The InAs quantum structures were formed in silicon by sequential ion implantation and subsequent thermal annealing. Two kinds of crystalline InAs nanostructures were successfully synthesized: nanodots (NDs) and nanopyramids (NPs). The peaks at 215 and 235 cm−1, corresponding to the transverse optical (TO) and longitudinal optical (LO) InAs single-phonon modes, respectively, are clearly visible in the Raman spectra. Moreover, the PL band at around 1.3 µm, due to light emission from InAs NDs with an average diameter 7±2 nm, was observed. The InAs NPs were found only in samples annealed for 20 ms at temperatures ranging from 1000 up to 1200°C. The crystallinity and pyramidal shape of InAs quantum structures were confirmed by HRTEM and XRD techniques. The average size of the NPs is 50 nm base and 50 nm height, and they are oriented parallel to the Si (001) planes. The lattice parameter of the NPs increases from 6.051 to 6.055 Å with the annealing temperature increasing from 1100 to 1200°C, due to lattice relaxation. Energy dispersive spectroscopy (EDS) shows almost stoichiometric composition of the InAs NPs.
Słowa kluczowe
Czasopismo
Rocznik
Tom
Numer
Strony
338-343
Opis fizyczny
Daty
wydano
2011-04-01
online
2011-02-20
Twórcy
autor
- Maria Curie-Skłodowska University, Pl. M. Curie-Skłodowskiej 1, 20-031, Lublin, Poland, s.prucnal@fzd.de
autor
- Maria Curie-Skłodowska University, Pl. M. Curie-Skłodowskiej 1, 20-031, Lublin, Poland, mturek@kft.umcs.lublin.pl
autor
- Maria Curie-Skłodowska University, Pl. M. Curie-Skłodowskiej 1, 20-031, Lublin, Poland
autor
- Maria Curie-Skłodowska University, Pl. M. Curie-Skłodowskiej 1, 20-031, Lublin, Poland
autor
- Maria Curie-Skłodowska University, Pl. M. Curie-Skłodowskiej 1, 20-031, Lublin, Poland
autor
- Institute of Ion Beam Physics and Materials Research, Forschungszentrum Dresden-Rossendorf, P.O. Box 510119, 01314, Dresden, Germany
autor
- Institute of Ion Beam Physics and Materials Research, Forschungszentrum Dresden-Rossendorf, P.O. Box 510119, 01314, Dresden, Germany
autor
- Institute of Ion Beam Physics and Materials Research, Forschungszentrum Dresden-Rossendorf, P.O. Box 510119, 01314, Dresden, Germany
autor
- Institute of Ion Beam Physics and Materials Research, Forschungszentrum Dresden-Rossendorf, P.O. Box 510119, 01314, Dresden, Germany
autor
- Maria Curie-Skłodowska University, Pl. M. Curie-Skłodowskiej 1, 20-031, Lublin, Poland
Bibliografia
- [1] J. Valenta, N. Lalic, J. Linnros, Appl. Phys. Lett. 84, 1459 (2004) http://dx.doi.org/10.1063/1.1655705[Crossref]
- [2] J.H. Chen et al., Jpn. J. Appl. Phys. 46, 6586 (2007) http://dx.doi.org/10.1143/JJAP.46.6586[Crossref]
- [3] X.J. Hao et al., Sol. EnergyMater. Sol. Cells 93, 273 (2009) http://dx.doi.org/10.1016/j.solmat.2008.10.017[Crossref]
- [4] L.E. Brus, J. Chem. Phys. 80, 4403 (1984) http://dx.doi.org/10.1063/1.447218[Crossref]
- [5] T. Canham, Appl. Phys. Lett. 57, 1046 (1990) http://dx.doi.org/10.1063/1.103561[Crossref]
- [6] S. Sapra, D.D. Sarma, Phys. Rev. B 69, 125304 (2004) http://dx.doi.org/10.1103/PhysRevB.69.125304[Crossref]
- [7] J. Murphy, J.L. Coffer, Appl. Spectrosc. 56, 16A (2002) http://dx.doi.org/10.1366/0003702021954214[Crossref]
- [8] M.D. Dvorak, B.L. Justus, D.K. Daskill, D.G. Hendershot, Appl. Phys. Lett. 66, 804 (1995) http://dx.doi.org/10.1063/1.113426[Crossref]
- [9] T. Shmizu-Iwayama et al., J. Appl. Phys. 75, 7779 (1994) http://dx.doi.org/10.1063/1.357031[Crossref]
- [10] R. Ding et al., Mater. Chem. Phys. 76, 262 (2002) http://dx.doi.org/10.1016/S0254-0584(01)00537-5[Crossref]
- [11] R.L. Wells, S.R. Aubuchon, S.S. Kher, M.S. Lube, Chem. Mater. 7, 793 (1995) http://dx.doi.org/10.1021/cm00052a027[Crossref]
- [12] A. Meldrum, L. A. Boatner, C. W. White, Nucl. Instrum. Meth. B 178, 7 (2001) http://dx.doi.org/10.1016/S0168-583X(00)00501-2[Crossref]
- [13] F. Komarov et al., Nucl. Instrum. Meth. B 266, 3557 (2008) http://dx.doi.org/10.1016/j.nimb.2008.06.010[Crossref]
- [14] A.L. Tchebotareva, J.L. Brebner, S. Roorda, C.W. White, Nucl. Instrum. Meth. B 175–177, 187 (2001) http://dx.doi.org/10.1016/S0168-583X(00)00660-1[Crossref]
- [15] K. Suzuki et al., IEEE Trans. Electron Devices 54, 262 (2007) http://dx.doi.org/10.1109/TED.2006.888676[Crossref]
- [16] G.E. Walter, P.N. Krishnan, S.W. Freiman, J. Appl. Phys. 52, 2832 (1981) http://dx.doi.org/10.1063/1.329013[Crossref]
- [17] Y. Hibino, H. Hanafusa, K. Ema, S. Hyodo, Appl. Phys. Lett. 47, 812 (1985) http://dx.doi.org/10.1063/1.95992[Crossref]
- [18] M.Yu. Ladanov et al., J. Exp. Theor. Phys. 101, 554 (2005) http://dx.doi.org/10.1134/1.2103225[Crossref]
- [19] M. Yamaguchi, K. Morigaki, J. Phys. Soc. Jpn. 62, 2915 (1993) http://dx.doi.org/10.1143/JPSJ.62.2915[Crossref]
- [20] C.J. Patel, Q.X. Zhao, O. Nur, M. Willander, Appl. Phys. Lett. 72, 3047 (1998) http://dx.doi.org/10.1063/1.121536[Crossref]
- [21] G.K. Williamson, W.H. Hall, Acta Metall. 1, 22 (1953) http://dx.doi.org/10.1016/0001-6160(53)90006-6[Crossref]
- [22] M. Levinstein, S. Rumyantsev, M. Shur, Handbook Series on Semiconductor Parameters, vol. 2 (World Scientific, Singapore, 1996) http://dx.doi.org/10.1142/9789812832078[Crossref]
Typ dokumentu
Bibliografia
Identyfikatory
Identyfikator YADDA
bwmeta1.element.-psjd-doi-10_2478_s11534-010-0107-8