Shear modulus and damping ratio of recycled concrete aggregate from cyclic torsional shear test

Gabryś Katarzyna

Roads and Bridges - Drogi i Mosty

|

2023

|

Vol. 22, no. 4

387--398

EN

This study examines the small-strain dynamic properties of three mixtures of recycled concrete aggregate (RCA) using laboratory investigations typical of natural soils, namely cyclic torsional shear (CTS) tests. In order to construct two samples, crushed concrete curbs originating from a demolition site in Warsaw was employed. To create the third sample, crushed concrete from demolished buildings also Warsaw was used, mainly from concrete wall and floor elements. A series of CTS tests were performed to investigate the impact of various parameters, including confining pressure, excitation frequency, and number of vibration cycles on the G−modulus, Gmax−modulus, shear modulus degradation curve G(γ)/Gmax, D−ratio, Dmin−ratio, variation in damping curve D(γ)/Dmin. The resulting stiffness and damping characteristics of the analysed concrete aggregate were compared with those of natural gravel and sand aggregate – natural aggregate (NA). The results collected from the CTS tests indicate that the performance of most RCA is comparable to that of NA and can be used as an unbound granular material (UGM).

PL

W niniejszym badaniu zbadano właściwości dynamiczne przy małych odkształceniach trzech mieszanek kruszywa betonowego z recyklingu (RCA) przy użyciu badań laboratoryjnych typowych dla gruntów naturalnych, a mianowicie badania cyklicznego ścinania skrętnego (CTS). Do wykonania dwóch próbek wykorzystano pokruszone krawężniki betonowe pochodzące z rozbiórki w Warszawie. Do stworzenia trzeciej próbki wykorzystano pokruszony beton z rozebranych budynków, także z Warszawy, głównie z betonowych elementów ścian i podłóg. Przeprowadzono serię testów CTS w celu zbadania wpływu różnych parametrów, w tym ciśnienia ograniczającego, częstotliwości wzbudzenia i liczby cykli wibracji na moduł G, moduł Gmax, krzywą degradacji modułu ścinania G(γ)/Gmax, współczynnik D, współczynnik Dmin, zmianę krzywej tłumienia D(γ)/Dmin. Uzyskane charakterystyki sztywności i tłumienia analizowanego kruszywa betonowego porównano z charakterystykami naturalnego kruszywa żwirowo-piaskowego – kruszywa naturalnego NA). Wyniki zebrane z badań CTS wskazują, że wydajność większości destruktu betonowego jest porównywalna z kruszywem naturalnym i może być stosowana jako niezwiązany materiał ziarnisty (UGM).

2

The application of composites based on recycled materials for electromagnetic field shielding

Jakubas Adam, Łada-Tondyra Ewa, Suchecki Łukasz

Przegląd Elektrotechniczny

|

2023

|

R. 99, nr 1

190--193

EN

This paper presents the possibilities of using polymer-metal composites as electromagnetic shields. Recycled materials such as iron scale and nanocrystalline tapes were used to build the composites. In the course of the work, research was carried out into the effectiveness of shielding electromagnetic fields in the range from 40 Hz to 15 GHz. The shielding effectiveness was shown to be competitive to that of other composite materials based on non-metallic fillers and comparable to that of layered composites containing e.g. aluminum.

PL

W artykule przedstawiono możliwości wykorzystania kompozytów polimerowo-metalowych jako ekranów elektromagnetycznych. Do budowy kompozytów wykorzystano materiały z recyklingu, takie jak zendra i taśmy nanokrystaliczne. W toku prac prowadzono badania nad skutecznością ekranowania pól elektromagnetycznych w zakresie od 40 Hz do 15 GHz. Wykazano, że skuteczność ekranowania jest konkurencyjna w stosunku do innych materiałów kompozytowych na bazie wypełniaczy niemetalicznych i porównywalna z kompozytami warstwowymi zawierającymi m.in. aluminium.

