Wyniki wyszukiwania - BazTech

1

Adhesion between orthodontic bracket and dental ceramics

Malkiewicz Konrad, Krasowski Michał, Bartczak Jakub, Radziejewska Marta, Janas-Naze Anna, Horodyska Estera

Polimery

|

2023

|

Vol. 68, nr 7-8

371--377

EN

The strength of the connection between orthodontic brackets and sandblasted dental ceramics was evaluated. The strength of the bracket-ceramics connection was determined in four time intervals. Based on the obtained results, basic statistics were calculated. For the comparative analysis of average values, the following were used: ANOVA analysis of variance and Tukey’s HSD post-hoc test at the significance level of α = 0.05. The statistical analysis performed did not show any influence of the method of surface treatment (with sanding, without sanding) between orthodontic brackets and ceramics. At the same time, it has been shown that with samples storing time in aqueous environment, the quality of the connection decreases significantly, regardless of the surface treatment method used.

PL

Zbadano wytrzymałość połączenia zamków ortodontycznych z ceramiką dentystyczną poddaną piaskowaniu. Wytrzymałość połączenia zamek-ceramika wyznaczono w czterech przedziałach czasowych. Do analizy porównawczej wartości średnich zastosowano m.in. analizę wariancji ANOVA oraz test post - hoc Tukeya HSD na poziomie istotności α = 0,05. Przeprowadzona analiza statystyczna nie wykazała wpływu metody obróbki powierzchni porcelany dentystycznej (z piaskowaniem, bez piaskowania) na jakość połączenia zamków ortodontycznych z ceramiką. Jednocześnie wykazano, że wraz z upływem czasu przechowywania próbek w środowisku wodnym, istotnie zmniejsza się jakość połączenia, niezależnie od stosowanej metody obróbki powierzchni.

2

Materiały ceramiczne w stomatologii

Wydra M., Grelowska I.

Szkło i Ceramika

|

2017

|

R. 68, nr 6

11--15

PL

Na przestrzeni ostatnich 20 lat nastąpił gwałtowny postęp w dziedzinie protetyki stomatologicznej. Rozwój ten widoczny jest zarówno w aspekcie poprawy właściwości mechanicznych i estetycznych wprowadzanych materiałów, jak i technologii ich obróbki. Ma to związek z dążeniem do stworzenia uzupełnień protetycznych spełniających rosnące wymagania estetyczne pacjentów. Dotychczas stosowane materiały i metody, choć sprawdzone i bardzo skuteczne, coraz częściej są zastępowane przez nowe technologie. W artykule przedstawiono klasyfikację materiałów ceramicznych stosowanych w stomatologii odtwórczej z uwzględnieniem wybranych aspektów. Wskazano różnice pomiędzy powszechnie stosowanymi uzupełnieniami metalowo-ceramicznymi a stosunkowo nowymi pełnoceramicznymi. Szczególną uwagę poświęcono materiałom na bazie dwutlenku cyrkonu, które ze względu na wyjątkowe właściwości estetyczne i mechaniczne, w ostatnich latach cieszą się rosnącą popularnością i zaczynają wypierać z użycia ceramikę krzemianową. Omówiono również schematy postępowania w systemach CAD/CAM, które stanowią alternatywę dla czaso- i pracochłonnych uzupełnień wykonywanych tradycyjnymi metodami. Wskazano również obszary, w których systemy te wymagają jeszcze dopracowania.

EN

Over the last 20 years there has been a rapid development in dental prosthetics, which can be observed in the improvements in the mechanical and aesthetic properties of the materials introduced, as well as in their processing technology. This improvement can be linked with a desire to create prosthetic restorations meeting the ever-increasing aesthetic requirements of patients; and as a consequence, materials and methods used, although proven and very effective, are increasingly being replaced by new technologies. The article presents the classification of ceramic materials used in restorative dentistry, taking into account selected aspects. Differences between commonly used metal-ceramic restorations and relatively new all-ceramic ones were noted. Much attention was paid to materials based on zirconium dioxide, which due to their unique aesthetic and mechanical properties have become increasingly popular in recent years and have begun to replace silicate ceramics. Use of CAD/CAM systems as an alternative to time-consuming and labor-intensive traditional restoratives, was also discussed. Weaknesses of these systems, which still need to be improved, were also indicated.

