Surface condition of La2Zr2O7 based TBC system after hot corrosion in molten sulfate Na2SO4 salts

Jasik Anna, Moskal Grzegorz, Jucha Sebastian, Kuligowski Krzysztof

Ochrona przed Korozją

2019

nr 3

82--85

The top coat of thermal barrier coatings systems based on lanthanum zirconate after corrosion tests in molten sodium sulphide salt at 920 and 970°C was characterized in this article. Scanning electron microscopy and X-ray diffraction methods were used to analyse surface topography, as well as the phase composition of corrosion products. It was determined the La2Zr2O7 coatings exhibit very good corrosion resistance in liquid salt environments. The basic destruction process has been associated with the formation of a lanthanum sulphate phase. Additionally, an effect similar to thermal etching was observed in splat areas, as well as a cracks network formed in the interspalt areas.

Artykuł dotyczy charakterystyki warstwy wierzchniej ceramicznych powłok izolacyjnych w systemach powłokowych barier cieplnych na bazie cyrkonianu lantanu w warunkach korozji wysokotemperaturowej w ciekłych osadach siarczanu sodu w temperaturze 920 i 970°C. Jako podstawową metodykę badawczą zastosowano skaningową mikroskopię elektronową w celu charakterystyki topografii powierzchni oraz rentgenowską analizę strukturalną, której celem była charakterystyka składu fazowego produktów korozji. Stwierdzono, że powłoki typu La2Zr2O7 charakteryzują się wysoką odpornością korozyjną, a jedynymi procesami degradacji korozyjnej jest tworzenie siarczanu lantanu. Dodatkowo stwierdzono również tworzenie się efektów zbliżonych do trawienia termicznego w obrębie przetopionych cząstek oraz siatki pęknięć w na ich granicach.