Examination of mechanical behaviour of aged duplex steel using X-ray and neutron diffraction methods

Baczmański A., Dakhlaoui R., Braham C., Wierzbanowski K.

Archives of Metallurgy and Materials

|

2008

|

Vol. 53, iss. 1

89-96

EN

The parameters characterizing the elastoplastic mechanical behaviour of each phase in austeno-ferritic duplex stainless steels were determined using X-ray and neutron diffraction during a uniaxial tensile test. The elastoplastic self-consistent model was used to predict the evolution of the lattice elastic strains during loading and to identify the critical resolved shear stresses and work hardening parameters of the material. The effect of ageing treatment on the elastoplastic behaviour of both phases was also studied. It was found that thermal ageing of austeno-ferritic steel caused microstructural transformations and consequently a significant increase of the hardness of ferrite, while the mechanical properties of austenite remained practically unchanged.

PL

Parametry opisujące własności sprężysto-plastyczne każdej z faz w nierdzewnej stali austeno-ferrytycznej zostaly wyznaczone przy użyciu dyfrakcji rentgenowskiej i neutronowej podczas testu rozciągania in situ. Zastosowano sprężysto-plastyczny model samo-uzgodniony do przewidywania sprężystych odkształceń sieci podczas próby rozciągania oraz do wyznaczenia krytycznych naprężeń ścinających na płaszczyznach poślizgu i parametrów umocnienia materiału. Zbadano również efekt wplyw starzenia na własności sprężysto-plastyczne obu faz. Stwierdzono, że proces termicznego starzenia stali austeno-ferrytycznej spowodowal transformacje mikrostrukturalne i w konsekwencji wyrainy wzrost twardoki ferrytu, podczas gdy własności mechaniczne austenitu pozostaly praktycznie niezmienione.

2

EBSD study of corrosion fatique of austenic-ferritic steel

Głowacka A., Nolze G., Świątnicki W. A.

Archives of Metallurgy and Materials

|

2006

|

Vol. 51, iss. 1

7-10

EN

Fatigue crack propagation investigations have been performed in austenitic-ferritic duplex stainless steel 00H22N5M3 in air and during hydrogen charging, using various frequencies of loading. Strong differences of crack propagation velocity depending on the test conditions were noticed. Lower frequency with applied hydrogen charging led to the huge increase of crack propagation velocity compared to the tests performed in air. To understand such a behaviour in each case and characterize crack mode, the samples were observed using electron back-scattered diffraction (EBSD). It was shown that in air, the fatigue crack propagation involved plastic deformation and the resulting cracks had ductile character. The presence of hydrogen led to more brittle mode of cracking. This effect was also connected with frequency of loading: lower frequency, which assured longer time for hydrogen-crack tip interaction, resulted in the highest crack propagation velocity and the brittle cracking mode with lower amount of plastic deformation. The performed observations indicated that the path of the crack went mostly transgranularly through both austenite and ferrite phases. Phase and grain boundaries were not the preferred paths for crack propagation.

PL

Tematem pracy były badania propagacji pęknięć zmęczeniowych w niskowęglowej dwufazowej stali ferrytyczno-austenitycznej typu 00H22N5M3 w atmosferze otoczenia oraz w warunkach nasycenia wodorem. Stwierdzono występowanie istotnych różnic w prędkości rozprzestrzeniania się pęknięć w zależnosci od rodzaju testów. Niższe częstotliwości cyklicznego obciążenia w połączeniu z ładowaniem wodorem prowadziły do znaczącego wzrostu prędkości propagacji pęknięć zmęczeniowych w porównaniu do testów przeprowadzonych w powietrzu. Celem prześledzenia przebiegu pęknięć zmęczeniowych poprzez materiał oraz określenia ich charakteru próbki były zanalizowane przy użyciu dyfrakcji elektronów wstecznie rozproszonych EBSD. Rozprzestrzenianie się pęknięć w powietrzu prowadziło do odkształceń plastycznych dając w rezultacie pęknięcia o charakterze ciągłym. Obecność wodoru prowadzi do bardziej kruchego pękania. Efekt jest również zwiazany z częstotliwością cyklicznego obciążania. Niższe częstotliwości, połączone z dłuższym oddziaływaniem wodoru z koniuszkiem pękniecia, prowadzą do maksymalnej prędkości propagacji. Pękanie ma charakter kruchy i praktycznie nie istnieje wokół niego obszar zdeformowany. Przeprowadzone obserwacje udowodniły, iż bieg pękniecia ma charakter transgranularny zarówno w fazie austenitycznej jak i ferrytycznej. Propagacja pęknięć nie występuje wzdłuż granic międzyfazowych i międzyziarnowych.

