1
Content available remote The influence of antimony, lead and sulphur on the surface tension of liquid copper
Siwiec G., Botor J.
Archives of Metallurgy and Materials
|
2004
|
Vol. 49, iss. 3
611-621
EN
In the present paper, the results of the study on the influence of antimony, lead and sulphur on the surface tension of liquid copper are presented. The measurements of the surface tension of liquid Cu-Sb alloys containing maximum 5.12 ź 10-2 mole fraction of Sb, liquid Cu-Pb alloys containing maximum 3.47 ź 10-2 mole fraction of Pb and liquid Cu-S alloys containing maximum 1.59 10-2 mole fraction of S were made. The measurements were carried out by means of the sessile drop method, in the temperature range 1393-1553 K. The results of the experiment show that sulphur has the strongest influence on the decrease in the surface tension of copper. Weaker influence is shown by lead and antimony, consecutively.
PL
W pracy przedstawiono wyniki badań nad wpływem antymonu, olowiu i siarki na napięcie powierzchniowe ciekłej miedzi. Przeprowadzone badania obejmowały pomiary napięcia powierzchniowego ciekłych stopów miedzi z antymonem o maksymalnej zawartości 5.12 x 10(-2) ułamka molowego Sb, stopów miedzi z ołowiem o maksymalnej zawartości 3.47x10(-2) ułamka molowego Pb oraz stopów miedzi z siarką o maksymalnej zawartości 1.59x10(-2) ułamka molowego S. Badania prowadzono w zakresie temperatur 1393-1553K. Wykorzystano metodę kropli leżącej. Stwierdzono, ze Sb, Pb i S obniżają napięcie powierzchniowe ciekłej miedzi, przy czym największą aktywność powierzchniową wykazuje siarka, w dalszej kolejności ołów i antymon.
2
Napięcie powierzchniowe i jego związek z wybranymi parametrami charakteryzującymi fazę ciekłą.
Siwiec G., Botor J.
Rudy i Metale Nieżelazne
|
2002
|
R. 47, nr 12
601-607
PL
Przedstawiono podstawowe informacje dotyczące napięcia powierzchniowego, skutki jego występowania oraz związek z wybranymi parametrami charakteryzującymi fazę ciekłą. Na podstawie wyników badań napięcia powierzchniowego ciekłej miedzi przeanalizowano wpływ trudności eksperymentalnych w wysokich temperaturach na uzyskiwane wyniki pomiarowe.
EN
The basic knowledge regarding surface tension and the consequences of its presence as well as its relation with certain parameters characterizing the liquid phase have been presented. Basing on the results of the research on surface tension in liquid copper, the influence of difficulties encountered during experiments performed at high temperatures on the obtained measurement results have been analyzed.
3
Content available remote Cracking of metals in the presence of liquid copper
Tasak E., Kąc S., Ziewiec A.
Metallurgy and Foundry Engineering
|
1999
|
T. 25, no. 2
127--137
EN
Liquid metals, among others copper, in contact with steel can result in its catastrophical cracking. Such an influence of copper or other liquid metals is particularly dangerous when any structure is subjected to performance of heavy loading. The aim of this work was to investigate thc phenomena across the border copper-steel, and to estimatc the influence of stresses on steel cracking. Thc expcriments were carried out at different temperatures on the specimens under extcrnal stresses, and specimens under no stresses. The mechanism explaining embrittlement of copper in the presence of liquid metals was described, and the critical stress level causing the embrittlement was estimated. Under no stresses in stcee, no cracking was obscrved.
PL
Ciekłe metale, m.in. miedź, w kontakcie ze stalą mogą powodować jej katastroficzne pękanie. Taki wpływ miedzi czy innych ciekłych metali jest szczególnie niebezpieczny kiedy konstrukcja poddana jest działaniu wysokich obciążeń. Celem pracy było zbadanie zjawisk zachodzących na granicy miedź - stal oraz określenie wpływu naprężeń na pękanie stali. Badania przeprowadzono - przy różnych temperaturach - na próbkach, poddanych działaniu naprężeń zewnętrznych oraz bez oddziaływania naprężeń. Ustalono mechanizm wyjaśniający kruchość cickłomctaliczną stali w obecności ciekłych metali oraz wyznaczono krytyczny poziom naprężeń, wywołujący tę kruchość. Bez obecności naprężeń w stali nic występują pęknięcia. 73