1

Ozone Effect On the Properties of Aramid Fabric

Wang Y., Wiener J., Militky J., Mishra R., Zhu G.

Autex Research Journal

|

2017

|

Vol. 17, no. 2

164--169

EN

The limitation of aramid fiber is its surface property, which results in its very poor interfacial adhesion to most of commercial resins. In order to improve the surface property of the aramid fiber, ozone treatment was carried out in this work. The aramid fabrics were evaluated in terms of surface morphology, wicking effect, tensile property, and ball bursting test. The results showed that the surface morphology of aramid fabrics did not undergo an obvious change; the wicking effect increased slightly with an increase in ozone treatment time; the tenacity and elongation of aramid fibers and fabrics did not significant change after ozone treatment, but the tenacity and elongation of aramid yarns showed significant improvement after ozone treatment, and increased with the increase of ozone treatment time; the ball bursting load and penetration displacement had a slight increase as well after ozone treatment. Therefore, ozone treatment could be one method to improve the surface property of the aramid fiber.

2

Problemy klejenia komponentów z lekkich kompozytów odpornych na przebicia

Godzimirski J., Tkaczuk S.

Technologia i Automatyzacja Montażu

|

2016

|

nr 2

40--46

PL

Zbadano przydatność kilku klejów do łączenia ceramiki typu SiC i Al2O3 z tkaniną aramidową Mikroflex. Zaproponowano próbki do badania wytrzymałości połączeń klejowych tych materiałów na ścinanie i oddzieranie. Przeprowadzone badania wykazały gorsze właściwości adhezyjne ceramiki SiC. Jednak w badaniach wytrzymałościowych na oddzieranie stwierdzono kohezyjne zniszczenie spoin klejowych na powierzchni ceramiki SiC. Założono, że przyczyną takiego zniszczenia może być ukosowanie krawędzi płytek, wytworzonych z tego materiału. Potwierdziły to przeprowadzone obliczenia numeryczne. Wynika z tego, że charakter zniszczenia połączeń klejowych (adhezyjny lub kohezyjny) wynika nie tylko z właściwości adhezyjnych powierzchni łączonych materiałów i właściwości kleju, ale również zależy od kształtu i sposobu obciążenia połączenia klejowego, z których wynika rozkład naprężeń w spoinie klejowej.

EN

Examining the feasibility of a number of adhesives for bonding ceramic type SiC and Al2O3 with aramid fabric Mikroflex. Proposed sample for testing the strength of adhesive bonds these materials shear and peel strength. The study showed poorer adhesion properties of SiC ceramics. However, strength tests peel found cohesive destruction of the adhesive joints on the surface of SiC ceramics. It was assumed that the cause of such destruction can be scarfing tiles made from this material. This was confirmed by numerical calculations carried out. It follows that the failure mode of the bond (adhesive or cohesive) derives not only from the surface of the adhesive properties of the joined materials and adhesive properties, but also depends on the shape and method of loading of the glue joint, which shows the stress distribution in the adhesive joint.

3

Numeryczna analiza uderzenia pocisku w warstwy aramidowe umieszczone na podłożu imitującym ciało człowieka

Pacek D., Wiśniewski A.

Problemy Techniki Uzbrojenia

|

2016

|

R. 45, z. 139

61--79

PL

Przedmiotem artykułu jest wskazanie istotnych aspektów analizy numerycznej uderzenia pocisku w elastyczne warstwy tkaniny aramidowej umieszczone na plastycznym podłożu imitującym ciało człowieka. Przedstawiono przegląd wyników badań kamizelek kuloodpornych na różnych podłożach oraz uzasadniono potrzebę ich stosowania. Wyjaśniono, dlaczego plastelina balistyczna jest podkładem imitującym ciało człowieka obowiązującym w większości światowych norm związanych z badaniem osłon osobistych. Zaprezentowano metody modelowania tkanin oraz wyniki własnych analiz numerycznych. Ze względu na istotny wpływ wzajemnego oddziaływania wiązek włókien (przędz) tworzących przeplot tkaniny na jej deformację, jest ona przedstawiona w symulacjach za pomocą modelu bezpośrednio opisującego jej mezostrukturę. Symulacje przeprowadzono z użyciem, wykorzystującego jawny schemat całkowania równań ruchu, programu ANSYS AUTODYN v.16. Przedstawiono wyniki symulacji uderzenia 9 mm pocisku Parabellum FMJ (Full Metal Jacket) w warstwy tkaniny Twaron® T750 umieszczone na plastelinie balistycznej. Wyniki symulacji porównano z wynikami uzyskanymi podczas badań kuloodporności.