3

Zmiany struktury powierzchni ceramik dentystycznych oraz ich wpływ na wytrzymałość połączenia z materiałem kompozytowym

Łapińska B., Szynkowska M. I., Rogowski J., Nowak J., Sokołowski G., Sokołowski J., Łukomska-Szymańska M.

Przemysł Chemiczny

|

2017

|

T. 96, nr 2

370--374

PL

Przedstawiono wyniki badania zmian składu chemicznego oraz morfologii powierzchni ceramik dentystycznych po zastosowaniu różnych metod jej obróbki. W celu modyfikacji powierzchni ceramiki zastosowano obróbkę strumieniowo- ścierną z użyciem korundu szlachetnego o wielkości ziaren 50 μm, trawienie kwasem fluorowodorowym (HF) oraz kombinację tych metod lub obróbkę tribochemiczną systemem Rocatec®. Zarówno trawienie HF, jak i obróbka tribochemiczna umożliwiły uzyskanie znaczących zmian w morfologii powierzchni badanych ceramik oraz najwyższej wytrzymałości połączenia z materiałem kompozytowym. Największy spadek wytrzymałości połączenia ceramika-kompozyt w czasie zaobserwowano w przypadku stosowania obróbki tribochemicznej.

EN

Microcryst. aluminosilicate and Li disilicate ceramic cylinders (diam. 5 mm) were surface-treated by sandblasting with air-borne Al2O3 (diam. 50 μm or 110 μm), etching with HF (9%) or by combination of both methods, and then studied for chem. compn. of the surface and then for bond strength to a dental composite. Both, HF etching and tribochem. surface treatment resulted in an increase in the bonding strength.

4

Właściwości ceramiki litowo-silikatowej po obróbce jej powierzchni

Łapińska B., Szynkowska M. I., Szczesio A., Domarecka M., Sokołowski J., Łukomska-Szymańska M.

Przemysł Chemiczny

|

2017

|

T. 96, nr 2

391--395

PL

Przedstawiono wyniki badania struktury powierzchni ceramiki krzemianu litu wzmocnionej tlenkiem cyrkonu oraz zmian składu chemicznego jej powierzchni po zastosowaniu obróbki strumieniowo-ściernej korundem szlachetnym o wielkości ziaren 50 μm, trawienia kwasem fluorowodorowym oraz kombinacji tych metod. Zastosowane metody znacząco wpłynęły na strukturę powierzchni ceramiki oraz wytrzymałość jej połączenia z materiałem kompozytowym. Wydłużenie czasu trawienia nie wpłynęło znacząco na rozwinięcie badanej powierzchni. Największą wytrzymałość połączenia ceramika-kompozyt uzyskano po piaskowaniu i trawieniu jej powierzchni 9-proc. kwasem fluorowodorowym przez 60 s.

EN

ZrO₂-reinforced Li silicate ceramic surface was treated by sandblasting with air-borne 50 μm Al₂O₃ particles, etching with 9% HF, and by combination of both methods. All treatments resulted in increasing bond strength to composite material. Prolonged HF etching did not change significantly surface morphol. The highest bond strength was achieved after sandblasting with Al₂O₃ and 60 s long HF etching of ceramic surface.

5

Zastosowanie technologii CAD/CAM w stomatologii odtwórczej : przegląd piśmiennictwa

Bębenek K., Błaszczyk A., Kiryk J., Kotowski D., Kowalska K., Szczygielski T., Mazgajczyk E., Szymczyk P., Badora G., Bryła E., Dobrzyński M., Rybak Z.