3

Wpływ piasku korundowego na właściwości betonu cementowego

Horszczaruk Elżbieta, Kiernożycki Włodzimierz

Materiały Budowlane

|

2023

|

nr 9

9--12

PL

W artykule przedstawiono wyniki badań wpływu odpadowego piasku korundowego używanego do piaskowania konstrukcji metalowych na właściwości betonu. Piasek korundowy zastosowano jako zamiennik 25, 50 i 75% objętości kruszywa drobnego. Przeprowadzone zostały badania konsystencji mieszanek betonowych i gęstości objętościowej betonów. Badano wytrzymałość na ściskanie i rozciąganie przy rozłupywaniu betonów po 7 i 28 dniach dojrzewania. Określono również nasiąkliwość betonów i głębokość penetracji wody pod ciśnieniem. Badania potwierdziły możliwość zastosowania piasku korundowego jako zamiennika kruszywa drobnego w betonach cementowych.

EN

The paper presents the results of research on the influence of waste corundum sand used for sandblasting metal structures on the properties concrete. Corundum sand was used as a substitute for sand in the amount of 25%, 50 and 75% of the fine aggregate volume. Tests were carried out on the consistency of concrete mixes and the bulk density of concretes. The compressive strength and tensile splitting strength were measured at the age of the concrete of 7 and 28 days. The water absorption of concretes and the depth of water penetration under pressure were also determined. The tests confirmed the possibility of using corundum sand as a substitute for fine aggregate in cement concrete.

4

Comparative analysis of natural nanosilica versus commercial nanosilica on compressive strength and durability of high-performance concrete

Tjahjani A.R. Indra, Fulazzaky Mohamad Ali, Jonbi Jonbi, Tinumbia Nuryani, Meutia Wita, Suraedi Daral, Ranna Prima

Archives of Civil Engineering

|

2023

|

Vol. 69, nr 3

49--63

EN

This study provides a comparative analysis of natural nanosilica (NSn), which is an extract of natural silica sand processed into nanosilica with commercial nanosilica (NSc) derived from semiconductor industrial waste, in 80 MPa high performance concrete (HPC). The percentage of using nanosilica is (3%, 5%, 10%, 15%) by weight of cement used directly and combined with 5% silica fume. Analysis was carried out through compressive strength test, durability through permeability test, rapid chloride penetration test (RCPT), and microstructure test through scanning electron microscopy (SEM). The results of the analysis show that natural nanosilica is equivalent to commercial nanosilica, in applications it is better to use silica fume incorporation. The optimum percentage of using NSn10% and (SF) 5%, while 5% NSc and 5% SF, in these proportions shows the best compressive strength and durability. It’s just that the use of natural nanosilika is 5% more than commercial nanosilika. The benefit of this research is that natural materials such as silica sand with high SiO2 content, can be processed into nanosilica as an advanced material, which can be used as an eco-friendly construction material.

5

Cegły szklane o podwyższonej wytrzymałości mechanicznej powstałe na bazie surowców odpadowych

Łączka Karolina

Szkło i Ceramika

|

2022

|

R. 73, nr 4

22--23

PL

Cegły szklane są interesującą alternatywą dla powszechnie stosowanych luksferów. Te monolityczne, proste w formie odlewy ze szkła mogą być wykorzystywane zarówno we wnętrzu, jak i na zewnątrz budynku. Umożliwiają skuteczne doświetlenie pomieszczenia światłem dziennym, mogą także być elementem dekoracyjny przegrody, bądź tworzyć całą ściankę działową.

6

Badania eksperymentalne modułu Younga belek ze styrobetonu z zawartością 60% regranulatu EPS zbrojonych ekologicznym materiałem odpadowym

Juraszek Janusz, Walusiak Hubert

Materiały Budowlane

|

2022

|

nr 11

10--12

PL

W artykule przedstawiono wyniki badań belek wykonanych ze styrobetonu zawierającego 60% regranulatu EPS (polistyren ekspandowany), który został wzmocniony ekologicznym surowcem w postaci odpowiednio przygotowanej wełny owczej. Przeprowadzono próby zginania 3-punktowego w celu wyznaczenia odkształcalności badanych elementów. Nowością jest zastosowanie specjalnie dedykowanych światłowodowych czujników odkształceń z siatką Bragga (Fiber Bragg Grating - FBG ), które umożliwiły precyzyjne wyznaczenie wartości modułu Younga trzech rodzajów próbek wykonanych ze styrobetonu. Wprowadzenie zaprawy cementowej wraz włóknami wełny owczej w dolnej warstwie próbki styrobetonowej zwiększyło o 18,9% wartość modułu Younga w porównaniu z próbką bez wełny. Wykorzystanie włókien wełny odpadowej umożliwia skuteczne zagospodarowanie odpadów oraz zmniejszenie zużycia kruszywa naturalnego w mieszance.