EN

Essential aspects of numerical analysis for bullet hitting elastic layers of aramid fabric placed on a plastic substratum imitating the human body are presented in the paper. A review of results for bullet-proof vests tested on various substrata is included in the paper with justification of their use. It is explained why the ballistic plasticine is used as a sub-structure imitating the human body in most standards binding in the world for testing individual protections. Methods for modelling the fabrics with results of own numerical analyses are presented. As mutual reaction of yarns creating the interweaving of the fabric has an essential impact on its deformation then it is represented in simulations by a model that directly describes its mezzo-structure. Simulations were carried out by using an explicit procedure for integration of motion equations in program ANSYS AUTODYN v.16. The results of hitting by 9 mm bullet Parabellum FMJ (Full Metal Jacket) into the layers of Twaron® T750 fabric placed on ballistic plasticine are presented. Results of simulation and bulletproof resistance tests are compared.

4

Performance Stability of Ballistic Para-Aramid Woven Fabrics Modified by Plasma-Assisted Chemical Vapour Deposition (PACVD)

Struszczyk M. H., Puszkarz A. K., Miklas M., Wilbik-Hałgas B., Cichecka M., Urbaniak–Domagała W., Krucińska I.

Fibres & Textiles in Eastern Europe

|

2016

|

Vol. 24, no. 4 (118)

92--97

EN

Plasma-assisted chemical vapour deposition (PACVD) is often used for the modification of the surface properties of a wide range of materials. The resulting effect of PACVD modification considerably changes the behaviour of the material. The process of surface modification by PACVD of a textile is significantly complex due to the topography resulting in the fabric structure. Taking ecology and economy into account, PACVD modification is more efficient as compared with traditional finishing processes. However, the stability of the PACVD effect gets lost during usage of the textile under standard conditions. The aim of the research was to verify in an enhanced accelerated ageing test the stability of PACVD modification of para-aramid woven fabrics applied for designing of soft ballistic inserts in body protectors. The simulated ageing yielded a significant change in the mechanical properties of non-modified textiles, whereas PACVD-modified samples showed prolonged stability of the properties obtained.

PL

Technika plazmy niskotemperaturowej (PACVD) jest często stosowana do modyfikacji właściwości powierzchni szerokiej gamy materiałów. Uzyskany efekt modyfikacji PACVD zmienia znacznie zachowanie się materiału. Proces modyfikacji PACVD wyrobów włókienniczych jest bardziej złożony ze względu na topografię wynikająca z ich struktury. Biorąc pod uwagę aspekty ekologii i ekonomii, modyfikacja PACVD jest bardziej efektywna, w porównaniu do tradycyjnych procesów wykończeniowych. Jednakże uzyskany efekt jest tracony w czasie użytkowania wyrobów włókienniczych w warunkach standardowych. Celem prowadzonych badań była weryfikacja w czasie przyspieszonego starzenia stabilności modyfikacji PACVD tkaniny ar amidowej stosowanej do projektowania miękkich wkładów balistycznych. W wyniku symulacji starzenia niezmodyfikowane tekstylia traciły swoje właściwości użytkowe szybciej niż w przypadku próbek modyfikowanych PACVD.

5

Modelowanie numeryczne uderzenia pocisku w ciało człowieka chronione kamizelką kuloodporną

Dominiak J., Stempień Z.