Inżynier i Fizyk Medyczny

|

2016

|

Vol. 5, nr 2

99--104

PL

Technologia CAD/CAM, obejmująca komputerowe wspomaganie projektowania CAD (Computer-Aided Design) oraz komputerowe wspomaganie wytwarzania CAM (Computer-Aided Manufacturing), już przeszło dwie dekady jest stosowana w stomatologii odtwórczej. W tym okresie nastąpił znaczny rozwój systemów wspomagających kliniczną pracę lekarza dentysty, co wynika przede wszystkim z rosnącego zapotrzebowania na coraz bardziej precyzyjne i wysoce estetyczne prace protetyczne, możliwe do wykonywania w jak najkrótszym czasie. Systemy wykorzystujące technologię CAD/CAM stanowią alternatywę dla tradycyjnych i czasochłonnych metod laboratoryjnych, tj. techniki traconego wosku, odlewnictwa z użyciem metalicznych stopów czy pokrywania ceramiką dentystyczną. Zaspokojenie wysokich wymagań pacjentów związanych z estetyką uzupełnień protetycznych uwarunkowane jest dostępnościąmateriałów niezbędnych do ich wykonania. Dlatego wciąż poszukuje się materiałów o jak najkorzystniejszych właściwościach fizykochemicznych oraz doskonałej estetyce przy jednoczesnym zachowaniu biokompatybilności. Pierwsze uzupełnienie protetyczne z użyciem systemu CAD/CAM zostało wykonane na początku lat osiemdziesiątych ubiegłego stulecia. Początkowo system ten wykorzystywano w wytwarzaniu m.in. koron, licówek, nakładów czy wkładów. Dynamiczny rozwój materiałoznawstwa, jak i samej technologii CAD/CAM umożliwił wykonywanie wielopunktowych mostów protetycznych oraz łączników bądź diagnostycznych szablonów implantologicznych.

EN

CAD/CAM technology, including computer aided design (CAD) and computer-aided manufacturing (CAM) more than two decades in restorative dentistry is used. Within this period, a significant development of systems has been observed to support the clinical work of a dentist. It is primarily due to the growing demand for increasingly precise and highly aesthetic prosthetic restorations as well as their quick performance. Systems using CAD/CAM technology constitute an alternative to traditional and time-consuming laboratory methods, ie. techniques of lost wax, molding using metallic alloys or dental ceramics coverage. Satisfying the high requirements of patients associated with aesthetic restorations results from the availability of materials necessary for their performance. Therefore, we continue to look for the materials with good physical and chemical properties as well as excellent aesthetics while maintaining biocompatibility. The first restoration using CAD/CAM system was made in the early eighties of the previous century. At the beginning, the system was used in the preparation i.e. crowns, veneers, onlays or cartridges. The dynamic development of dental materials and the CAD/CAM technology, allowed to perform multipoint bridges and prosthetic fittings or implant diagnostic templates.

6

Defekty powstające w strukturze połączenia uzupełnień protetycznych spieków z porcelaną licowaną

Czakon K., Wita K., Sobel A., Hajduga M.

Aktualne Problemy Biomechaniki

|

2016

|

z. 11

21--26

PL

Połączenie podbudowy protetycznej z warstwą porcelany ma znaczący wpływ na jakość uzupełnienia dentystycznego. Rozwój selektywnej laserowej mikro metalurgii proszków, przyczynił się do rozpoczęcia badań tej technologii w dziedzinie techniki dentystycznej. W artykule przedstawiono ocenę wpływu kondycjonowania piaskiem Al2O3 o gradacji: 50μm, 110μm, 250μm, powierzchni spieków przygotowanych laserowo, na klasę połączenia z fazą licującą. Wnioski zostały formułowane na podstawie wyników z przeprowadzonych pomiarów chropowatości i falistości powierzchni spieków laserowych.

