Room-temperature sensing performance of hydrogen using palladium-based film by optical setup

Yao Yiyun, Corso Alain J., Bazzan Marco, Tessarolo Enrico, Wang Zhanshan, Huang Qiushi, Qi Runze, Martucci A., Pelizzo Maria G.

Optica Applicata

|

2020

|

Vol. 50, nr 4

649--661

EN

H2 sensing performance of novel Pd–Pt alloy films has been compared with those obtained by using Pd films and H2-reducted PdO films. Two different detecting systems were used to measure the hydrogenation and de-hydrogenation phases with a H2 concentration of both 5% v/v nitrogen and 1% v/v nitrogen at room temperature. The sensitivity loss observed for the Pd–Pt alloy and H2-reducted PdO samples with respect to pure Pd samples can be explained in terms of the reduction in the lattice constant and interstitial volume due to the Pt addition, which determine a decrement of hydrogen atoms penetrating in the films. On the other hand, results show an improvement in time-response for Pd–Pt alloy and H2-reducted PdO films with respect to pure Pd ones, presumably due to the increase of its permeability to H2. Moreover, the sensing measurements repeated after 60 days show that the Pd–Pt alloy films, unlike the Pd-based ones, fully preserve their performances, demonstrating the advantage of the Pt inclusion for stability purposes when the samples are stored upon humidity.

2

Impedance spectroscopy in H2 sensing with TiO2/SnO2 nanomaterials

Szafraniak Bartłomiej, Kusior Anna, Radecka Marta, Zakrzewska Katarzyna

Metrology and Measurement Systems

|

2020

|

Vol. 27, nr 3

417--425

EN

Alternating current a.c. measurements enable to understand the physical and chemical processes occurring in semiconductor materials. Impedance spectroscopy has been successfully applied to study the responses of gas sensors based on metal oxides, such as TiO2, SnO2 and TiO2/SnO2 nanocomposites. This work is devoted to dynamic measurements of hydrogen sensor behaviour over the temperature range of 300-450°C. Frequency dependence of the impedance signal gives evidence that 50 mol% TiO2/50 mol% SnO2 nanocomposites should be treated as resistive-type sensors. Temporal evolution of the response to 500 ppm H2 at 320°C indicates a very short response time and much longer recovery.

3

Baterie akumulatorów stosowanych w zasilaczach UPS oraz warunki ich bezpiecznej eksploatacji

Wiatr J., Herlender K.

Elektro Info

|

2017

|

nr 12

46--51

4

Nanokompozytowe warstwy C-Pd do zastosowania w detekcji wodoru

Czerwosz E., Kamińska A., Kowalska E., Krawczyk S., Kozłowski M., Dłużewski P.

Elektronika : konstrukcje, technologie, zastosowania

|

2015

|

Vol. 56, nr 1

18-24

PL

W artykule zaprezentowano wyniki badań węglowo-palladowych nanokompozytowych warstw (C-Pd), przeznaczonych do zastosowania w czujnikach wodoru. Warstwy były otrzymywane w procesie PVD jak również w procesie dwustopniowym PVD/CVD. Wykorzystano transmisyjną mikroskopię elektronową (TEM) oraz skaningową mikroskopię elektronową (SEM) do badania topografii i morfologii warstw. Badania zmian rezystancji warstw PVD i PVD/CVD pod wpływem gazu zawierającego 1%H₂/N₂ prowadzono w warunkach normalnych. Poza tym badano zmiany rezystancji w warunkach wilgotności powietrza do 80% oraz w zakresie temperatur od -10 do 70°C. Zastosowano spektroskopię FTIR do stwierdzenia obecności molekuł fullerenu C₆₀ i octanu palladu w warstwach. Strukturę molekularną warstw C-Pd badano za pomocą spektroskopii podczerwieni FTIR. W niektórych warstwach obserwowano obecność pasm przypisanych do fulerenu (są to z reguły warstwy PVD). Natomiast w warstwach z procesu dwustopniowego PVD/CVD obecności tych pasm nie stwierdzono.