EN

The article presents the results of tests of beams made of polystyrene concrete containing 60% regranulate EPS (expanded polystyrene), which has been reinforced with ecological raw material in the form of properly prepared sheep wool. 3-point bending tests were carried out, and in order to determine the deformability of the tested elements, a new measurement method was used with the use of fiber-optic deformation sensors with a Bragg mesh (Fiber Bragg Grating - FBG). The aim of the research was to determine the value of Young's modulus for 3 variants of samples made of polystyrene concrete. The introduction of a cement mortar in the lower layer of polystyrene in the sample with sheep wool fibers increased the value of Young's modulus by 18.9% in relation to the sample without wool. The use of waste wool fibers enables effective waste management and reduction of the consumption of natural aggregate in the mix.

7

Wybrane parametry zapraw z dodatkiem cenosfer

Strzałkowski Jarosław, Stolarska Agata, Kożuch Dominik, Dmitruk Joanna

Inżynieria i Budownictwo

|

2022

|

R. 78, nr 9-10

422--425

PL

W pracy zaprezentowano wpływ procentowego zastąpienia piasku kwarcowego cenosferami na wybrane właściwości zapraw cementowych. Stopniowano ilość dodatku cenosfer co 20% całkowitej objętości kruszywa, zaczynając od zaprawy referencyjnej bez wypełniacza, po zaprawę wykonaną wyłącznie na bazie cenosfer. Oceniano takie parametry, jak gęstość, współczynnik przewodzenia ciepła i wytrzymałość na zginanie i ściskanie.

EN

The paper presents the effect of the percentage replacement of quartz sand with cenospheres on selected properties of cement mortars. The amount of cenospheres addition was graded every 20% of the total aggregate volume, starting from the reference mortar without filler, to mortar made solely on the basis of cenospheres. Parameters such as density, thermal conductivity as well as bending and compressive strength were assessed.

8

Study on some of the strength properties of soft clay stabilized with plastic waste strips

Kabeta Worku Firomsa

Archives of Civil Engineering

|

2022

|

Vol. 68, nr 3

385--395

EN

It is well known that if plastic wastes are not well managed, it has a negative impact on the environment as well as on human health. In this study, recycling plastic waste in form of strips for stabilizing weak subgrade soil is proposed. For this purpose, a weak clay soil sample was mixed with 0.2%, 0.3%, and 0.4% of plastic strips by weight of soil, and the experimental results were compared to the control soil sample with 0% plastic. Laboratory tests on the Standard compaction test, Unconfined compression test (UCS), and California bearing ratio (CBR) were conducted according to the American Society for Testing and Materials (ASTM). The results of the study reveal that there are significant improvements in the strength of weak soil stabilized with plastic waste strips. Accordingly, the Standard Proctor test shows that there is a small increment in the maximum dry density of the soil when it is mixed with plastic strips. The result from the CBR test shows that there is a significant increment of CBR value with the plastic strip content. The unconfined compressive strength test also shows that increasing the percentage of plastic strips from 0 to 0.4% resulted in increased strength of soil by 138% with 2 cm length plastic strips. Therefore, this study recommends the application of plastic strips for improvement of the strength of soft clay for subgrade construction in civil engineering practice as an alternative weak soil stabilization method.

9

Influence of Waste Toothbrush Fiber on Strength and Freezing–Thawing Behavior in High Plasticity Clay

Isik Fatih, Akbulut R. Kagan, Zaimoglu A. Sahin

Studia Geotechnica et Mechanica

|

2021

|

Vol. 43, nr 1

15--21

EN

The use of waste materials in civil engineering applications has gained importance nowadays. Consuming limited natural resources and increasing waste disposal costs have led researchers to evaluate waste materials for different geotechnical applications. In this respect, some waste materials are used as reinforcement in soils to improve their engineering properties. The main objective of this paper was to investigate the usability of waste polypropylene fiber as a reinforcement material in high plasticity fine-grained soils. For this purpose, waste toothbrush bristle (WTB) was used as a polypropylene fiber reinforcement material and added to fine-grained soil at ratios of 0.2%, 0.4%, 0.6% and 0.8% by dry total weight. The effect of WTB on freezing–thawing behavior and unconfined compression strength of unreinforced and reinforced clayey soil was evaluated. The results indicated that addition of WTB to high plasticity clay improved its behavior against freezing–thawing. Also, undrained shear strength increases with respect to increment in WTB ratio.

