One of the most important factors directly affecting microstructure and mechanical properties in directional solidification process is secondary dendrite arm spacing (SDAS). It is very important to measure the SDAS and examine the factors that may affect them. To investigate the effect of growth rate on the SDAS, the alloy specimens were directional solidified upward with different growth rates (V = 8.3-83.0 μm/s) at a constant temperature gradient (G = 4 K/mm) in a Bridgman-type growth apparatus. After the specimens are directionally solidified, they were exposed to metallographic processes in order to observe the dendritic solidification structure on the longitudinal section of the specimens. Coarsen secondary dendrite arm spacings (λ2C) were measured excluding the first arms near the tip of the dendrite. Local solidification times ( tf) were calculated by ratio of spacings to growth rates. It was determined that the tf values decreased with increasing V values. The relationships between tf and λ2C were defined by means of the binary regression analysis. Exponent values of tf were obtained as 0.37, 0.43, 0.46 and 0.47 according to increasing V values, respectively. These exponent values are close to the exponent value (0.33) predicted by the Rappaz-Boettinger theoretical model and good agreement with the exponent values (0.33-0.50) obtained by other experimental studies.
Czasopismo
Rocznik
Tom
Strony
931--938
Opis fizyczny
Bibliogr. 49 poz., fot., rys., tab., wzory
Twórcy
autor
- Niğde Ömer Halisdemir University, Institute of Science, Department of Physics, Niğde, Turkey, 0000-0002-7745-396X
autor
- Niğde Ömer Halisdemir University, Institute of Science, Department of Physics, Niğde, Turkey, ecadirli@gmail.com
Bibliografia
- [1] M.C. Flemings, Mater. Trans. A. 46 (5), 895-900 (2005).
- [2] Y. Sun, W.B. Andrews, K. Thornton, P.W. Voorhees, Sci. Rep. 8 (1), 17940 (2018).
- [3] D. Kammer, P.W. Voorhees, Acta Mater. 54 (6), 1549-1558 (2006).
- [4] S.P. Marsh, M.E. Glicksman, Metall. Trans. A. 27 (3), 557-567 (1996).
- [5] H. Neumann-Heyme, N. Shevchenko, Z. Lei, K. Eckert, O. Keplinger, J. Grenzer, C. Beckermann, S. Eckert, Acta Mater. 146, 176-186 (2018).
- [6] T. Cool, P.W. Voorhees, Acta Mater. 127, 359-367 (2017).
- [7] J.L. Fife, P.W. Voorhees, Acta Mater. 57 (8), 2418-2428 (2009).
- [8] S. Terzi, L. Salvo, M. Suery, A.K. Dahle, E. Boller, Acta Mater. 58 (1), 20-30 (2010).
- [9] N.L.M. Veldman, A.K. Dahle, D.H. Stjohn, L. Arnberg, Metall. Trans. A. 32, 147-155 (2001).
- [10] L. Collini, G. Nicoletto, R. Konecna, Mater. Sci. Eng. A. 488 (1-2), 529-539 (2008).
- [11] K.P. Young, D.H. Kirkwood, Metall. Trans. A. 6, 197-205 (1975).
- [12] B. Li, Ph.D. Thesis, University of Connecticut, Connecticut (2004).
- [13] T.Z. Kattamis, J.C. Coughlin, M.C. Flemings, T. Metall. Soc. AIME 239, 1504-1511 (1967).
- [14] M.C. Flemings, D.R. Poirier, R.V. Barone, H.D. Brody, JISI Lond. 208, 371-381 (1970).
- [15] M.C. Flemings, Metall. Trans. B. 5, 2121-2134 (1974).
- [16] U. Feurer, R. Wunderlin, Fachbericht der Deutschen Gesellschaft für Metallkunde, Oberursel, FRG, 1977.
- [17] K.J. Oswald, M.S. Misra, AFS Trans. 88, 845-862 (1980).
- [18] A. Inoue, M. Kohinata, A. Tsai, T. Masumoto, Mat. Trans. JIM 30 (5), 378-381 (1989).
- [19] P. Dantzer, J. Less-Common Met. 131 (1-2), 349-363 (1987).
- [20] H. Feufel, F. Schuller, J. Schmid, F. Sommer, J. Alloys and Compds. 267, 234-244 (1997).
- [21] P.P. Choi, J.S. Kim, O.T.H. Nguyen, D.H. Kwon, Y.S. Kwon, J.C. Kim, Mater. Sci. Eng. A. 449-451, 1119-1122 (2007).
