Flammability of plywood made from veneers protected with flame retardant based on diammonium hydrogen phosphate, citric acid and sodium benzoate

• Autorzy: Borysiuk P. , Jaskolowski W. , Boruszewski P. , Jenczyk-Tolloczko I. , Jablonski M. , Bylinski D.

Warianty tytułu

PL

Palnośćsklejek wytworzonych z fornirów zabezpieczonych środkiem ogniochronnym na bazie wodorofosforanu amonu, kwasu cytrynowego i benzoesanu sodu

• Języki publikacji: EN

Abstrakty

EN

Flammability of plywood made from veneers protected with flame retardant based on diammonium hydrogen phosphate, citric acid and sodium benzoate. In this study the impact of pine and beech veneer protection with flame retardant based on diammonium hydrogen phosphate, citric acid and sodium benzoate on the flammability of plywood made from them has been determined. Retention of the agent in veneers was 47 - 50 kg per 1 m3. It was determined that impregnated plywood manufactured from veneers do not sustain burning after removal of the source of fire. When taking into account values of oxygen index, greater fire resistance characterize pine plywood (oxygen index - 49%) in comparison to beech plywood (oxygen index – 36%).

PL

Palność sklejek wytworzonych z fornirów zabezpieczonych środkiem ogniochronnym na bazie wodorofosforanu amonu, kwasu cytrynowego i benzoesanu sodu. W ramach badań określono wpływ impregnacji fornirów sosnowych i bukowych preparatem ogniochronnym opartym na kompozycji wodorofosforanu amonu, kwasu cytrynowego i benzoesanu sodu na palność wytworzonych z nich sklejek. Retencja preparatu w fornirach wynosiła 47 - 50 kg na 1 m3. Ustalono, że sklejki wytworzone z zaimpregnowanych fornirów nie podtrzymywały palenia po usunięciu źródła ognia. Uwzględniając wartości indeksu tlenowego, większą ognioodpornością charakteryzują się sklejki sosnowe (indeks tlenowy – 49 %) w stosunku do sklejek bukowych (indeks tlenowy – 36 %).

• Wydawca: -
• Czasopismo: Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology
• Rocznik: 2011
• Tom: 73
• Opis fizyczny: p.167-171,fig.,ref.

Twórcy

autor

Borysiuk P.

• Faculty of Wood Technology, Warsaw University of Life Sciences-SGGW, 159 Nowoursynowska st., 02-776 Warsaw, Poland

autor

Jaskolowski W.

• Main School of Fire Service, 52/54 Slowackiego st., 01-629 Warsaw, Poland

autor

Boruszewski P.

• Faculty of Wood Technology, Warsaw University of Life Sciences-SGGW, 159 Nowoursynowska st., 02-776 Warsaw, Poland

autor

Jenczyk-Tolloczko I.

• Faculty of Wood Technology, Warsaw University of Life Sciences-SGGW, 159 Nowoursynowska st., 02-776 Warsaw, Poland

autor

Jablonski M.

• Faculty of Wood Technology, Warsaw University of Life Sciences-SGGW, 159 Nowoursynowska st., 02-776 Warsaw, Poland

autor

Bylinski D.

• Faculty of Wood Technology, Warsaw University of Life Sciences-SGGW, 159 Nowoursynowska st., 02-776 Warsaw, Poland

Bibliografia

• 1. DRYSDALE D., 2001: Introduction to Fire Dynamics, J.Willey & Sons Inc.
• 2. EN ISO 11925-2 „Reaction to fire tests - Ignitability of products subjected to direct impingement of flame - Part 2: Single-flame source test.”
• 3. ISO 4589-2 „Plastics - Determination of burning behaviour by oxygen index.”
• 4. KARTAL N., AYRILMIS N., IMAMURA Y., 2007: Decay and thermal resistance of plywood treated with various fire retardants. Building and Environment 42, 1207–1211
• 5. KRAJEWSKI A., WITOMSKI P., 2005: Ochrona drewna surowca i materiału. Wydawnictwo SGGW
• 6. OSIPIUK J., 2001: Trwałość zabezpieczenia drewna solnymi środkami ogniochronnymi. Wydawnictwo SGGW
• 7. United States Patent No: US 7736549 Flame retardant chemical composition. Jun 15, 2010