EN

The foundation prosthetic connection with a layer of porcelain has a significant impact on the quality of the dental supplement. The development of selective laser micro powders metalurgy, has contributed to the start of the examination of this technology in the field of dental technology. The article presents an impact assessment conditioning sand Al2O3 grit : 50μm, 110 μm, 250 μm, laser- sintered surface prepared, class connection with the phase of the veneering. Proposals were formulated based on the results of the measurements of roughness and waviness floor space laser sintered.

7

Trzypunktowe zginanie próbki z dwutlenku cyrkonu

Wirwicki M., Topoliński T.

Inżynieria i Aparatura Chemiczna

|

2013

|

Nr 2

125-126

PL

Celem badania była analiza właściwości mechanicznych materiału Cyrkon Lava, który jest stosowany do wytworzenia koron dentystycznych oraz mostów poprzez proces frezowania. Badania dotyczyły procesu trzypunktowego zginania na maszynie wytrzymałościowej Instron 8874 według normy PN-EN 843-1. Przeprowadzone badania pozwalają wnioskować o wysokiej wytrzymałości na zginanie oraz wpływie obrobionej powierzchni próbki na właściwości mechaniczne.

EN

Aim of this study was to evaluate mechanical properties of Cyrkon Lava material, used in production of dental crowns and bridges in the milling process. Research dealt with the three-point bending in the Instron 8874 testing machine in accordance with the PN-EN 843-1 standard. The research results confirm high flexural strength and the impact of sample surface on mechanical properties.

8

Wpływ sposobu przygotowania powierzchni ceramik krzemionkowych na wytrzymałość połączenia z materiałem kompozytowym

Łapińska B., Szynkowska M. I., Sokołowski K., Rylska D., Sokołowski J.

Inżynieria Materiałowa

|

2010

|

Vol. 31, nr 4

1074-1076

PL

Warunkiem połączenia pełnoceramicznych uzupełnień protetycznych, wykonanych z ceramiki krzemionkowej, z materiałem kompozytowym jest rozwinięcie powierzchni ceramiki i jej silanizacja. Metodami standardowo polecanymi do rozwinięcia powierzchni ceramiki są: piaskowanie korundem, trawienie 9,5% kwasem fluorowodorowym (HF) lub połączenie tych metod. Brak jest jednak zgodności, co do oceny skuteczności tych metod przygotowania powierzchni ceramiki do jej połączenia z kompozytem. Celem pracy była ocena wytrzymałości połączenia ceramiki krzemionkowej z materiałem kompozytowym w zależności od sposobu przygotowania jej powierzchni. Badaniu poddano próbki ceramik krzemionkowych wykonanych metodą napalania, które szlifowano na mokro papierami ściernymi o gradacji 600C, piaskowano korundem szlachetnym 50 um i trawiono 9,5% kwasem HF. Po silanizacji powierzchni ceramiki próbki łączono z materiałem kompozytowym za pomocą systemu wiążącego. Wytrzymałość połączenia oceniano w teście ścinania w urządzeniu do badań wytrzymałościowych Zwick-Roell Z005 przy prędkości przesuwu belki poprzecznej 2 mm/min. Stwierdzono istotne różnice w wytrzymałości połączenia materiału kompozytowego z poszczególnymi ceramikami. Powierzchnia próbek ceramiki była również oceniana w mikroskopie elektronowym skaningowym. Uzyskano większe zróżnicowanie powierzchni próbek ceramiki po ich trawieniu kwasem HF w porównaniu z piaskowaniem.