3

Rolling texture development in duplex type steel with strong initial texture

Ryś J., Ratuszek W., Witkowska M.

Archives of Metallurgy and Materials

|

2005

|

Vol. 50, iss. 4

857-870

EN

The present examination concerns a development of deformation textures in stainless steel of duplex type with strong initial texture. The ferritic-austenitic steel was subjected to cold-rolling within the range up to 90% of reduction. Different rolling conditions were applied employing three variants of rolling reductions per pass. The investigations included texture measurements, X-ray phase analysis and microstructure observations by means of optical microscopy. The occurrence of strong initial textures of both component phases was found after the preliminary thermo-mechanical treatment. Ferrite exhibited the {100}<001> cubic texture and the dominant component of the austenite texture was the {110}< 001> Goss orientation. The crystallographic relation between the major texture components of both phases was described by Bain orientation relationship. The experimental results indicate that formation of the ferrite-austenite banded structure in the course of cold-rolling along with the plastically compatible deformation of both phases result in the stability of major texture components up to high reductions and exert significant effect on the final rolling textures of ferrite and austenite.

PL

Przedstawione badania dotyczą rozwoju tekstur odkształcenia w stali nierdzewnej typu duplex o silnej teksturze wyjściowej. Stal ferrytyczno-austenityczną poddano walcowaniu na zimno zakresie do 90% deformacji. Zastosowano różne warunki walcowania wykorzystując trzy warianty odkształceń częściowych. Przeprowadzone badania obejmowały pomiary tekstur, rentgenowską analizę fazową oraz obserwacje mikrostruktury za pomocą mikroskopii świetlnej. Po wstępnej obróbce cieplno-mechanicznej stwierdzono występowanie silnej wyjściowej tekstury obu składowych faz. Ferryt wykazywał teksturę sześcienną {100}< 001> a w teksturze austenitu dominującą składową stanowiła orientacja Gossa {110}<001>. Relacje krystalograficzną pomiędzy głównymi składowymi wyjściowej tekstury obu faz opisywała zależność Baina. Uzyskane wyniki wskazują, że tworzenie się pasmowej struktury ferrytu i austenitu w trakcie walcowania na zimno przy równoczesnym plastycznie zgodnym odkształceniu obu faz prowadzi do stabilności głównych składowych tekstury do wysokich stopni odkształcenia wywiera istotny wpływ na końcowe tekstury walcowania ferrytu i austenitu.

4

Annealing textures and precipitation behaviour in ferritic-austenitic duplex type steels

Witkowska M., Ryś J., Ratuszek W., Zielińska-Lipiec A.

Archives of Metallurgy and Materials

|

2005

|

Vol. 50, iss. 2

471-478

EN

Development of annealing textures and precipitation behaviour in the course of recrystallization annealing were examined in two ferritic-austenitic stainless steels of duplex type; 00H18N6Mo3 and 00H24N6. Following thermo-mechanical pre-treatment both steels were cold-rolled up to high reductions and subsequently annealed within the temperature range 700÷950°C. Texture changes in the course of annealing resulted from recovery and &frasl or recrystallization processes within the bands of both phases, precipitation of sigma phase and secondary austenite due to the decomposition of ferrite. Differences in ferrite and austenite texture development between both duplex steels are attributed to different contribution of these processes depending on temperature and time of annealing. Contribution of the inverse (&alpha&rarr&gamma) transformation into texture formation results from the amount of strain induced &alpha-phase, which depends on chemical composition and phase stability.

PL

Badania dotyczyły rozwoju tekstur wyżarzania i procesów wydzielania podczas wyżarzania rekrystalizującego dwóch nierdzewnych stali ferrytyczno-austenitycznych typu duplex, 00H18N6Mo3 oraz 00H24N6. Po wstępnej obróbce cieplno-mechanicznej obie stale walcowano na zimno do wysokich odkształceń a następnie wyżarzano w zakresie temperatur 700÷950°C. Zmiany tekstury w trakcie wyżarzania wynikały z procesów zdrowienia i &frasl lub rekrystalizacji w obszarach pasm obu faz, wydzielania fazy sigma i austenitu wtórnego na skutek rozpadu ferrytu. Różnice pomiędzy obiema stalami w rozwoju tekstur ferrytu i austenitu przypisywane są różnemu udziałowi tych procesów zależnie od temperatury i czasu wyżarzania. Udział przemiany odwrotnej (&alpha&rarr&gamma) w tworzeniu tekstury wynika z ilości fazy-&alpha indukowanej odkształceniem i uzależniony jest od składu chemicznego i stabilności fazowej.