Mechanik

|

2013

|

R. 86, nr 7

585--590

PL

W chwili uderzenia pocisku w miękką kamizelkę kuloodporną chroniącą ciało człowieka wysoko wytrzymałe warstwy tekstylne osłony balistycznej pochłaniają energię pocisku. Część tej energii, która nie zostanie zaabsorbowana przez warstwy kamizelki, jest przejmowana przez ciało człowieka, co w literaturze określane jest jako „trauma balistyczna”. Celem badań było opracowanie modelu dyskretnego „pocisk Parabellum 9 × 19 mm – tekstylna osłona balistyczna – ciało człowieka” oraz numeryczna analiza skutków udaru balistycznego dla różnych konstrukcji osłon. Model geometryczny ciała człowieka odwzorowano na podstawie obrazów z tomografii komputerowej. Uwzględniono w nim najważniejsze organy decydujące o utrzymaniu funkcji życiowych. Poszczególne warstwy kamizelki kuloodpornej modelowano jako dopasowane powłoki, wykorzystując specjalistyczne oprogramowanie do projektowania odzieży zgodnie z cyfrowym modelem człowieka. Badania pokazały, że redukcja skutków udaru balistycznego podczas uderzenia pocisku wymaga nie tylko zastosowania wysoko wytrzymałych włókien, lecz także doboru odpowiedniej liczby warstw.

EN

At the moment of bullet impact into the ballistic package protecting human body absorbing the bullet’s energy by the ballistic layers appears. However, the part of bullet’s energy which is not absorbed by the layers of body armor, is taken by human torso. The aim of presented research is creating the discrete model „bullet Parabellum 9 × 19 mm – textile aramid vest – human body” and numerous analysis of ballistic impact results. The model of human body was based on the pictures from the computer tomography. In the geometrical model the most important organs, which keep human body function were taken into consideration.

6

Koncepcja osobistej osłony balistycznej z wykorzystaniem tkanin aramidowych i węglików spiekanych

Juskowiak E., Rybczyński R., Kurowski J., Jamroziak K.

Przetwórstwo Tworzyw

|

2012

|

[R.] 18, nr 3

217-221

PL

W pracy wykonano badania porównawcze próbek materiałowych o przeznaczeniu na kompozytowe, osobiste osłony balistyczne. Celem badań było sprawdzenie zachowania się w materiale balistycznym węglika spiekanego podczas prób na przestrzelenie. Metodą formowania w autoklawie wykonano 3 typy próbek. Były to próbki wzmocnione tkaniną aramidową w układzie: tkanina aramidowa z jedną warstwą płytek z węglika spiekanego i tkanina aramidowa z dwiema warstwami płytek z węglika spiekanego. Układy warstwowe tkanin aramidowych i węglików spiekanych nasycano żywicą epoksydową. Dodatkowo badaniu poddano próbkę handlową wykonaną z 5 warstw tkanin aramidowych na matrycy elastomerowej. Wszystkie cztery typy próbek badano pod kątem ich odporności na amunicję pistoletową 9x19 mm Parabellum. Próbki zostały ostrzelane z odległości 10m, oddając co najmniej trzy strzały do każdej. Pozytywne wyniki (brak przestrzelenia) zarejestrowano dla próbek: próbka wzmocniona aramidem bez węglików oraz próbka wzmocniona Aramisem z podwójną warstwą węglików spiekanych. Próbka z pojedynczą warstwą węglików spiekanych została przestrzelona. W kolejnych badaniach postuluje się użycie spoiw elastyczniejszych od zastosowanych np. elastomerowych, złagodzenie ostrych krawędzi płytek węglikowych oraz przełożenie warstwy płytek tkaniną aramidową.

EN

The paper presents a comparative study of samples of materials intended for use as composite personal armor. The aim of the study was to examine the behavior of sintered carbides in ballistic material in ballistic resistance test. 3 types of samples were made by molding in an autoclave. These samples were reinforced with aramid fabric, aramid fabric with one layer of tiles of sintered carbides and aramid fabric with two layers of sintered carbides. Layered systems of aramid fabrics and sintered carbides were impregnated in epoxy resin. Additionaly, a commercial sample of aramid fabrics bonded with elastomer was studied. All four types of samples were tested for their resistance to the ammunition 9x19 mm Parabellum. Each sample was shot from a 10m distance at leat three times. The sample with aramid only and sample reinforced with aramid and double layer of sintered carbides have passed this test. A sample of a single layer of sintered carbides was shoot trough. In further studies saturants more flexible from used for example elastomeric, sharping the edges of sintered carbides and covering the layer of sintered carbides with aramid layer are postulated.