The article presents a comparative analysis of the yarns used for manufacturing hernia meshes. For the analysis, two different linear masses, 46 dtex and 72 dtex, of transparent and dyed yarns were used; the dye used in the yarns was adequate for their intended use. The DSC tests showed the influence of thermal treatment on the change of thermal properties of the yarns. At the same time, it was proved that the aforementioned treatment had a bearing on the changes of crystallinity degree. All types of yarns were also subjected to physicochemical tests required for all the materials used for the production of hernia meshes.
Polypropylene/polyhedral oligomeric silsesquioxane (PP/POSS) nanocomposites were prepared by the melt blending method. Positron Annihilation Lifetime Spectroscopy (PALS) was used to study the effects of the structure and of the amount of POSS on the free volumes in PP. The PALS parameters: o-Ps lifetime and its intensity, were compared to the crystallinity degree and to the mass flow rate (MFR) of nanocomposites. The presence of POSS nanofillers affected the PP microstructure and the size and number of free volumes in the polymer. The crystallinity degree was decreased and the intensity of o-Ps component was increased by increasing POSS contents. The MFR values increased for nanocomposites, thus POSS nanoparticles can act as plasticizers and generate more free volumes in PP.
PL
Nanokompozyty polipropylen/poliedryczne oligomeryczne silseskwioksany (PP/POSS) przygotowano metodą mieszania w stanie stopionym polimeru. Wpływ struktury oraz ilości zastosowanych nanonapełniaczy POSS na objętości swobodne w polipropylenie określono z zastosowaniem spektroskopii czasów życia pozytonów (PALS). Ustalono zależności pomiędzy parametrami PALS: czasem życia o-Ps (τ3) inatężeniem (I3) składowej o-Ps oraz wartościami stopnia krystaliczności (Xc) i masowego wskaźnika szybkości płynięcia (MFR) badanych materiałów. Obecność nanonapełniaczy POSS wpłynęła na liczbę i rozmiary objętości swobodnych w polimerze, co spowodowało zmianę mikrostruktury osnowy polipropylenowej. Wraz ze zwiększaniem zawartości napełniaczy POSS zmniejszał się stopień krystaliczności kompozytów, zwiększało natężenie składowej o-Ps, adodatkowo wzrastała wartość MFR – nanocząstki POSS pełniły w układzie rolę plastyfikatorów.
3
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
The article presents the results of analysis and research of the disc plasticizing mechanism operation on the mechanical, thermal, and structural properties of extruded material. The analysis of velocity distribution and trajectories of the material's displacement leads to a conclusion that the flow of polymer melt through the clearance between the discs arranges the supermolecular structure and in this way results in an extrudate with improved mechanical properties.
PL
Przedstawiono wyniki badań i analizy wpływu oddziaływania tarczowego mechanizmu uplastyczniającego na właściwości wytłaczanego tworzywa (rys. 1, 4). Na podstawie rozkładu prędkości i trajektorii ruchu tworzywa (rys. 2, 3) wnioskowano, że przepływ tworzywa polimerowego w szczelinie tarczowej (w stopniu zależnym od jej wymiaru, rys. 2) sprzyja porządkowaniu struktury nadcząsteczkowej (tabela 1, rys. 6, 7), dzięki czemu można otrzymać wytłoczynę o właściwościach mechanicznych (tabela 2) lepszych niż uzyskane w wyniku wytłaczania ślimakowego.
4
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Przedstawiono wyniki badań charakterystyki odkształceniowo-naprężeniowej uzyskane w próbie cyklicznego rozciągania - ściskania, przy założeniu stałego poziomu amplitudy odkształcenia. Badaniom poddano poliacetal oraz jego kompozyty o zawartości 10 i 26% włókna szklanego. Rejestrowano zależność pomiędzy naprężeniem i wydłużeniem próbki, uzyskując pętle histerezy. Wykazano zmiany właściwości mechanicznych badanych próbek spowodowane cyklicznym obciążeniem. Badano strukturę oraz wyznaczono metodą DSC stopień krystaliczności próbek nieobciążonych i po obciążeniu.
