Content available remote Experimental phase studies in the TeO2–CdO system
EN
In the present study, phase equilibrium in the TeO2–CdO system has been investigated. Different compositions of (1-x)TeO2–xCdO, where x = 0.10, 0.20, 0.25, 0.30 and 0.40 in molar ratio were prepared. The samples waited at 750°C in a platinum crucible for 30 minutes and then quenched in a water bath. DTA studies performed on as-cast samples. According to the DTA results, all samples were heat-treated at 550°C for 24 hours to obtain phase equilibrium. XRD and SEM/EDS studies were performed on the crystallized samples for microstructural analysis.
PL
W prezentowanej pracy zbadano równowagę fazową w układzie TeO2–CdO. Przygotowano różne składy (1-x)TeO2 – xCdO, gdzie x = 0,10, 0,20, 0,25, 0,30 i 0,40 mol.%. Próbki przetrzymywano w 750°C w tyglu platynowym przez 30 min., a następnie szybko chłodzono w kąpieli wodnej. Badania DTA przeprowadzono na świeżo wytopionych próbkach. Zgodnie z wynikami DTA, wszystkie próbki wygrzewano w 550°C przez 24 h, aby uzyskać stan równowagi fazowej. Badania XRD i SEM/EDS przyprowadzono na wykrystalizowanych próbkach w przypadku analizy mikrostrukturalnej.
2
Content available remote Microstructural and thermal characterization of the TeO2–WO3 system
EN
In the present study, thermal behaviour and microstructure of the TeO2–WO3 system have been investigated. Different compositions of (1-x)TeO2 – xWO3 system (x = 0.02, 0.05, 0.15, 0.25 and 0.40 in molar ratio) were prepared. The samples waited at 750°C in a platinum crucible for 30 min and then quenched in a water bath. DTA studies were performed on glassy samples. Afterwards, all samples were heat-treated at 550°C for 24 h and furnace cooled to obtain phase equilibrium. XRD and SEM/EDS studies were performed on the crystallized samples for microstructural analysis.
PL
W prezentowanej pracy zbadano zachowanie cieplne i mikrostrukturę tworzyw w układzie TeO2-WO3. Przygotowano różne składy układu (1-x)TeO2 – xWO3, gdzie x = 0.02, 0.05, 0.15, 0.25 i 0.40 w stosunku molowym. Próbki przebywały w 750°C w tyglu platynowym przez 30 min a potem szybko chłodziły się w wodzie. Badania DTA przeprowadzono na próbkach szklistych. Następnie, wszystkie próbki zostały wygrzane w . 550°C przez 24 h i schłodzone z piecem w celu osiągnięcia równowagi fazowej. Badania XRD i SEM/EDS przeprowadzono na krystalizowanych próbkach w przypadku analizy mikrostrukturalnej.