10

Gospodarka materiałowa w dobie transformacji gospodarczej

Tomaszewska Justyna

Materiały Budowlane

|

2021

|

nr 3

36--38

PL

Niwelowanie negatywnych skutków środowiskowych, powodowanych intensywnym rozwojem cywilizacyjnym oraz eksploatacją zasobów naturalnych w sposób zapewniający ich dostępność przyszłym pokoleniom, stanowią aktualne wyzwania, przed którymi stoi Unia Europejska. Zadania te są realizowane w ramach Europejskiego Zielonego Ładu, stanowiącego plan działań na rzecz zrównoważonej gospodarki Wspólnoty. Efektem tej inicjatywy ma być przeciwdziałanie utracie różnorodności biologicznej, zmniejszenie poziomu zanieczyszczeń oraz bardziej efektywne wykorzystanie zasobów dzięki przejściu na gospodarkę o obiegu zamkniętym. Wdrażane rozwiązania legislacyjne i organizacyjne mają doprowadzić do zmiany dotychczas funkcjonującego modelu gospodarczego, na taki, który zapewni efektywny przepływ surowców, energii, pracy i informacji, dzięki czemu stanie się możliwe odbudowanie zaangażowanych zasobów ludzkich i środowiskowych.

EN

Eliminating the negative environmental effects caused by the rapid civilization development and the exploitation of natural resources in a way that ensures their availability for future generations are the current challenges that the European Union is facing. These tasks are carried out under the European Green Deal, which is an action plan to sustainable EU economy. The initiative is expected to counteract the loss of biodiversity, reduce the level of pollution and support the efficient consumption of resources through the transition to Circular Economy (CE). The implemented legislative and organizational solutions are expected to change the existing economic model into one that will ensure the effective flow of raw materials, power, labour and information so that it is possible to „rebuild” environmental and human resources.

11

Geopolimery zawierające materiały odpadowe

Duch Krzysztof

Materiały Budowlane

|

2021

|

nr 12

32--33

PL

W artykule przedstawiono wyniki badań właściwości kompozytów geopolimerowych z kruszywem z recyklingu betonu. Recepturę geopolimerów modyfikowano zawartością granulowanego mielonego żużla wielkopiecowego i popiołu lotnego oraz kruszywa z recyklingu. Uzyskane kompozyty geopolimerowe charakteryzowały się m.in. dużą wytrzymałością na ściskanie. Zachęca to do wykorzystania materiałów odpadowych w technologii wytwarzania ekologicznych kompozytów bezcementowych, jakimi są geopolimery.

EN

This paper presents the results of testing the properties of geopolymer composites with recycled aggregate concrete. The formulation of geopolymers was modified with a content of granulated ground blast-furnace slag, flue ash and recycled aggregate. The obtained geopolymer composites were characterized, among others, by high compressive strength. This encourages to use waste materials in technology in the technology of producing ecological cement-free composites, such as geopolymers.

12

Thermal and mechanical properties of lightweight concrete with waste copper slag as fine aggregate

Jaskulski Roman, Dolny Piotr, Yakymechko Yaroslav

Archives of Civil Engineering

|

2021

|

Vol. 67, nr 3

299--318

EN

The article presents the results of investigation of mechanical and thermal properties of lightweight concrete with waste copper slag as fine aggregate. The obtained results were compared with the results of concrete of the same composition in which natural fine aggregate (river sand) was used. The thermal properties tests carried out with the ISOMET 2114 device included determination of the following values: thermal conductivity coefficient, thermal volume capacity and thermal diffusivity. After determining the material density, the specific heat values were also calculated. The thermal parameters were determined in two states of water saturation: on fully saturated material and dried to constant mass at 65°C. Compressive strength, open porosity and bulk density are given as supplementary values. The results of the conducted research indicate that replacing sand with waste copper slag allows to obtain concrete of higher ecological values, with similar mechanical parameters and allowing to obtain significant energy savings in functioning of cubature structures made of it, due to a significantly lower value of thermal conductivity coefficient.