EN

Increasing the ceramic surface area and its silanisation is critical for achieving successful bonding between all-ceramic restorations and composite resin. Standard procedures include sandblasting, etching with 9.5% hydrofluoric acid (HF) or combination of these methods. However, there is an ongoing debate on the best methods of ceramic surface treatment to achieve optimal ceramic-composite bonding. Aim of this study was to evaluate shear bond strength between feldspathic ceramic and resin composite due to different ceramic surface conditioning methods. Specimens of feldspathic build up ceramic, polished, were treated with airborne particle abrasion with 50 ?m aluminum oxide and etched with 9.5% hydrofluoric acid. After silanisation of ceramic surface, specimens were bonded with resin composite by means of bonding system. Shear bond strength was tested in universal testing machine Zwick-Roell Z005 at a crosshead speed 2.0 mm/min. Comparing ceramics significant differences in shear bond strength were observed. SEM analysis of ceramic surfaces was performed. In comparison to airborne particle abrasion, HF etching resulted in greater diversity of morphological surface of ceramics.

9

„Metaloceramika - ukryte wady” czyli problemy protetyki stomatologicznej

Rogalińska A, Hajduga M.

Aktualne Problemy Biomechaniki

|

2010

|

z. 4

157--162

PL

Uzupełnienia protetyczne na podbudowie metalicznej z licowaną ceramiką w obecnej protetyce stomatologicznej są najpopularniejszą i najchętniej wykorzystywaną kombinacją materiałów. Połączenie metal- ceramika zyskało ogromną popularność przy wykonywaniu koron, mostów ze względu nie tylko na walory estetyczne, poprzez ceramikę, ale przede wszystkim dzięki uzyskaniu własności wytrzymałościowych przez wykonanie metalowej podbudowy, osadzonej bezpośrednio na oszlifowane kikuty zębów czy implanty. Połączenie obu materiałów nie zawsze jest idealne. Uzupełnienie często nie wykazują żadnych nieprawidłowości w przypadku obserwacji zewnętrznej. Nie oznacza to, iż w obszarze chemicznego połączenia tych materiałów nie ma swoistych, mikroskopijnych wad. Praca przedstawia typy wad w obszarze styku dwóch różnych faz materiałów protetycznych oraz określa co mogą spowodować.

EN

Metallic porcelain veneered dental restorations are currently the most commonly chosen type of restoration in the dental profession. The use of ceramics fused to metal has gained wide popularity when choosing a material suitable for making dental crowns and bridges not only for aesthetic reasons, but more importantly due to the strength properties of the metallic substructure when placed on the previously grinded dental stump. The process of fusing dental ceramic to the metallic substructure does not always prove to be a success. Metal-ceramic dental restorations do not always exhibit flaws visible to the eye on the outer surface; often the metal-ceramic fusing process creates microscopic flaws. This thesis presents the different kinds of flaws which can occur when bonding two different kinds of prosthetic materials together and the outcome we can expect as a result.

10

Charakter struktury połączenia porcelany na podbudowie cyrkonowej w zależności od gatunku materiału licującego

Legutko A., Hajduga M.

Aktualne Problemy Biomechaniki

|

2009

|

z. 3

121--126

PL

W branży techniki dentystycznej pojawiła się nowa technologia CAD/CAM wykonawstwa pełnoceramicznych koron i mostów. Na rynku materiałów dla techniki dentystycznej dostępnych jest kilkanaście systemów pełnoceramicznych oferujących materiały do wykonania ceramicznej podbudowy i licowania. System Cercon Smart Ceramics firmy DeguDent składa się z ceramiki cyrkonowej przeznaczonej na podbudowy i porcelany skaleniowej stosowanej do licowania tych podbudów. W pracy przedstawiono charakter struktury połączenia tych materiałów, a także sprawdzono czy porcelana innego producenta może być stosowana zamiennie z porcelaną zalecaną w systemie Cercon.

EN

The purpose of thesis is characterizing connection between cercon base materials and covering porcelain and checking which forces (mechanical or chemical) are responsible too linkage materials. At the second part of thesis is described preparation samples of materials to research. Executed observations on optical microscope Zeiss M1m Imager and scanning electron microscope FEI E-SEM XL30 with X EDAX GEMINI 4000. Got results of qualitative and quantitative analyses which have showed character of materials connection. Researched materials Cercon Base, Cercon Ceram Kiss and Lava Ceram are compatible for each other.