EN
The results of investigations of strain-stress characteristics obtained during the cyclic tensile - compression test, at constant level of strain amplitude were presented in this work. Polyacetal and its composites filled with 10 and 26% of glass fibre have been tested. The relationship between tensile stress and elongation of the sample was recorded. As a result hysteresis loops were obtained. The change in mechanical properties and structure of test specimens caused by cyclic loading has been shown. The degree of crystallinity was determined using DSC method.
A method was developed for the preparation of chitosan staple fibres containing silver nanoparticles. An aqueous colloidal solution of PVA-encapsulated metallic silver with a particle size of 50-60 nm was admixed to the chitosan-containing spinning solution. From the mixed spinning solution, the fibre was spun by a wet method. The mechanical, electrical, antibacterial, morphological and structural properties of the silver-containing chitosan fibre are highlighted. With a silver content greater than 51 mg/kg, the fibre possessed antibacterial activity. The silver content did not deteriorate the tenacity of the fibre or cause a change in the molecular mass distribution. The impact of spinning conditions on the morphological properties was assessed by scanning electron microscopy (SEM) and atomic force microscopy (AFM). X-ray radiography (WAXS) showed the influence of spinning conditions on the supermolecular structure of the fibre.
PL
W artykule opisano metodę otrzymywania i właściwości odcinkowych włókien chitozanowych zawierających nanocząstki srebra. Podczas przygotowania roztworu przędzalniczego z chitozanu krewetkowego, wprowadzono koloidalny wodny roztwór nanocząstek srebra metalicznego o rozdrobnieniu 50-60 nm w otoczce ochronnej PVA, a następnie formowano włókna metodą mokrą. Omówiono także właściwości mechaniczne, elektryczne, morfologiczne, przeciwbakteryjne oraz strukturalne otrzymanych włókien. Włókna charakteryzowały się właściwościami bakteriobójczymi przy zawartości srebra powyżej 51 mg/kg. Zawartość nanocząstek srebra nie wpłynęła na wytrzymałość właściwą włókien chitozanowych natomiast analiza rozkładu mas cząsteczkowych włókien wykazała zmiany. Dokonano oceny wpływu warunków formowania na właściwości morfologiczne otrzymanych włókien stosując AFM. Badania rentgenograficzne WAXS wykazały wpływ warunków formowania na budowę nadcząsteczkową włókien.
The influence of oak wood age on the crystallinity index of cellulose was determined. Antique wood originating from Warsaw woodwork from the middle of the 18th century, the turn of XIXth and 20th century and the middle of the 20th century was analysed. It was reported, using FTIR spectrometry, that the crystallinity index increases with wood age. It is consistent with previous examinations in other papers and shows that the chosen method of crystallinity index analysis is correct.
PL
Wraz z upływem czasu stare drewniane okna, drzwi, podłogi podobnie jak i inne elementy stolarki budowlanej nabierają wartości muzealnej i dlatego, jako świadectwo kultury materialnej minionych stuleci powinno zostać zachowane dla przyszłych pokoleń. Za pozostawieniem tych elementów, poza argumentami dotyczącymi wartości zabytkowych i estetycznych, przemawiają właściwości samego drewna, które pomimo upływu czasu często nie ulegają istotnym zmianom, a materiał ten zachowuje pełne funkcje użytkowe. Wobec panujących obecnie niejednoznacznych poglądów na temat skutków długotrwałego starzenia się drewna, istnieje potrzeba podejmowania możliwie wielostronnych badań zmierzających do określenia właściwości zabytkowego drewna. Celem niniejszych badań było określenie indeksu krystaliczności celulozy w drewnie pochodzącym z zabytkowej warszawskiej stolarki budowlanej z połowy 18, przełomu 19 i 20 wieku, a także z połowy 20 wieku w porównaniu do drewna pozyskanego współcześnie. Analizę stopnia krystaliczności celulozy przeprowadzono metodą spektrometrii w podczerwieni FTIR przy użyciu modelu Nicolet 6700, Thermo Fisher Scientific Inc. Wyniki przeprowadzonych badań pozwalają stwierdzić, że w zabytkowym drewnie, w porównaniu do drewna pozyskanego współcześnie, następuje zmiana indeksu krystaliczności celulozy. Wielkość zmian uzależniona jest od wieku drewna. Największym indeksem krystaliczności celulozy charakteryzuje się drewno elementów stolarki budowlanej z 18 wieku, a najmniejszą różnicę wykazało drewno pochodzące z zabytkowych elementów z połowy 20 wieku. Obserwacje te potwierdzają z fachowej literatury, co świadczy także na korzyść wybranej metody określania indeksu krystaliczności.