PL

W badaniach opisanych w niniejszej pracy określono właściwości termiczne betonu lekkiego oraz jego właściwości mechaniczne (wytrzymałość na ściskanie i rozciąganie). W części serii zamiast piasku jako kruszywo drobne zastosowano odpadowy żużel pomiedziowy, co umożliwiło określenie wpływu tego materiału na właściwości cieplne betonu lekkiego oraz ocenę, czy wpływ ten jest równie wyraźny jak w przypadku betonu zwykłego i ciężkiego. Zbadano również wpływ ilości użytego cementu (200 kg/m3 i 300 kg/m3) oraz stosunku woda/cement (0,50, 0,55 i 0,60). Wykonano łącznie dwanaście serii betonu. W sześciu z nich jako kruszywo drobne zastosowano piasek rzeczny, a w kolejnych sześciu zastąpiono go odpadowym żużlem pomiedziowym. Wymiany dokonano w stosunku masowym 1:1. Zastosowano cement portlandzki wieloskładniowy CEM II/B-M (V-LL) 32,5 R. Kruszywo grube składało się z dwóch frakcji kruszywa lekkiego. Frakcją 4-8 mm był kruszywo Certyd, a frakcję 8-16 mm stanowił keramzyt. Całkowita ilość wody zastosowanej w recepturach uwzględniała chłonność kruszywa lekkiego, którą badano przed przygotowaniem receptur. Właściwości cieplne badano na próbkach o średnicy 150 mm i grubości ok. 25-30 mm. W celu zbadania właściwości betonu w dwóch różnych stanach granicznego nasycenia, część próbek przechowywano w wodzie do momentu przeprowadzenia badań, a pozostałą część umieszczono w suszarce w temperaturze 65°C do momentu osiągnięcia stabilnej masy. Wytrzymałość na ściskanie badano na kostkach 100 mm. Wpływ rodzaju zastosowanego kruszywa drobnego nie był w tym przypadku jednoznaczny, gdyż w przypadku połowy serii, wymiana piasku na odpadowy żużel pomiedziowy spowodowała wzrost wytrzymałości, a w przypadku pozostałych serii jej spadek. Określono również porowatość materiału. Analiza wyników wykazała, że zwiększa się ona wraz z ilością cementu w betonie i współczynnikiem w/c. Ponadto beton wykonany z wykorzystaniem odpadowego żużla pomiedziowego wykazuje nieco wyższą porowatość niż beton wykonany z wykorzystaniem piasku o tych samych pozostałych parametrach (stosunek w/c i ilość cementu). Właściwości cieplne zmierzono metodą niestacjonarną za pomocą urządzenia ISOMET 2114 wyposażonego w sondę powierzchniową. Uzyskane wartości właściwości cieplnych poddano analizie statystycznej. Ze względu na dużą ilość danych analizę ograniczono do jednoczynnikowej analizy wariancji (ANOVA). Ponieważ w przypadku każdego z rozpatrywanych wariantów analiza wykazała, że otrzymane różnice między seriami są istotne statystycznie, przeprowadzono następnie analizę post hoc. Niezależnie od wymienionych powyżej czynników różnicujących poszczególne serie analizie poddano również wartości otrzymane w przypadku próbek nasyconych wodą i wysuszonych do stałej masy. Wyniki badania współczynnika przewodności cieplnej wskazują na istotne różnice w wartościach tego parametru w zależności od nasycenia betonu. Próbki wysuszone charakteryzują się niższą wartością współczynnika przewodnictwa cieplnego. Większe zróżnicowanie tego parametru w zależności od poziomu nasycenia betonu wodą dało się zaobserwować w przypadku serii z wykorzystaniem piasku. W tej grupie nie ma również korelacji pomiędzy porowatością a zróżnicowaniem wyników uzyskanych na próbkach nasyconych i wysuszonych. Serie betonu wykonane z wykorzystaniem odpadowego żużla pomiedziowego wykazują korelację pomiędzy spadkiem przewodności cieplnej a porowatością. Korelacja ta jest jednak przeciwna od tej, jakiej należałoby się spodziewać. Wraz ze wzrostem porowatości zmniejsza się wpływ stanu nasycenia próbek.

