Topography and nanomechanical properties of Pd-C films

• Autorzy: Joanna Rymarczyk , Elzbieta Czerwosz , Asta Richter
• Języki publikacji: EN

Abstrakty

EN

Atomic force microscopy (AFM) topographical studies and results of nanoindentation experiment for several palladium-carbon films (Pd-C film) deposited on various substrates and with varying palladium content are presented. Pd-C films were prepared by a physical vapor decomposition (PVD) process and next were modified by a chemical vapor decomposition (CVD) method to obtain carbonaceous porous structure with dispersed palladium nanograins and a variation in roughness. The dependence of film topography on the kind of substrate such as Al2O3, Mo polycrystalline foil and fused silica was studied by AFM. Nanomechanical properties such as hardness and the reduced indentation modulus were determined by nanoindentation. A comparison of these values for films with different Pd content deposited on various substrates is presented.

Słowa kluczowe

EN

carbon; palladium; nanoindentation; hardness; reduced modulus

• Czasopismo: Open Physics
• Rocznik: 2011
• Tom: 9
• Numer: 2
• Strony: 300-306

Daty

wydano

2011-04-01

online

2011-02-20

Twórcy

autor

Joanna Rymarczyk

• Tele & Radio Research Institute, Ratuszowa 11, 03-450, Warsaw, Poland,

autor

Elzbieta Czerwosz

• Tele & Radio Research Institute, Ratuszowa 11, 03-450, Warsaw, Poland

autor

Asta Richter

• Dept. of Engineering Physics, Univ. of Applied Sciences Wildau, Bahnhofstrasse 1, 15745, Wildau, Germany

Bibliografia

• [1] X.M.H. Huang, M. Manolidis, Seong Chan Jun, J. Hone, Appl. Phys. Lett. 86, 143104 (2005) http://dx.doi.org/10.1063/1.1897445[Crossref]
• [2] S.E. Lyshevski, Nano- and micro-electromechanical systems: fundamentals of nano- and micro engineering (CRC Press, Boca Raton, FL, 2005)
• [3] R. Duś, E. Nowicka, R. Nowakowski, Acta Phys. Pol. A 114, 29 (2008)
• [4] G. Timp, Nanotechnology (Springer, New York, 1999) http://dx.doi.org/10.1007/978-1-4612-0531-9[Crossref]
• [5] A.C. Fischer-Cripps, Nanoindentation (Springer-Verlag, New York, 2002)
• [6] E. Czerwosz et al., Vacuum 82, 372 (2008) http://dx.doi.org/10.1016/j.vacuum.2007.08.003[Crossref]
• [7] M. Kozłowski et al., Journal of Achievements in Materials and Manufacturing Engineering 37, 304 (2009)
• [8] W.C. Oliver, G.M. Pharr, J. Mater. Res. 7, 1564 (1992) http://dx.doi.org/10.1557/JMR.1992.1564[Crossref]
• [9] B. Wolf, A. Richter, New Journal of Physics 5, 15.1 (2003) http://dx.doi.org/10.1088/1367-2630/5/1/315[Crossref]
• [10] A. Richter, R. Ries, R. Smith, M. Henkel, B. Wolf, Diam. Relat. Mater. 9, 170 (2000) http://dx.doi.org/10.1016/S0925-9635(00)00188-6[Crossref]

Identyfikatory

DOI

10.2478/s11534-010-0134-5