• Autorzy: Borysiuk P. , Zbiec M. , Boruszewski P. , Maminski M. , Mazurek A.

Warianty tytułu

PL

Badanie możliwości jednoetapowego wytwarzania płyt fornirowo-wiórowych

• Języki publikacji: EN

Abstrakty

EN

Possibilities of single-stage pressing of veneered particleboards. Following work describes possibility of single-stage pressing of veneered particleboards. Three variants of the 16mm thick boards of 620kg/m3 density were manufactured for the test: (1) single-layer particleboard, (2) single-layer double-stage pressed veneered particleboard (3) single layer single-stage pressed veneered particleboard. Manufactured particleboards were tested against density distribution, MOR, MOE, IB, Stell and absorbability after 24h soaking in water. Possibility of single-stage pressing of veneered particleboards was established, it was also determined that mechanical properties of such boards are mainly dependent on grain direction in the outer veneers. Veneered particleboards have usually better physical properties, such as swell and absorbability.

PL

Badanie możliwości jednoetapowego wytwarzania płyt fornirowo-wiórowych. Praca opisuje możliwość jednoetapowego wytwarzania płyt wiórowych fornirowanych. W ramach pracy wykonano 3 warianty płyt o grubości 16mm i gęstości nominalnej 620kg/m3: (1) płyta wiórowa jednowarstwowa, (2) płyta wiórowa jednowarstwowa fornirowana w dwóch etapach, (3) płyta wiórowa jednowarstwowa fornirowana w jednym etapie. Dla wytworzonych płyt zbadano profil gęstości, MOR, MOE, IB spęcznienie i nasiąkliwość po 24h moczenia w wodzie. Ustalono, że istnieje możliwość wytwarzania płyt wiórowych fornirowanych w 1 operacji, przy czym ich parametry wytrzymałościowe uzależnione są na ogół od kierunku przebiegu słojów w fornirach. Płyty fornirowane charakteryzują się równocześnie korzystniejszymi parametrami fizycznymi (spęcznienie i nasiąkliwość).

• Wydawca: -
• Czasopismo: Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology
• Rocznik: 2011
• Tom: 73
• Opis fizyczny: p.172-175,fig.,ref.

Twórcy

autor

Borysiuk P.

• Faculty of Wood Technology, Warsaw University of Life Sciences-SGGW, 159 Nowoursynowska st., 02-776 Warsaw, Poland

autor

Zbiec M.

• Faculty of Wood Technology, Warsaw University of Life Sciences-SGGW, 159 Nowoursynowska st., 02-776 Warsaw, Poland

autor

Boruszewski P.

• Faculty of Wood Technology, Warsaw University of Life Sciences-SGGW, 159 Nowoursynowska st., 02-776 Warsaw, Poland

autor

Maminski M.

• Faculty of Wood Technology, Warsaw University of Life Sciences-SGGW, 159 Nowoursynowska st., 02-776 Warsaw, Poland

autor

Mazurek A.

• Faculty of Wood Technology, Warsaw University of Life Sciences-SGGW, 159 Nowoursynowska st., 02-776 Warsaw, Poland

Bibliografia

• 1. BORYSIUK P., DZIURKA D., JABŁOŃSKI M., ZBIEĆ M., 2005: Application of waste corrugated cardboard as an internal layer of blockboard. Annals of Warsaw Agricultural University, Forestry and Wood Technology, 56/05, 60–64
• 2. CZECHOWSKA J., BORYSIUK P., MAMIŃSKI M., BORUSZEWSKI P., 2008: Lowdensity particleboards filled with waste PUR foam. Annals of Warsaw University of Life Sciences – SGGW, Forestry and Wood Technology, 63, 156-160
• 3. DZIURKA D., ŁĘCKA J., 2010: Veneered lightweight particleboards for furniture industry. Annals of Warsaw University of Life Sciences – SGGW, Forestry and Wood Technology, 71, 166-169;
• 4. GÖKAY N., GŰRSEL Ç., 2005: The influence of lamination technique on the properties of particleboards; Building and Environment, 40, 83-87;
• 5. HOLZHACKER A., MĘTRAK C., ŻUROWSKI J., 1967: Meblarstwo. Wydawnictwo Przemysłu Lekkiego i Spożywczego, Warszawa
• 6. PN-EN 310 Płyty drewnopochodne. Oznaczanie modułu sprężystości przy zginaniu i wytrzymałości na zginanie.
• 7. PN-EN 317 Płyty wiórowe i płyty pilśniowe. Oznaczanie spęcznienia na grubość po moczeniu w wodzie.
• 8. PN-EN 319 Płyty wiórowe i płyty pilśniowe. Oznaczanie wytrzymałości na rozciąganie w kierunku prostopadłym do płaszczyzn płyty.
• 9. STARECKI A., DROUET T., LEŚNIKOWSKI A., ONIŚKO W., 1994: Technologia tworzyw drzewnych. Wydawnictwa Szkolne i Pedagogiczne, Warszawa