13

Multi-component sorption and utilization of solid waste to simultaneous removing basic dye and heavy metal from aqueous system

Sočo Eleonora, Pająk Dariusz, Kalembkiewicz Jan

Archives of Environmental Protection

|

2020

|

Vol. 46, no. 1

62--75

EN

The presented work introduces a simple modification of coal fly ash (FA) with 30% solution of H2O2, used as a new efficient sorbent for the removal of organic dye crystal violet (CV) in the presence of Cu(II) ions in single- and bi-component systems Cu(II)-CV. FT-IR, TG, SEM-EDS, and XRD suggested that the mechanism of Cu(II) and CV sorption onto FA-H2O2 includes ion-exchange and surface adsorption process. Comparing the values of the reduced chi-square test (χ2/DoF) and the determination coefficient R2 obtained for CV of the considered isotherms, the fitting degree follows the sequence: Jovanović > Langmuir > Elovich > Freundlich > Redlich-Peterson (R-P) > Tóth > Halsey > BET. Sorption of Cu(II) ions in a single system by means of FA-H2O2 was well fitted by the Langmuir and R-P model. The studies of equilibrium in a bi-component system by means of extended Langmuir (EL), extended Langmuir-Freundlich (ELF), and Jain-Snoeyink (JS) models were analysed. The estimation of parameters of sorption isotherms in a bi-component system Cu(II)-CV has shown that the best of fit calculated values of experimental data for both sorbates have been the EL model and the JS model, but only in the case of a CV dye. The sorption kinetic of Cu(II) and CV onto FA-H2O2 was discussed by means of the PFO, PSO, and intra-particle diffusion models.

PL

W pracy przedstawiono prostą modyfikację popiołu lotnego węglowego (FA) za pomocą 30% roztworu H2O2 oraz wykorzystanie go jako nowego skutecznego sorbentu do usuwania barwnika organicznego fioletu krystalicznego (CV) w obecności jonów Cu(II) w układzie jedno- i dwuskładnikowym Cu(II)-CV. Badania FT-IR, TG, SEM-EDS i XRD potwierdziły, że mechanizm sorpcji Cu(II) i CV na FA- H2O2 obejmuje proces wymiany jonowej i adsorpcji powierzchniowej. Porównując wartości zredukowanego testu chi-kwadrat (χ2/DoF) i współczynnika determinacji R2 uzyskane dla rozpatrywanych izoterm CV, stopień dopasowania odpowiednich modeli odpowiada następującej kolejności: Jovanović > Langmuir > Elovich > Freundlich > Redlich-Peterson (RP) > Tóth > Halsey > BET. Sorpcja jonów Cu(II) w układzie jednosładnikowym za pomocą FA-H2O2 została dobrze opisana za pomocą modelu Langmuira i R-P. Przeanalizowano badania równowagi w układzie dwuskładnikowym wykorzystując rozszerzony model Langmuira (EL), rozszerzony Langmuira-Freundlicha (ELF) i Jain-Snoeyinka (JS). Estymacja parametrów izoterm sorpcji w układzie binarnym Cu(II)-CV wykazała, że najlepsze dopasowanie wartości obliczonych do danych doświadczalnych dla obu sorbatów posiada model EL oraz model JS, ale tylko w przypadku barwnika CV. Kinetykę sorpcji Cu(II) i CV na FA-H2O2 przeanalizowano za pomocą modeli PFO, PSO i dyfuzji wewnątrzziarnowej.

