsteels: Grades, properties, marking
• [14] PN-EN 480-14:2008 Domieszki do betonu, zaprawy i zaczynu. Metody badań. Część 14: Oznaczanie podatności korozyjnej stali zbrojeniowej w betonie za pomocą potencjostatycznego badania elektrochemicznego
• [15] Andrade C., Alonso M.C., Gonzalez A.: An initial effort to use the corrosion rate measurements for estimating rebar durability. Corrosion rates of steel in concrete. ASTM STP 1065, Berke, Chackerand Whiting, Philadelphia, 1990, 29 - 37