7
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Przedstawiono wyniki badań charakterystyki odkształceniowo-naprężeniowej uzyskane w próbie cyklicznego rozciągania, przy założeniu stałego poziomu amplitudy naprężenia, wyprasek wtryskowych z PP, ABS oraz PA. Rejestrowano zależność pomiędzy naprężeniem rozciągającym i wydłużeniem próbki, uzyskując pętle histerezy. Wykazano zmiany właściwości mechanicznych badanych próbek spowodowane cyklicznym obciążeniem. W badaniach DSC zaobserwowano nieznaczne zmiany stopnia krystaliczności cyklicznie obciążanych próbek.
EN
The results of investigations of strain-stress characteristics obtained during the cyclic tensile test, constant level of stress amplitude were presented in this work. The injection molded parts form PP, ABS and PA were tested. The relationship between tensile stress and elongation of the sample was recorded. As a result hysteresis loops were obtained. The change in mechanical properties of test specimens caused by cyclic loading has been shown. In DSC studies small changes in polymer crystallinity degree during cyclic loading were observed.
8
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
It the paper, an analysis of strength characteristics of polyethylene products, obtained by different methods of processing was presented, to obtain definite input data for numerical analysis with the use of finite element method (FEM). The dependence of variations of stress and deformation values on the conditions of tests was analyzed using as examples the samples of high-density polyethylene obtained in the technological processes, subjected to the uniaxial tension at a testing machine. Crystallity degree was determined for the samples obtained from extruded or injected products. The changes of internal characteristics of the products were tested in chosen areas of testing samples under influence of external load increasing in time. The results of laboratory tests formed the basis for development of the characteristics of material and values of parameters for numerical models were determined, dependently on the method applied for polymer sample production. The numerical simulations were conducted in linear formulation, being the simplified analysis in the scope of Hooke's law being in force, and also in physically non-linear range, taking into account the real characteristics of plastic during the process of sample loading. The numerical investigations allowed to define the state of strain and stress in the whole sample analyzed dependently on the processing conditions.
PL
W artykule przedstawiono analizę cech wytrzymałościowych wytworów z polietylenu, otrzymanych różnymi metodami przetwórstwa, celem uzyskania określonych danych wejściowych do analizy numerycznej z wykorzystaniem metody elementów skończonych (MES, ang. finite element method). Próbki z polietylenu dużej gęstości poddano jednoosiowemu rozciąganiu z wykorzystaniem maszyny wytrzymałościowej i przeanalizowano zmiany wartości naprężenia oraz odkształcenia w zależności od warunków prowadzenia badań. Określono także stopień krystaliczności próbek otrzymanych z wytworu wytłaczanego i wtryskiwanego oraz badano zmiany, pod wpływem narastającego w czasie obciążenia zewnętrznego, cech wewnętrznych wytworu w wybranych obszarach próbek badanych. Na podstawie wyników badań laboratoryjnych opracowano charakterystyki materiałowe i określono wartości parametrów modeli numerycznych, w zależności od zastosowanej metody wytwarzania próbki. Symulacje numeryczne prowadzono w ujęciu liniowym, stanowiącym uproszczoną analizę w zakresie obowiązywania prawa Hooke'a, jak również w zakresie fizycznie nieliniowym, uwzględniającym rzeczywiste charakterystyki tworzywa w trakcie procesu obciążania próbki. Badania numeryczne pozwoliły na określenie stanu odkształcenia oraz naprężenia w całej próbce w zależności od warunków jej wytwarzania.
