The effects of artificial-aging temperature on tensile strength, hardness, microstructure, and fault morphology in AlSiMg

Andoko, Yanuar, Puspitasari P., Ariestoni T. B.

Journal of Achievements in Materials and Manufacturing Engineering

|

2020

|

Vol. 98, nr 2

49--55

EN

Purpose: This research examined the effects of artificial-aging temperature and time on tensile strength, hardness, microstructure, and fault morphology in AlSiMg. Design/methodology/approach: This research was conducted using aluminium alloy at 120°C, 150°C, and 180°C artificial-aging temperature and 6 hours holding time. The tensile test used ASTM B211-03 standard and hardness test adapted to ALCOA 6061 standard. Findings: Tensile test results indicated the highest tenacity on aluminium alloy at a 150ºC temperature that was 47.263% strain level. In addition to the strain level, this research also obtained the highest tensile strength level at 180ºC that was 62.267 kgf/mm2 and the highest hardness value that was 110 HV. The increase in tensile strength and hardness at 180°C was caused by the increase in Mg, Si, and Al. Based on the microstructure test, the highest tenacity was obtained at 150°C temperature as the result of closed and gathered Mg2Si precipitates; while at 180°C temperature, the precipitates appeared to be more distributed, causing a rise in hardness value and tensile strength. AlSiMg tenacity also exhibited from the number of dimples compared to cleavages at 150°C temperature. Research limitations/implications: The limitation that found in this research was conducted using AlSiMg aluminium Al6061 specimen with an artificial-aging treatment at 120ºC, 150°C, and 180°C temperature for 6 hours and then compared to the raw material. AlSiMg tensile specimen was made according to ASTM E8-E8M standard. Practical implications: This research can be applied in industrial manufacture process to find tensile strength, hardness, microstructure, and fault morphology of Al6061 alloy. Originality/value: According to research result, can be understood that by conducting these experiments, Artificial-aging treatment temperature variations in AlSiMg aluminium alloy could increase hardness.

2

The study of colour changes under artificial weathering of light red meranti and yellow balau wood from Shorea genus

Jankowska Agnieszka

Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology

|

2020

|

No. 111

37--42

EN

The study of colour changes under artificial weathering of light red meranti and yellow balau wood from Shorea genus. This paper deals with the change in colour of selected tropical wood species from Shorea genus such as light red meranti and yellow balau. The artificial weathering method was used to determine the colour stability of wood surface. The used ageing method consisted of alternating soaking wood in water, drying at a temperature of 70°C and UV irradiation exposure. The colour changes were evaluated using CIE L*C*h system. Changes of particular colour parameters (lightness L*, chroma C*, hue h) were determine as well as the total colour change ΔE*. The results showed that tested species of wood change their colour similarly under the influence of the artificial weathering (the changes in the tested wood appearance occurred in similar scope). Surfaces of tested wood species initially became darker and then lighter. The largest changes in intensity of the colour of wood took place at the beginning of artificial weathering process. The intensity of changes decreased with the progress of aging process.

PL

Badanie zmian barwy drewna meranti różowego i balau jasnego z rodzaju Shorea. Niniejszy artykuł dotyczy zmiany barwy dwóch gatunków drewna tropikalnego z rodzaju Shorea, takich jak meranti różowego i balau jasnego. Do określenia stabilności barwy powierzchni drewna zastosowano metodę sztucznego starzenia, która polegała na naprzemiennym moczeniu drewna w wodzie, suszeniu w temperaturze 70°C i ekspozycji na promieniowanie UV. Przeprowadzono 60 cykli sztucznego starzenia. Zmiany barwy oceniono za pomocą systemu CIE L*C*h. Określono zmiany poszczególnych parametrów barwy (jasność L*, barwa C*, odcień h), a także całkowitą zmianę barwy ΔE*. Wyniki przeprowadzonych badań pozwalają na stwierdzenie, że barwa badanego drewna zmienia się podobnie (zmiany występowały w podobnym zakresie). Powierzchnie badanych gatunków drewna początkowo stały się ciemniejsze, a następnie jaśniejsze. Największe zmiany w intensywności barwy drewna miały miejsce na początku procesu sztucznego starzenia. W trakcie jego trwania intensywność zmian malała.

