Methods of mitigating alkali reactivity of gravel aggregate

Owsiak Zdzisława, Czapik Przemysław, Zapała-Sławeta Justyna

Structure and Environment

|

2022

|

Vol. 14, no. 3

102--109

EN

Effectiveness of selected chemical admixtures and mineral additives to mitigate alkali-silica reaction was compared based on reactive gravel aggregate. Lithium compounds in the form of nitrate and lithium polysilicate were used as chemical admixtures. Natural pozzolans containing zeolite were used as mineral additive. Efficiency of the additive was enhanced by modification with ammonium ions. Linear changes of mortars with crushed gravel aggregates were studied with the accelerated and long-term methods. Additionally, scanning electron microscopy was used for microstructural observations. It was demonstrated that at elevated temperatures the application of lithium compounds provided better protection. Under conditions similar to those in the field, 20-30% of natural pozzolans proved to be more effective in inhibiting the expansion. Regardless of the method of protection applied, the presence of alkali-silica reaction products was detected in the microstructure of the mortars.

PL

Na przykładzie reaktywnego kruszywa żwirowego porównano efektywność ograniczenia reakcji alkalia-kruszywo przy pomocy wybranych domieszek chemicznych i dodatków mineralnych. Jako domieszki chemiczne zastosowano związki litu w postaci azotanu i polikrzemianu litu. W przypadku dodatków mineralnych zastosowano naturalną pucolanę, zawierającą zeolit, której efektywność zwiększano poprzez modyfikację jonami amonowymi. Wykonano badania zmian liniowych zapraw z rozdrobnionym kruszywem żwirowym metodą przyspieszoną i długoterminową. Dodatkowo wykonano obserwacje mikrostruktury z wykorzystaniem elektronowego mikroskopu skaningowego. Wykazano, że w warunkach podwyższonej temperatury lepsze zabezpieczenie uzyskano po zastosowaniu związków litu. W warunkach zbliżonych do eksploatacyjnych zastosowanie 20-30% pucolany naturalnej skuteczniej hamowało ekspansję zapraw z kruszywem reaktywnym. Niezależnie od sposobu zabezpieczenia, w mikrostrukturze zapraw wykryto obecność produktów reakcji alkalia-krzemionka.

2

Wytrzymałość trójskładnikowych cementów z dodatkiem proszku marmurowego i naturalnej pucolany

Messaoudene I., Jauberthie R., Rechache A., Bounechada A.

Cement Wapno Beton

|

2015

|

R. 20/82, nr 1

32--37

PL

Korzyści związane z dodatkiem wapienia lub naturalnej pucolany do cementu portlandzkiego, zastępujące część tego cementu, są dobrze znane. Jednak oba te dodatki mineralne zmieniają w sposób niekorzystny pewne właściwości cementu. Dodatek wapienia powoduje zwiększenie wczesnej wytrzymałości i zmniejszenie wytrzymałości po twardnieniu zaprawy przez 28 dni. Natomiast pucolana odwrotnie zmniejsza wytrzymałość wczesną a zwiększa po dłuższym okresie dojrzewania zaprawy. W pracy przygotowano i zbadano właściwości zapraw z dwuskładnikowych cementów, w których pucolana zastępowała część cementu oraz z trójskładnikowych, w której część dodatku pucolany zastępowano proszkiem marmurowym. Wyniki pomiarów wytrzymałości wykazały, że zaprawa z cementu zawierającego 10% pucolany i 10% proszku marmurowego ma największą wytrzymałość tak wczesną jak i po 28 dniach oraz 90 dniach twardnienia. Wytrzymałość na ściskanie wynosiła około 63 MPa, a na zginanie około 9 MPa, po 90 dniach twardnienia. Stosowanie cementów trójskładnikowych pozwala więc na usunięcie niekorzystnych właściwości cementów dwuskładnikowych, tylko z dodatkiem wapienia lub pucolany, i przynosi równocześnie korzyści ekonomiczne oraz w zakresie ochrony środowiska, zmniejszając zużycie klinkieru.

EN

The benefits of limestone filler and natural pozzolana as partial replacement of Portland cement are well established. However, both supplementary materials have certain shortfalls. Limestone addition causes only an increase of early strength and decrease the strength of mortars after longer curing. This effect is contrary to pozzolana which reduce the early strength and is improving later ones. In the paper the mortars from binary and ternary cements were produced in which Portland cement was replaced by natural pozzolana and marble powder. Results of strength measurements have shown that mortar from cement with the addition of 10% of pozzolana and 10% of marble powder addition has the highest early strength as well as after 28 and 90 days of hardening. The compressive strength was about 63 MPa and flexural strength was about 9 MPa after 90 days. The use of ternary cements is permitting to overcome the disadvantage of binary cements, only with limestone or pozzolana addition, and simultaneously provides the economic and environmental advantages, by reducing Portland clinker production.

3

Chemiczna aktywacja naturalnej pucolany za pomocą stałego aktywatora

Allahverdi A., Rahmani A.

Cement Wapno Beton

|

2009

|

R. 14/76, nr 4

205-213

PL

Otrzymano spoiwo złożone w 77% z naturalnej pucolany pumeksowej, a w 23% z aktywatora zawierającego ponad 90% cementu portlandzkiego i niewielkie ilości substancji chemicznych złożonych z siarki i metali alkalicznych. Zbadano właściwości zaczynu i zapraw sporządzonych z tego spoiwa. Czas wiązania był zawarty w granicach od 210 minut (początek wiązania) do 300 minut (koniec wiązania). Wytrzymałość zaprawy wzrastała z około 23 MPa po 28 dniach do 45 MPa po rocznym dojrzewaniu. Badania wykazały, że opracowany aktywator pozwala na otrzymanie dobrej jakości spoiwa z naturalnej pucolany pumeksowej. Jest to spoiwo niezwykle przyjazne dla środowiska.

EN

The binder was produced consisting of 77% of natural pozzolana pumice-type and 23% of activator composed chiefly of Portland cement and small addition of chemical substances containing sulfure and alkali metals. The properties of paste and mortars prepared on the basis of this binder were investigated. Setting time of the binder was the range from 210 min (beginning of setting) to 300 minutes (final setting time). The compressive strength was 23 MPa after 28 days of hardening till 45 MPa after one year of curing. The experimental results showed that the elaborated activator gives the possibility for producing good quality binder from natural puzzolana of pumice-type. This binder is very environmental friendly.