9
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Purpose: The intention of this research was to test, if injection moulded polyoxymethylene parts, manufactured in different cavities of the multicavity injection mould with geometrically balanced runners, differ in crystallinity degree. Design/methodology/approach: The values of crystallinity degree were calculated on the basis of DSC (Dynamic Scanning Calorimetry) testing method results (DSC curves). Findings: It was found that there are differences in crystallinity degree for parts from particular mould cavities. The reason of this is the difference in thermal conditions, specific for each cavity. Research limitations/implications: It is supposed that the parts from each multicavity injection mould would have differences in properties. However, it is always dependent on cavities and runners’ layout. Since in this research a particular injection mould was used, the conclusions can not be directly extrapolated to other moulds. Each case requires its own analysis. Higher crystallinity degree will occur in parts obtained from areas of higher mould temperature. Practical implications: The results of this investigation are important for mould designers, especially when moulds are used for precision injection moulding. It was proved here that differences in parts’ properties can occur for multicavity injection moulds. In order to avoid this it is required to minimize the temperature differences in the mould. Originality/value: Geometrically balanced runners in the mould were supposed to assure the equal filling of all cavities. The results obtained lately by other researchers have shown that this is not always true. That investigation was mostly focused on filling imbalance that leads for example to difference in weight of parts from different cavities. In this paper it was shown that not only weight of parts can differ but also other properties.
Purpose: Crystallinity degree of injection moulded parts made from polyoxymethylene was tested. The parts came from a mulitcavity injection mould with geometrically balanced runners. The purpose of research was to check if there are differences in crystallinity degree between parts from different cavities. Methodology DSC (Dynamic Scanning Calorimetry) tests were made and according to the obtained DSC curves crystallinity degree value was calculated for injection moulded parts. Findings: The results of research made show that the parts from particular mould cavities differ in crystallinity degree and the values are affected by thermal conditions which are different across the mould and, of course, for each cavity too. Research limitations: In this research only one multicavity injection mould was tested. It has a specific layout of runners and cavities and cooling channels that determine the polymer flow in the mould and other conditions like mould temperature distribution. It is usually supposed that the parts placed in areas of higher temperature in the mould will have higher crystallinity degree values. However, each mould requires separate analysis as it is built in another way and the extrapolation of the results of this research to other injection moulds can lead to errors. Practical implications: The results of this investigation can be useful for mould designers. The occurrence of different properties of parts from multicavity injection moulds is especially important in case of precision injection moulding, particularly for small parts. The way to minimize the problem with unequal part properties like crystallinity degree (which results in different mechanical properties) is minimizing the temperature differences in the mould. Originality The research made in last years by other scientists show that even when using geometrically balanced runners in the mould the problems with unequally filling cavities can occur, especially due to shearing phenomena in runners. This leads to differences in weight of parts. The work was mostly focused on the problems with filling imbalance and phenomena in runners or showing different weight of the parts. In this paper it was shown other important consequences of filling imbalance in the mould.
11
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Material for investigations was NiCrBSi powder for components' coatings which improve their corrosion resistance as well as resistance to friction wear and erosion. Plasma spraying method was used to produce a coating with thickness of 300 [mikro]m on low-alloy steel which was then remelted with the base material. Using X-ray quality analysis, phase composition was determined for: NiCrBSi powder, obtained coating and the alloyed surface layer. Crystallinity degree was also calculated for NiCrBSi layer sprayed on the base material.
12
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Commercial grade polyethylenes: high density (PE-HD) and ultra-high molecular weight one (PE-UHMW) were subjected to the surface modification by electron beam irradiation (0.6-1.5MeV/50-500kGy) and ion beam bombardment (He+ 160keV/2ź1013-5ź1016 ions/cm2; Ar+ 130keV/1ź1013-2ź1016 ions/cm2). Effects of modifications were studied by spherical nanoindentation and scratch hardness tests. Contrary to electron beam irradiation, the ion beam bombardment, especially of He+ ions, can significantly increase (up to 3 times) hardness of the surface layer of polyethylene in comparison to the bulk. According to Grazing Incidence X-ray Diffraction (GIXRD) it is associated with an increased degree of crystallinity due to the surface modification. Nuclear Reaction Analysis (NRA) reveals a hydrogen release due to ion bombardment which saturates at the CH atomic composition. It cannot however be associated with cross-polymerization or crosslinking of macromolecules because of some unsaturations being present and a graphite formation. Partially graphitized and/or better organized modified macromolecular chains "rooted" in the polymer substrate explain low friction and wear resistance of ion bombarded polyethylenes. Even high stress crackings are not able to proceed with further delamination of the modified surface layer. Treatment of the material with heavy Ar+ ions of energy 150-300keV was combined with an electrical doping by implantation of polyethylene with I+ ions of energy 150keV. Apart an increase in hardness, the modification results additionally in a significant reduction of the surface resistivity (more than 20 times), facilitating a removal of static charge.
