Degradation of coatings based on 310S steel doped with Al and Ir additives by the scratch test

• Autorzy: Barbara Kucharska
• Języki publikacji: EN

Abstrakty

EN

Mechanical tests of PVD coatings made on steel 310S were carried out within this study by the scratch test method. It was found that the additions of Al and Ir caused lower critical load values compared to the coating without additions. Despite the reduction of the critical load of the coating by the aluminium addition, the effect of aluminium was considered advantageous owing to the refinement of the structure causing the coating to become more plastic and reducing the number and sizes of micro-cracks. The addition of iridium results in an embrittlement of the coating structure and its poorer adhesion to the substrate. Comparison of the findings from the scratch test with the observations from an optical and a scanning microscopes was also made.

Słowa kluczowe

EN

scratch test; magnetron sputtering coating; adhesion; iron-nickel-chromium steel

• Czasopismo: Open Physics
• Rocznik: 2011
• Tom: 9
• Numer: 4
• Strony: 1122-1130

Daty

wydano

2011-08-01

online

2011-04-30

Twórcy

autor

Barbara Kucharska

• Institute of Materials Engineering, Czestochowa University of Technology, 42-200, Czestochowa, Armii Krajowej 19, Poland,

Bibliografia

• [1] V. Jardret, H. Zahouanl, J.L Loubet, T.G. Mathla, Wear 218, 8 (1998) http://dx.doi.org/10.1016/S0043-1648(98)00200-2[Crossref]
• [2] E. Harry, A. Rouzand, P. Juliet, Y. Pauleau, Thin Solid Films 342, 207 (1999) http://dx.doi.org/10.1016/S0040-6090(98)01499-0[Crossref]
• [3] LA. Dobrzanskl, M. Polok, P. Panjan, S. Bugllosl, M Adamlak, J. Mater. Process. Tech. 155–156, 1995 (2004) http://dx.doi.org/10.1016/j.jmatprotec.2004.04.405[Crossref]
• [4] M.K. Khan, M.E. Fltzpatrlck, S.V. Halnsworth, L Edwards, Mat. Scl. Eng. A-Struct. 527, 297 (2009) http://dx.doi.org/10.1016/j.msea.2009.07.035[Crossref]
• [5] J. Stallard, S. Poulad, D.G. Teer, Trlbol. Int. 39, 159 (2006) http://dx.doi.org/10.1016/j.triboint.2005.04.011[Crossref]
• [6] N.X. Rabdall, G. Favaro, C.H. Frankel, Surf. Coat. Tech. 137, 146 (2001) http://dx.doi.org/10.1016/S0257-8972(00)01097-5[Crossref]
• [7] D. Beegan, S. Chowdhury, M.T. Laugler, Surf. Coat. Xech. 201, 5804 (2007) http://dx.doi.org/10.1016/j.surfcoat.2006.10.031[Crossref]
• [8] R. Mlshra, B. Basu, R. Balasubramaniam, Mat. Scl. Eng. A-Struct. 373, 370 (2004) http://dx.doi.org/10.1016/j.msea.2003.09.107[Crossref]
• [9] S.J. Bull, E.G. Berasetequl, Xrlbol. int. 39, 99 (2006)
• [10] B. Kucharska, Mater. Sci.-Poland 26, 181 (2008)
• [11] S.J. Bull, Xrlbol. Int. 30, 491 (1997)
• [12] B. Kucharska, Inzynlerla Materlafowa 175, 358 XXXI (2010)

Identyfikatory

DOI

10.2478/s11534-011-0005-8