Heat Storage and Release Characteristics of Ceramic-Imbedded Woven Fabric for Emotional Clothing

Kim Hyun Ah, Kim Seung Jin

Autex Research Journal

|

2019

|

Vol. 19, no. 2

165--172

EN

This study examined the heat storage and release characteristics of ZrC-imbedded woven fabrics by light emission and thermal manikin experiments. The surface temperature of the ZrC-imbedded fabric was higher than that of the regular PET fabric. Furthermore, the Clo values of both the total and torso of the ZrC-imbedded fabric by the thermal manikin experiment were higher than those of the regular PET fabric, which suggests that the heat release is caused by far infrared rays emitted from the ZrC particles imbedded in the yarns as they receive light. This was confirmed by the higher emissivity and emissive power of the ZrC-imbedded fabric. However, the tactile hand of the ZrC-imbedded fabric needs to be improved by adjusting the structural parameters of the fabric and finishing process factors.

2

Far-Infrared Emission Characteristics and Wear Comfort Property of ZrC-Imbedded Heat Storage Knitted Fabrics for Emotional Garments

Kim H. A., Kim S. J.

Autex Research Journal

|

2017

|

Vol. 17, no. 2

142--151

EN

This study examined the far-infrared emission characteristics and wear comfort properties of ZrC-imbedded heat storage knitted fabrics. For this purpose, ZrC-imbedded, heat storage PET (polyethylene terephthalate) was spun from high-viscosity PET with imbedded ZrC powder on the core part and low-viscosity PET on the sheath part using a conjugated spinning method. ZrC-imbedded PET knitted fabric was also prepared and its physical properties were measured and compared with those of regular PET knitted fabric. In addition, ingredient analysis and the far-infrared emission characteristics of the ZrC-imbedded knitted fabrics were analyzed by energy dispersive X-ray spectroscopy and Fourier transform infrared spectroscopy. The thermal properties, moisture absorption, and drying properties of the ZrC-imbedded PET knitted fabric were measured and compared with those of the regular PET knitted fabric. The mechanical properties using the FAST (fabric assurance by simple testing) system and the dye affinity of the ZrC-imbedded knitted fabric were also measured and compared with those of regular PET knitted fabric.

3

Zastosowanie spektroskopii odbiciowej w dalekiej podczerwieni do charakteryzacji zwierciadeł Bragga z AlAs/GaAs

Możdżonek M., Gaca J., Wesołowski M.

Materiały Elektroniczne

|

2012

|

T. 40, nr 2

11-16

PL

Metodę spektroskopii odbiciowej w zakresie dalekiej podczerwieni zastosowano do badań zwierciadeł Bragga wykonanych z AlAs/GaAs na podłożu GaAs. Pomiary widm odbicia zwierciadeł zostały wykonane dla różnych kątów padania fali na próbkę oraz z polaryzacją fali s i p. Otrzymane z pomiarów widma analizowane były numerycznie, poprzez dopasowanie widma teoretycznego do widma zmierzonego. Klasyczną teorię dyspersji zastosowano do wyznaczenia funkcji dielektrycznych związków GaAs i AlAs . Z dopasowania widm wyznaczono grubości warstw wchodzących w skład badanej struktury oraz określono koncentracje nośników w warstwach. Wyniki pracy pokazują, że za pomocą widm odbicia z dalekiej podczerwieni można dokonać charakteryzacji zwierciadeł Bragga wykonanych z GaAs/AlAs.

EN

We present a study of GaAs/AlAs Bragg mirrors grown on GaAs substrates. Far-infrared reflectivity spectra were measured using polarized oblique-incidence Fourier transform spectroscopy. The optics of the features observed were analyzed, with respect to a given resonance mode. The far-infrared spectra were numerically modelled within a classical dispersion theory and then compared with the experimental data. The thicknesses of the layers and the free carrier concentration were determined when the best agreement between experimental and calculated spectra was reached. The results demonstrate that the oblique incidence far-infrared reflectance techniques can be applied to the characterization of GaAs/AlAs Bragg mirrors.

4

Kwantowe lasery kaskadowe : podstawy fizyczne

Pabjańczyk A., Sarzała R. P., Wasiak M., Bugajski M.

Elektronika : konstrukcje, technologie, zastosowania

|

2009

|

Vol. 50, nr 5

30-43

PL

W pracy omówiono zasady działania, właściwości i podstawowe zastosowania kwantowych laserów kaskadowych. Przedstawiono także historię ich rozwoju i opisano podstawowe konstrukcje laserów działających w zakresie średniej i dalekiej podczerwieni. Kolejnym zagadnieniem, które zostało przedyskutowane są problemy materiałowe związane z wytwarzaniem laserów kaskadowych.

EN

The paper discusses quantum cascade lasers fundamentals, their properties and basie applications. A brief history of mid-infrared and far-infrared cascade lasers development is presented and basic device designs are reviewed. Finally the materials related aspects and fabrication of cascade lasers are detailed.

5

Określanie koncentracji azotu w monokryształach krzemu otrzymywanych metodą Czochralskiego na podstawie widm absorpcyjnych w zakresie dalekiej podczerwieni

Możdżonek M., Zabierowski P., Majerowski B.

Materiały Elektroniczne

|

2007

|

T. 35, nr 3-4

31-46

PL

Monokryształy krzemu otrzymane metodą Czochralskiego (Cz - Si) domieszkowano azotem poprzez wzrost w atmosferze Ar + N2. Wykonując pomiary absorpcji optycznej po izotermicznych wygrzewaniach zbadano proces generacji płytkich donorów termicznych (STDs) związanych z kompleksami N[indeks dolny]i-O[indeks dolny]mi. Określono warunki procesów termicznych, w których koncentracja defektów ulega nasyceniu ( 650°C min. Igodz. lub 600°C min. 3 godz.). Przedstawiono metodę określania koncentracji azotu w monokryształach Cz - Si w zakresie l x 10[indeks górny]13 ≥ [N] < 5 x 10[indeks górny]14 at.cm-³ opartą o pomiar absorpcji w zakresie dalekiej podczerwieni w niskich temperaturach.

EN

The nitrogen doping of Czochralski silicon crystals was accomplished by adding a small amount of N[sub]2 gas to the argon ambient in the growth chamber. The generation process of shallow thermal donors (STDs) attributed to N[sub]i-O[sub]mi complexes with the measurement of their optical absorption after isothermal annealing was investigated. On the basis of the obtained results, we proposed the annealing conditions when concentration of complexes reaches a saturated value (650°C, min. 1 h or 600°C, min. 3 h). We have defined the method for the quantitative measurement of nitrogen in CZ silicon crystals by means of low temperature Fourier transform infrared spectroscopy (LT-FTIR), based on measurement in the far-infrared range. This method can be used for the detection of the nitrogen concentration in the range of 1 x l0[sup]13 - 5 x l0[sup]14 at.cm-³.