EN

The results of some properties studies of carbonaceous-palladium (C-Pd) nanocomposite films that can be applied in hydrogen sensors are presented. These films were obtained by PVD method as well as by two-step process PVD/CVD. Transmission electron microscopy (TEM) and scanning electron microscopy (SEM) were used to investigate a topography and a morphology of C-Pd films. The resistivity changes at normal atmosphere and ambient temperature for both kinds of films due to interaction with gas containing 1%H₂/N₂ were measured. The resistivity changes at the temperature range from -10 to 80°C and at humidity up to 80% were also studied. FTIR spectroscopy was used to state the presence of the fullerene C₆₀ and palladium acetate molecules in the film.

5

TiO2-based nanopowders for gas sensor

Radecka M., Jasiński M., Klich-Kafel J., Rękas M., Łysoń B., Czapla A., Lubecka M., Sokołowski M., Zakrzewska K., Heel A., Graule T. J.

Materiały Ceramiczne

|

2010

|

T. 62, nr 4

545-549

EN

Flame spray synthesis (FSS) was used to grow TiO2-based nanopowders from which TiO2:Cr nanosensors were obtained. Structural properties of crystalline TiO2:Cr nanopowders at different Cr loadings (0.1–5.0 at.%) have been investigated. Material studies have been performed using standard methods: X-ray diffraction (XRD) transmission electron microscopy (TEM) and Brunauer-Emmett-Teller adsorption isotherms analysis (BET). High specific surface area (37-126 m2/g) and small crystallite size (9-27 nm) have been reached. Incorporation of Cr into TiO2 lattice affects the specific surface area of nanopowders, the crystallite size and the rutile to anatase ratio. Gas sensing characteristics of TiO2:Cr nanosensors upon interaction with H2 have been recorded in the self-assembled experimental system. The detection of hydrogen was carried out over the concentration range of 50-3000 ppm at the temperatures extending from 200 to 400oC. It is demonstrated that nanomaterials based on TiO2:Cr are attractive for ultimate sensors applications due to a decrease in the operating temperature down to 210-250oC, accompanied by an increase in the sensor response. Taking into account the possible operating costs, the best candidates for the commercial use are TiO2:1 at.% Cr and TiO2:5 at.% Cr nanosensors.

PL

Do otrzymania nanoproszków dla czujników gazu opartych na TiO2:Cr zastosowano syntezę płomieniową FSS (flame spray synthesis). Określono właściwości strukturalne nanoproszków TiO2:Cr o różnych stężeniach Cr (0.1–5.0 at.%). Badane materiały scharakteryzowano za pomocą standardowych metod, a mianowicie dyfrakcyjnej analizy rentgenowskiej (XRD), mikroskopii transmisyjnej (TEM) oraz analizy izoterm adsorpcji Brunauer-Emmett-Tellera (BET). Otrzymano materiały o wysokiej powierzchni właściwej (37-126 m2/g) i rozmiarach krystalitów w zakresie 9-27 nm. Wprowadzenie Cr do sieci TiO2 wpływa na powierzchnię właściwą nanoproszków, rozmiar krystalitu i stosunek rutylu do anatazu. Do pomiaru charakterystyk nanoczujników TiO2:Cr w wyniku oddziaływania z H2 zastosowano specjalnie skonstruowany układ pomiarowy. Wyznaczenie kinetyki zmian oporu elektrycznego spowodowanego zmianą ilości wodoru przeprowadzono w zakresie stężeń 50-3000 ppm H2 w temperaturach od 200 do 400oC. Pokazano, że obniżeniu temperatury pracy do 210-250oC towarzyszy wzrost sygnału pomiarowego, co powoduje, że materiały oparte na TiO2:Cr są atrakcyjne z punktu widzenia zastosowań w czujnikach gazu. Biorąc pod uwagę przewidywane koszty eksploatacyjne, najlepszymi kandydatami do komercyjnego wykorzystania są nanoczujniki TiO2:1 at.% Cr oraz TiO2:5 at.% Cr.