- [22] M. Rappaz, W.J. Boettinger, Acta Mater. 47 (11), 3205-3219 (1999).
- [23] H.-J. Diepers, C. Beckermann, I. Steinbach, Acta Mater. 47 (13), 3663-3678 (1999).
- [24] S. Steinbach, L. Ratke, Mat. Sci. Eng. A. 413-414, 200-204 (2005).
- [25] M. Easton, C. Davidson, D. St John, Metall. Trans. A 41 (6), 1528-1538 (2010).
- [26] E. Üstün, E. Çadırlı, J. Alloys and Compds. 855, 157331 (2021).
- [27] M. Jaradeh, T. Carlberg, Mat. Sci. Technol. 23 (4), 475-482 (2007).
- [28] M. Kahlweit, Scripta Metall. 2 (5), 251-254 (1968).
- [29] M.C. Flemings, T.Z. Kattamis, B.P. Bardes, AFS Trans. 176, 501-506 (1991).
- [30] M. Tiryakioğlu, Metall. Trans. A. 50, 3030-3032 (2019).
- [31] A. F. Ferreira, J.A. Castroa, L.O. Ferreira, Materials Research 20 (1), 68-75 (2016).
- [32] I.L. Ferreira, A.L.S. Moreira, J.A.S. Aviz, T.A. Costa, O.L. Rocha, A.S. Barros, A. Garcia, J. Manuf. Process. 35, 634-650 (2018).
- [33] M. Chen, T.Z. Kattamis, Mater. Sci. Eng. A. 247 (1-2), 239-247 (1998).
- [34] B. Donadoni, G.L. Gouveia, A. Garcia, J.E. Spinelli, J. Manuf. Process. 54, 14-18 (2020).
- [35] P.A.D. Jacome, M.C. Landim, A. Garcia, A.F. Furtado, I.L. Ferreira, Thermochim. Acta 523 (1-2), 142-149 (2011).
- [36] A. Juarez-Hernandez, H. Jones, J. Cryst. Growth 208 (1-4), 442-448 (2000).
- [37] G. Matache, D. M. Stefanescu, C. Puscasu, E. Alexandrescu, Int. J. Cast Metal. Res. 29 (5), 303-316 (2016).
- [38] G. Matache, D. M. Stefanescu, C. Puscasu, E. Alexandrescu, A. Bührig-Polaczek, Int. J. Cast Metal. Res. 28 (6), 323-336 (2015).
- [39] Q. S. Hamed, R. Elliott, Cast Metals 6 (1), 36-41 (1993).
- [40] V. Ronto, A. Roosz, Int. J. Cast Metal. Res. 13 (6), 337-342 (2001).
- [41] V. Ronto, A. Roosz, Int. J. Cast Metal. Res. 14 (2), 131-135 (2001).
- [42] J. He, J.M. Zeng, A. Yan, Adv. Mater. Res. 51, 8-92 (2008).
- [43] T. Sivarupan, C.H. Caceres, J.A. Taylor, Metall. Trans. A 44 (9), 4071-4080 (2013).
- [44] R. Chen, Y.F. Shi, Q.Y. Xu, B.C. Liu, Trans. Nonferrous Met. Soc. China 24 (6), 1645-1652 (2014).
- [45] H. Liao, Y. Sun, G. Sun, Mater. Sci. Eng. A. 335 (1-2), 62-66 (2002).
- [46] J.A. Dantzig, M. Rappaz, Solidification, EPFL Press, Lausanne, Switzerland (2009).
- [47] V. Fourlakidis, A. Dioszegi, Mater. Sci. Eng. A. 618, 161-167 (2014)
- [48] H.P. Tang, Q.D. Wang, C. Lei, B. Ye, K. Wang, H.Y. Jiang, W.J. Ding, X.F. Zhang, Z. Lin, J.B. Zhang, J. Alloys and Compds. 801, 596-608 (2019).
- [49] J. Wang, G. Yang, Acta Mater. 56 (17), 4585-4592 (2008).
Uwagi
Opracowanie rekordu ze środków MNiSW, umowa nr SONP/SP/546092/2022 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2024).
Typ dokumentu
Bibliografia
Identyfikatory
Identyfikator YADDA
bwmeta1.element.baztech-244fe116-79c7-4fa6-b9ab-f10054e92f9b