3

Impact of the type of quench aging after hyperquenching on the mechanical strength properties of AW-7020 alloy

Hajdukiewicz G.

Journal of KONES

|

2018

|

Vol. 25, No. 2

141--148

EN

The article attempts to determine the influence of selected types of the heat treatment on the strength properties of the AW-7020 alloy used in the shipbuilding industry. The text presents information on the applied types of heat treatment. There are presented the results of the static tensile test of the material after its earlier hyperquenching and aging (natural and artificial) as well as comparison to the test results of the alloy without heat treatment. To illustrate the nature of the supersaturation and aging process, a test was carried out for a series of samples in a transitional state. During the tests for all the samples were determined: elongation at rupture and reduction of area at fracture, strength limit Rm and proof stress Re0.2. The results of the tests showed that the choice of the type of aging after saturation has significant importance for the strength properties of the AW-7020 alloy. It has been shown that it is possible to significantly accelerate the achievement of higher strength properties of the tested alloy, replacing the natural aging of the material with artificial aging.

4

Effect of the type of aging after supersaturating on hardness and AW-7020 stop structure

Abramczyk N., Żuk D.

Journal of KONES

|

2018

|

Vol. 25, No. 3

9--16

EN

Effect of the type of aging after supersaturating on hardness and AW-7020 stop structure

5

Comparison of impact of immersed and micro-jet cooling during quenching on microstructure and mechanical properties of hypoeutectic silumin AlSi7Mg0.3

Czekaj E., Kwak Z., Garbacz-Klempka A.

Metallurgy and Foundry Engineering

|

2017

|

Vol. 43, no. 3

153--168

EN

This article presents research the results of the mechanical properties at the ambient temperature of hypoeutectic cast silumin EN AC-AlSi7Mg0.3 (according to EN 1706:2011; analogic to alloy A356 according to AA – the Aluminum Association). As related to the commonly known and used process of immersion during quenching, the research also used a micro-jet system of cooling. After quenching, the experimental samples were also submitted to artificial aging in three different variations. The achieved results were compared with the mechanical properties of the alloy in the as-cast state. Samples from the experimental alloy were subjected to micro-jet cooling during quenching; in principle, they had a similar level of properties as related to the samples that were cooled by immersion; only in some cases did the micro-jet cooling give better results. Further works in the field should be aimed at constructing machines for micro-jet cooling with water pressure levels significantly higher than the typical pressure of community waterworks.

PL

W artykule zostały zaprezentowane wyniki badań podstawowych właściwości mechanicznych (UTS, YS, E, N, HB) w temperaturze pokojowej podeutektycznego siluminu odlewniczego EN AC-42100 (EN AC-AlSi7Mg0.3) (zgodnie z EN 1706:2011; analogia stopu A356 według Aluminium Association). W odniesieniu do powszechnie znanego i stosowanego zabiegu chłodzenia zanurzeniowego (I, ang. immersing) podczas przesycania, w badaniach wykorzystywano również mikrostrumieniowy (M, ang. micro-jet) system chłodzenia. Po przesycaniu – metodą chłodzenia zanurzeniowego lub mikrostrumieniowego – próbki doświadczalne poddawane były także sztucznemu starzeniu w trzech różnych wariantach: S1, S2 i S3. Uzyskiwane wyniki były porównywane z właściwościami mechanicznymi stopu w stanie po odlaniu (stan F, ang. fabrication). Próbki z doświadczalnego stopu poddane mikrostrumieniowemu chłodzeniu przy przesycaniu miały w zasadzie podobne właściwości mechaniczne w stosunku do właściwości próbek chłodzonych zanurzeniowo i tylko w niektórych przypadkach mikrostrumieniowe chłodzenie dawało lepsze wyniki. Dalsze prace w tym obszarze powinny dotyczyć konstruowania urządzeń do mikrostrumieniowego chłodzenia o ciśnieniach wody znacznie przewyższających ciśnienie sieci wodociągowej, tj. do poziomu nawet kilkuset barów.

