Investigation on the Physical and Dimensional Properties of Single Jersey Fabrics made from Cotton Sheath - Elastomeric Core Spun

Kumar V., Sampath V. R.

Fibres & Textiles in Eastern Europe

2013

Vol. 21, no. 3 (99)

73--75

In this study, the physical and dimensional properties of single jersey fabrics made from cotton / elastomeric core spun yarn were investigated. The main purpose of this paper was to investigate the suitability of cotton - spandex core spun yarn for circular knitting as an alternative for bare spandex feeding and the effect of stitch length variables on knitted fabric geometric quality attributes such as wale density, course density, stitch density and areal density under different states of relaxation. The results clearly indicate that the resulting yarn is highly suitable for circular knitting and change in stitch length values does not have any significant impact on wale density values. At the same time, the remaining geometric properties of the samples were found to be inversely proportional to the stitch length values uniformly at all the states of relaxation. Along with this, the ability of the samples to reach the dimensional equilibrium state after repeated cycles of washing and drying was also studied. It is evident from the results that all the three samples produced with ascending stitch length orders attained a perfect state of dimensional stability before five cycles of washing and drying, and also the sample knitted with the smallest stitch length value reached its equilibrium state in a quick time.

Głównym celem badań była ocena możliwości zastosowania przy produkcji dzianin na maszynach cylindrycznych bawełnianych przędz rdzeniowych elastomerowych jako alternatywę dla stosowania gołych przędz elastomerowych. Badano również wpływ długości splotu na geometrie i jakość dzianin, w tym na gęstość rządków i kolumienek, gęstość splotów i gęstość powierzchniową przy rożnych stanach relaksacji. Uzyskane wyniki wyraźnie wskazują, że proponowana przędza nadaje się jak najbardziej do projektowanego zastosowania. Stwierdzono również, że zmiany długości splotu nie mają wyraźnego wpływu na gęstość kolumienkową. Jednocześnie stwierdzono, że geometryczne właściwości próbek są odwrotnie proporcjonalne do długości splotu. Badano również zdolność próbek do osiągnięcia geometrycznej równowagi po kolejnych powtarzanych cyklach prania i suszenia. Stwierdzono, że wszystkie wyprodukowane próbki uzyskiwały stabilność wymiarową przed piątym cyklem prania i suszenia, w tym również te, które miały najmniejszą długość splotu.

Properties of plain knits from siro-spun viscose/spandex yarns

Beceren Y., Candan C., Duru Cimilli S., Ülger K.

Fibres & Textiles in Eastern Europe

2010

Vol. 18, no. 1 (78)

41--46

This paper focuses on the dimensional and selected physical properties of a series of plain jersey fabrics made from viscose siro-spun and carded ring yarns of 2/10 tex and 20 tex, respectively. Elastane yarn was incorporated into the fabric using the plaiting technique. In general, for both greige and dyed knitted fabrics, the stitch density decreased, whereas the weight increased as the stitch length increased. Moreover, for greige and dyed dry-relaxed fabrics from siro yarn, the twist had an influence on fabric properties, the effect being relatively more prominent for slack samples. Moreover, both slack and tight dry relaxed dyed samples from high twist siro yarns featured lower resistance to abrasion. As far, as dyed and laundered samples from siro yarns are concerned, the results revealed that irrespective of the loop length, the samples from average twist siro yarns tended to give a higher stitch density and weight values. When abrasion resistance values of samples from both average and high twist siro yarns were studied, it could be suggested that in addition to yarn properties, the effect of fabric properties on the abrasion behavior of the samples became more prominent after laundering. As far as the abrasion resistance and pilling properties of the samples are concerned, the fabrics from siro-spun yarns tended to perform better. Finally, the pilling test method employed affected not only the size and shape of the pill entanglements on the surface of the samples but also the degree of fibre damage within the fuzz entanglements.

W pracy omówiono właściwości geometryczne i wybrane parametry fizyczne serii dzianin lewo-prawych wykonanych z przędz wiskozowych typu siro-spun i zgrzeblonych przędz obrączkowych o masie liniowej 2/10 tex i 20 tex. Przędze elastomerowe zostały wprowadzone w dzianinę metodą wplecenia. Ogólnie można powiedzieć, że zarówno dla dzianin surowych jak i barwionych gęstość splotów maleje podczas gdy ciężar powierzchniowy wzrasta wraz ze wzrostem długość splotu. Ponadto, dla surowych i barwionych dzianin z przędzy „siro” relaksowanych w stanie suchym, skręt przędzy ma wpływ na parametry dzianiny. Efekt ten jest bardziej widoczny w przypadku dzianin luźnych. Ponadto dzianiny luźne jak i ścisłe relaksowane w stanie suchym wykonane z przędz typu „siro” o dużym skręcie wykazują mniejsza odporność na ścieranie. Biorąc pod uwagę próbki barwione i prane z przędz „siro, wyniki wskazują, że niezależnie od długości oczka, próbki wykonane z przędz o średniej wartości skrętu posiadają wyższą gęstość splotów oraz większy ciężar powierzchniowy. Biorąc pod uwagę odporność na ścieranie próbek wykonanych z przędz o średniej i dużej wartości skrętu można zasugerować, że efekt wpływu właściwości dzianin na odporność na ścieranie jest bardziej widoczny po praniu. Uwzględniając odporność na ścieranie i piling dzianin można powiedzieć, że dzianiny z przędz „siro” wykazują lepsze właściwości. Metoda sprawdzania pilingu ma istotne znaczenie nie tylko na wielkość i kształt pil i sposób splątania włókien ale również na stopień zniszczenia włókien.