PL
Próbki handlowych polietylenów: o dużej gęstości (PE-HD) oraz o bardzo wysokim ciężarze cząsteczkowym (PE-UHMW) poddano modyfikacji powierzchniowej metodą naświetlania wiązką elektronów lub bombardowania wiązką jonów (He+ lub Ar+). Efekt modyfikacji materiału uzyskany za pomocą nanoindentacji kulistej oceniano na podstawie odporności powierzchni na zarysowanie. W odróżnieniu od efektów naświetlania wiązką elektronów, bombardowanie jonowe, zwłaszcza jonami He+, może znacznie zwiększyć twardość (nawet do 3 razy) warstwy wierzchniej polietylenu w porównaniu z wnętrzem materiału. Wyniki uzyskane metodą rozpraszania promieniowania rentgenowskiego padającego pod małymi kątami (GIXRD) sugerują, że jest to konsekwencją wzrostu stopnia krystaliczności warstwy wierzchniej polimeru w wyniku modyfikacji. Analiza warstwy wierzchniej metodą reakcji jądrowej (NRA) ujawnia uwalnianie wodoru wywołane bombardowaniem jonowym, które zatrzymuje się na poziomie składu atomowego CH (rys. 4 i 5). Jednakże tego wyniku nie należy traktować jako potwierdzenia polimeryzacji krzyżowej (cross-polymerization) lub sieciowania makrocząsteczek polimeru, ponieważ w jego warstwie wierzchniej stwierdzono obecność zarówno wiązań podwójnych jak i grafitu. Obecność częściowo zgrafityzowanych i/lub lepiej zorganizowanych zmodyfikowanych łańcuchów makrocząsteczek, „zakorzenionych” w podłożu polimerowym, wyjaśnia niski współczynnik tarcia i znakomitą odporność na ścieranie bombardowanych jonami polietylenów. Nawet duże obciążenia, powodujące pękanie twardej warstwy wierzchniej, nie są w stanie doprowadzić do jej delaminacji. Modyfikowanie materiału za pomocą ciężkich jonów Ar+ o energii 150-300keV połączono z elektrycznym domieszkowaniem polietylenu dokonując implantacji warstwy wierzchniej polimeru jonami I+ o energii 150keV. W wyniku modyfikacji oprócz wzrostu twardości, uzyskano dodatkowo znaczne obniżenie oporności powierzchniowej (nawet 20-krotne), zapobiegające gromadzeniu się ładunku elektrostatycznego.
W celu wykazania wpływu warunków uplastyczniania polietylenu PE-LD w układzie ślima-kowo-tarczowym wytłaczarki ślimakowo-tarczowej na porządkowanie łańcuchów polimerowych przeprowadzono analizę obliczeniowo-symulacyjną, wytłaczanie tworzywa i pomiar właściwości mechanicznych oraz budowy strukturalnej. Wpływ strefy tarczowej na porządkowanie łańcuchów polimerowych określono przy następujących czynnikach zmiennych: szczelinie, wydajności, początkowym położeniu w szczelinie i średnicy tarczy. Na podstawie uzyskanych wyników stwierdzono, że tarczowy mechanizm wytłaczarki ślimakowo-tarczowej wpływa na właściwości mechaniczne przetwarzanego tworzywa polimerowego.
EN
In an aim of prove that conditions of plasticization in the system screw-disc of the screw-disc extruder polyethylene LDPE influence on the ordering of polymer chains, realized: the analytical-simulating, polymer material extrusion moulding and measurement mechanical properties and structure. The influence of disc zone on arrangement the polymer chains was qualified by factors of variables: the chink dimension, efficiency, place of location in disc crevice, the diameter of the shield. On the ground results research is ascertained that processing properties of the disc mechanism of the screw-disc extruder influence on mechanical properties of processed polymer material.