14

Kierunki rozwoju prefabrykacji

Adamczewski Grzegorz, Woyciechowski Piotr

Materiały Budowlane

|

2019

|

nr 10

57--59

15

Charakterystyka środowiskowa systemów ETICS w latach 2014-2019

Michałowski Bartosz, Marcinek Marta, Tomaszewska Justyna, Czernik Sebastian, Piasecki Michał, Geryło Robert, Michalak Jacek

Materiały Budowlane

|

2019

|

nr 12

20--23

PL

W artykule przedstawiono oszacowanie oddziaływań środowiskowych obliczonych z wykorzystaniem metody oceny cyklu życia (LCA) dla złożonego systemu izolacji cieplnej ETICS. Analizie poddano wyniki uzyskane na podstawie danych dotyczących produkcji w 2012 r. i w 2017 r. w pięciu lokalizacjach produkcyjnych na terenie Polski. Cykl życia, będący przedmiotem analizy, obejmował moduły od A1 do A3, tj. od wydobycia surowców aż do gotowego wyrobu dostarczonego do bramy fabryki. Porównanie wartości wskaźników charakterystyki środowiskowej badanych systemów ETICS wskazuje, że w rozpatrywanych pięciu latach nastąpiło zmniejszenie ich negatywnego wpływu na środowisko naturalne.

EN

The paper presents the impact of the External Thermal Insulation Composite System (ETICS) on the natural environment. Analysis of environmental impact factors was conducted based on the life cycle assessment (LCA) methodology. Experimental results were obtained from the verified inventory data from the production at five different locations, following the year 2012 and 2017, respectively.The life cycle analysis of the examined products covered modules from A1 to A3, i.e. from raw materials extraction, up to the finished, packed product at the factory gate. Results of the LCA showed that within the last five years, the negative impact of the ETICS system on the natural environment decreased significantly.

16

Mineralne surowce wtórne : problemy polskiego nazewnictwa i klasyfikacji w związku z realizacją gospodarki o obiegu zamkniętym

Pietrzyk-Sokulska E., Radwanek-Bąk B., Kulczycka J.

Przegląd Geologiczny

|

2018

|

Vol. 66, nr 3

160--165

EN

One of the challenges of today’s economies in the world is the need to increase the use of waste materials as secondary raw materials that are suitable for further use. This constitutes a core of the circular economy. This allows on the one hand to minimize the risk of price volatility and availability of resources, on the other, to meet the increasing global environmental requirements, creating the core of circular economy. This applies in particular to mineral resources. Circular economy implementation requires a number of problems. The basic one concern the development of clear definitions of waste/recyclables (secondary resources), as now many of the terms are used interchangeably or imprecise, resulting in information chaos and the inability to quantify the source data. Next are: to develop standards describing particular typical waste products (secondary) arising in subsequent recovery phases, then - keeping records and balancing the amount of processed waste and recovered secondary raw materials. This publication focuses on the problem of terminology and definitions, due to its importance and urgency for already conducted activities related to the preparation of raw materials policy of the country. The Polish naming and waste management legislation has been reviewed, against the background of European regulations. The definition of recycled materials (secondary resources) has been proposed for their classification strictly linked to the current classification of waste.

17

Structure and Properties of Lightweight Ceramic Aggregates Based on Local Silesian Waste Materials

Smoleń J., Pawlik T., Sopicka-Lizer M., Michalik D.

Archives of Metallurgy and Materials

|

2018

|

Vol. 63, iss. 3

1321--1328

EN

This paper is focused on the manufacturing and properties of light weight aggregates made from local waste materials. The waste materials were car windshield glass contaminated by PVB foil, fly ash, mine slates as well as wastes after toothpaste production. The main aim of the research was to combine car windshield glass and the aluminosilicate coal mine slates as a basis for light weight aggregates manufacturing. Fly ash were added in order to modify rheological properties of the plastic mass. Toothpaste wastes were introduced as a source of carbonates and CO2 evolution during thermal treatment. After milling and mixing all materials they were pressed and sintered at temperature range of 950°C-1100°C in air. The results show that it is possible to receive light weight aggregates only from the Silesian local waste materials. The significant influence of sintering temperature on properties of aggregates was observed.

18

Effect of cellular concrete powder on durability of normal strength concrete

Gyurkó Z., Szijártó A., Abed M., Nemes R.

