Microstructural and thermal characterization of the TeO2–WO3 system

Celikbilek M., Karaduman G., Ersundu A. E., Solak N., Tatar D., Aydin S.

Materiały Ceramiczne

2010

T. 62, nr 4

556-559

In the present study, thermal behaviour and microstructure of the TeO2–WO3 system have been investigated. Different compositions of (1-x)TeO2 – xWO3 system (x = 0.02, 0.05, 0.15, 0.25 and 0.40 in molar ratio) were prepared. The samples waited at 750°C in a platinum crucible for 30 min and then quenched in a water bath. DTA studies were performed on glassy samples. Afterwards, all samples were heat-treated at 550°C for 24 h and furnace cooled to obtain phase equilibrium. XRD and SEM/EDS studies were performed on the crystallized samples for microstructural analysis.

W prezentowanej pracy zbadano zachowanie cieplne i mikrostrukturę tworzyw w układzie TeO2-WO3. Przygotowano różne składy układu (1-x)TeO2 – xWO3, gdzie x = 0.02, 0.05, 0.15, 0.25 i 0.40 w stosunku molowym. Próbki przebywały w 750°C w tyglu platynowym przez 30 min a potem szybko chłodziły się w wodzie. Badania DTA przeprowadzono na próbkach szklistych. Następnie, wszystkie próbki zostały wygrzane w . 550°C przez 24 h i schłodzone z piecem w celu osiągnięcia równowagi fazowej. Badania XRD i SEM/EDS przeprowadzono na krystalizowanych próbkach w przypadku analizy mikrostrukturalnej.