14
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
The compatibilizing effect of functionalized low density polyethylene (PE-LD) on PE-LD/polyamide 6 (PA6)/ethylene-propylene-diene terpolimer (EPDM) ternary blends has been studied. Compatibility was evaluated by means of differential scanning calorimetry, which was used also for studying the melting and crystallization phenomena. Torque-time measurements were performed in order to determine the processing behavior. The functionalized PE-LD modify the processing behavior, the crystallinity degree of PE-LD and PA6 and impact properties of the studied blends. These effects result from chemical reactions between functional groups of compatibilizing agents and the end groups of polyamide.
PL
Zbadano kompatybilizujący wpływ polietylenu małej gęstości funkcjonalizowanego kwasem akrylowym (PE-LD/AA), bezwodnikiem maleinowym (PE-LD/MA) bądź bismaleinoimidem (PE-LD/BMI) na różniące się składem trójskładnikowe mieszaniny PE-LD/poliamid 6 (PA6)/terpolimer etylen-propylen-dien (EPDM) (tabela 1). Mieszalność oceniano za pomocą skaningowej kalorymetrii różnicowej, którą stosowano też do badania zjawisk topnienia i krystalizacji (rys. 1 i 2). W celu scharakteryzowania właściwości przetwórczych mierzono momenty obrotowe badanych układów w funkcji czasu oraz wartości jednostkowej energii mieszania po 1 minucie (tabela 1). Funkcjonalizowany PE-LD modyfikuje właściwości przetwórcze, stopień krystaliczności PE-LD i PA6 (rys. 3) oraz udarność mieszanin (rys. 4). Wpływ ten przypisano reakcjom chemicznym między grupami funkcyjnymi kompatybilizatorów oraz grupami końcowymi PA6. Określono wpływ składu na zbadane właściwości mieszanin.
15
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Zbadano wpływ amorficznej krzemionki na formowanie struktur krystalicznych polietylenu dużej gęstości i polipropylenu. Otrzymane wyniki metodami DSC i WAXS jednoznacznie wykazały, że krzemionka inhibituje procesy krystalizacji i silnie redukuje stopień krystaliczności badanych polimerów. Relacja powyższa jest szczególnie charakterystyczna dla kompozytów HDPE/Sio[2].
EN
The influence of amorphous silica content on the crystallization and crystallinity degree of linear thermoplastics have been studied. Obtained results has clearly proved that the addition of small amount of amorphous silica into the high density polyethylene and isotatctic polypropylene sharply decreases the crystallinity degree. It suggests, that SiO[2] act as nonactive filler into polyolefin resins.
16
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Dokonano przeglądu (38 poz. lit.) wyników badań procesu degradacji poliolefin ze szczególnym uwzględnieniem polietylenu i polipropylenu. Na tej podstawie omówiono wpływ budowy chemicznej polimeru, jego stopnia krystaliczności, Grubości próbki oraz warunków zewnętrznych (długość fali i (stężenie promieniowania, temperatura, ciśnienie tlenu) na przebieg procesu starzenia świetlnego. Podkreślono fakt, że niewidłowa analiza przebiegu procesu fotodegradacji wymaga pomiaru zmian kilku cech starzonej próbki. Ocena dokonali wyłącznie na podstawie zmian właściwości mechaniczni bądź tylko przyrostu ilości produktów fotooksydacji jest niepełna.
EN
Literature review (38 references) on investigations of photodegradation of polyolefines, especially polyethylene and polypropylene, has been done. The influences of chemical structure of the polymer, its crystallinity degree, sample thickness and outdoor factors (wavelength and radiation intensity, temperaturę, oxygen pressure) on the course of light ageing have been discussed. It has been stressed that proper analysis of the course of photodegradation requires measurements of changes of couple of characteristics of ageing sample. Analyses done on the basis either only mechanical properties' changes or just increasing of photooxidation products amount are not sufficient.