Architecture Civil Engineering Environment

|

2018

|

Vol. 11, no. 2

59--64

EN

Present research program is dealing with the effects of cellular concrete powder (CCP) on the compressive strength and durability of concrete. CCP is an industrial by-product, which was applied as supplementary cementitious material (SCM) in the concrete mix. In the previous research of the authors of this paper, it was found that the cellular concrete powder, applied as an additive to the concrete mix, can increase the compressive strength and the resistance against freezing of concrete [1]. In that paper, the results were compared to a reference mix and a mix that contains air-entraining agent, which is a typical solution to increase concrete durability. Increasing of durability can be achieved by the application of supplementary materials, like silica-fume or metakaolin. Present paper is dealing with the comparison of concrete with metakaolin and cellular concrete powder, on the basis of compressive strength and frost resistance, using them as a cement substituting material. Different amount of metakaolin and CCP were added to the concrete mix, by substituting a given percentage (3, 10 or 17%) of cement with them. The results show the positive effect of both supplementary materials and based on present research the maximum amount of useful CCP can be approximated for the given concrete mix.

PL

Przedstawiony program badawczy dotyczy wpływu sproszkowanego betonu komórkowego (CCP) na wytrzymałość betonu na ściskanie i jego trwałość. CCP jest przemysłowym produktem ubocznym, który został zastosowany jako dodatek do cementu w mieszance betonowej. W poprzednich badaniach autorów tego artykułu stwierdzono, że sproszkowany beton komórkowy, stosowany jako dodatek do mieszanki betonowej, może zwiększać wytrzymałość na ściskanie i odporność na zamarzanie betonu [1]. W tym artykule porównano wyniki z mieszanką referencyjną i mieszanką zawierającą domieszkę napowietrzającą, co jest typowym rozwiązaniem zwiększającym trwałość betonu. Zwiększenie trwałości można osiągnąć przez zastosowanie dodatków w postaci pyłu krzemionkowego lub metakaolinu. W niniejszym artykule przedstawiono porównanie betonu z metakaolinem i sproszkowanym betonek komórkowym w odniesieniu do wytrzymałości na ściskanie i mrozoodporności, wykorzystując te dodatki jako materiał zastępujący cement. Do mieszanki betonowej dodano różne ilości metakaolinu i CCP, zastępując nimi określony procent (3, 10 lub 17%) cementu. Wyniki badań pokazują pozytywny wpływ obu dodatków i pozwalają wyznaczyć dla danej mieszanki betonowej maksymalną przybliżoną wartość CCP.

19

Wpływ bio-popiołów na wybrane właściwości zapraw cementowych

Jura J., Ulewicz M.

Przegląd Naukowy Inżynieria i Kształtowanie Środowiska

|

2017

|

Vol. 26, No. 2

234--240

PL

W artykule przedstawiono możliwość wykorzystania popiołu lotnego ze spalania dwóch rodzajów biomasy w kotle fluidalnym do modyfikacji składu zapraw cementowych. Określono wpływ wykorzystania popiołów lotnych na ich właściwości mechaniczne i fizyczne (wytrzymałość na ściskanie, mrozoodporność, nasiąkliwość) zapraw. W badaniach część piasku normowego zastąpiona została popiołami lotnymi ze spalania drewna z dodatkiem łupin orzecha kokosowego oraz drewna z dodatkiem słonecznika w ilości 10, 20 i 30% masy cementu. Dodatek popiołu wpłynął, w zależności od składu, na zwiększenie wytrzymałości na ściskanie nawet o ponad 17%, zmniejszenie spadku wytrzymałości na ściskanie po badaniach mrozoodporności do wartości 0,5%, a także nieznaczne wzrosty ubytku masy i nasiąkliwości.

EN

Paper presents the possibility of using fly ash from the combustion of two types biomass in fluidized bed boiler to modifications cement mortars composition. The influence of the use of ashes on their mechanical and physical properties (compressive strength, frost resistance, water absorption) of cement mortars. In research part of standarized sand was replaced by fly ash from the combustion of wood with coconut husks and wood with sunflower in the amount of 10, 20 and 30% by weight of cement. The addition of ash, depending on the composition, increase the compressive strength about 17%, decrease a reduction compressive strength after frost resistance tests to 0,5% and slightly increases weight loss and absorbency.

20

Prefabrykacja betonowa. Cz.5 Materiałowe aspekty produkcji

Adamczewski G., Woyciechowski P.

Builder

|

2017

|

R.21, nr 7

70--72, 74