6

Development of strength and electrical properties of Al-Si-Mg casting aluminum alloys with an Mg content of 1 wt%

Knych T., Wiecheć J., Uliasz P.

Metallurgy and Foundry Engineering

|

2016

|

Vol. 42, no. 1

47--56

EN

Silumins (i.e., alloys where the main alloy additive is silicon) are the largest casting aluminum alloy group. Materials of this kind are characterized by high strength properties, high corrosion resistance, and low density, which make it possible to use them for construction purposes. A new group of developed properties typical for casting silumins are electrical and thermal conductivity. Thermal and electrical conductivity can be optimized by the suitable selection of chemical composition of the alloy, in the process of precipitation hardening, or by means of a combination of both. The present paper includes test results of the strength and electrical properties of AlSiMg casting aluminum alloys. The alloys that were subject to testing were AlSi5Mg1, AlSi7Mg1, and AlSi11Mg1. Heat treatment included homogenization at a temperature of 535°C over a time period of 8 h, quenched, and artificial aging. The strength tests involved a Brinell hardness measurement as well as an electrical properties test involving electrical conductivity measurement tests.

PL

Siluminy, czyli stopy aluminium z głównym dodatkiem stopowym w postaci krzemu, stanowią jedną z największych grup odlewniczych stopów aluminium. Materiały tego rodzaju charakteryzują się między innymi wysokimi własnościami wytrzymałościowymi, wysoką odpornością na działanie środowiska korozyjnego czy niskim ciężarem właściwym, co pozwala na ich stosowanie w celach konstrukcyjnych. Grupą własności odlewniczych stopów aluminium, nad którą aktualnie trwają intensywne badania są własności elektryczne oraz, powiązane z nimi, własności cieplne. Własności te można optymalizować przez odpowiedni dobór składu chemicznego stopów, wykorzystanie zjawiska utwardzania wydzieleniowego czy też w wyniku kombinacji obu metod. Niniejsza praca opisuje wyniki badań nad kształtowaniem własności wytrzymałościowych i elektrycznych odlewniczych stopów Al-Si-Mg. W badaniach wykorzystano trzy stopy o oznaczeniach AlSi5Mg1, AlSi7Mg1 oraz AlSi11Mg1. Materiały zostały poddane operacjom obróbki cieplnej w postaci homogenizacji w temperaturze 535°C przed 8 h, przesycaniu do wody oraz starzeniu sztucznemu. W ramach określenia własności wytrzymałościowych wykonano pomiary twardości analizowanych stopów przy użyciu metody Brinella. Własności elektryczne określono za pomocą pomiaru przewodności elektrycznej.

7

Wytrzymałość zmęczeniowa według Eurokodu 3 stali S235 starzonej samorzutnie i sztucznie

Wichtowski B.

Inżynieria i Budownictwo

|

2012

|

R. 68, nr 3

150-152

PL

Przedstawiono badania nieograniczonej wytrzymałości zmęczeniowej dwóch grup próbek ze stali S235 o zróżnicowanym starzeniu. Grupę pierwszą stanowiły próbki starzone samorzutnie przez 35 lat, a grupę drugą próbki dodatkowo starzone sztucznie. Dla tych próbek określono kategorie zmęczeniowe wg ČSN 731401:1998. Uzyskane wyniki porównano z kategoriami zmęczeniowymi zalecanymi przez Eurokod 3.

EN

Studies of endurance limit for two groups of specimens made of steel grade S235 with different aging are presented in this paper. The first group was formed by the specimens which had been naturally aged for 35 years while the other one – by specimens subjected to additional artificial aging. Fatigue classes for those specimens have been defined in compliance with ČSN 731401:1998 (Czech Standard) and then compared to relevant classes given in Eurocode 3.