Wyniki wyszukiwania - BazTech

1

An attempt to use „Tetra Pak” waste material in particleboard technology

Auriga Radosław, Borysiuk Piotr., Auriga Alicja

Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology

|

2021

|

No. 114

70--75

EN

An attempt to use „Tetra Pak” waste material in particleboard technology. The study investigates the effect of addition Tetra Pak waste material in the core layer on physical and mechanical properties of chipboard. Three-layer chipboards with a thickness of 16 mm and a density of 650 kg / m3 were manufactured. The share of Tetra Pak waste material in the boards was varied: 0%, 5%, 10% and 25%. The density profile was measured to determine the impact of Tetra Pak share on the density distribution. In addition, the manufactured boards were tested for strength (MOR, MOE, IB), thickness swelling and water absorption after immersion in water for 2 and 24 hours. The tests revealed that Tetra Pak share does not affect significantly the value of static bending strength and modulus of elasticity of the chipboard, but it significantly decreases IB. Also, it has been found that Tetra Pak insignificantly decreases the value of swelling and water absorption of the chipboards.

PL

Próba wykorzystania materiału odpadowego „Tetra Pak” w technologii płyt wiórowych. W ramach pracy zbadano wpływ udziału odpadowego materiału Tetra Pak w warstwie wewnętrznej płyt wiórowych na ich właściwości fizyczne i mechaniczne. Wytworzono trójwarstwowe płyty wiórowe o grubości 16 mm oraz gęstości 650 kg/m3 z 0%, 5%, 10% oraz 25% udziałem odpadowego materiału Tetra Pak. W celu określenia wpływu udziału Tetra Pak w płycie na rozkład gęstości zbadano profil gęstości. Ponadto wytworzone płyty zbadano pod katem właściwości wytrzymałościowych (MOR, MOE, IB) oraz określono spęcznienie oraz nasiąkliwość po 2 i 24 godzinach moczenia w wodzie. Przeprowadzone badania wykazały, że udział Tetra Pak nie wpływa istotnie statystycznie na wartość wytrzymałości na zginanie statyczne oraz moduł sprężystości wytworzonych płyt wiórowych. Wpływa jednak w istotny statystycznie sposób na spadek IB wytworzonych płyt. Ponadto zaobserwowano, że udział Tetra Pak w nieznacznym stopniu powoduje spadek wartości spęcznienia oraz nasiąkliwości jednak obniżenie tych właściwości nie jest istotne statystycznie.

2

Aluminum recovery from multimaterial Tetra-Pak waste pyrolysis

Klejnowska Katarzyna, Lewandowski Dariusz

Civil and Environmental Engineering Reports

|

2019

|

Vol. 29, no. 1

39--52

EN

A constant growth of the multimaterial waste production can be observed in the recent years. The multimaterial waste that contain aluminum are especially hard to process due to the fact that multiple layers of various materials are bonded permanently. Tetra-Pak waste contain high amounts of paper (approx. 70%) and are usually processed in papermills in order to recover cellulose. The overview on the methods used to process waste as well as the characteristics of the produced waste are presented in the paper. The application of pyrolysis has many advantages: the products are characterized by a high calorific value and can be used as fuels, and the process itself is much more environmentally friendly than the chemical methods used currently. The tests were performed with a special focus on the minimization of the aluminum oxidation level, so that in can be further processed. In order to determine the decomposition temperature of the individual components of the examined materials, the tests started with a thermogravimetric analysis of the pyrolysis process performed with the application of argon. The next step were the pyrolysis tests on a laboratory scale installation aimed in the verification of the results obtained during the thermogravimetry.

PL

Postępujący rozwój gospodarczy wiąże się z wytwarzaniem coraz większej ilości odpadów, w tym znacznej grupy odpadów wielomateriałowych. Odpady te składają się z co najmniej dwóch różnych materiałów, połączonych ze sobą w sposób trwały, co uniemożliwia ich rozdział za pomocą prostych metod mechanicznych. Opakowania Tetra-Pak składają się z siedmiu warstw celulozy (ok. 70%), polietylenu (ok. 25%) i aluminium (ok. 5%). W artykule zaprezentowano krótki przegląd metod stosowanych obecnie do przetwarzania tego typu odpadów. W ramach przeprowadzonych badań wykonano analizę termograwimetryczną w atmosferze argonu w celu określenia zakresów temperatur w których występuje ubytek masy oraz towarzyszących mu efektów termicznych. Następnie wykonano testy pirolizy w skali laboratoryjnej i określono zawartość glinu w produktach stałych oraz stopień jego utlenienia w materiale przed oraz po procesie pirolizy.

3

Energooszczędne przygotowanie mas papierniczych z surowców trudno rozwłóknialnych

Biel-Tyralska A., Tyralski T.

Przemysł Chemiczny

|

2015

|

T. 94, nr 9

1491-1495

PL

Przedstawiono wyniki doświadczalnych badań procesu przygotowania mas papierniczych z wielomateriałowych pojemników kartonowych po płynach spożywczych (np. firmy Tetra Pak), których liczba bardzo szybko wzrasta. Stwierdzono, że rozdrabnianie pojemników musi przebiegać selektywnie, tak aby warstwa kartonowa ulegała rozdrobnieniu na włókna, a folie pozostały nierozdrobnione i pozbawione włókien, co umożliwia odzysk aluminium. Zastosowano technologię frakcjonowania włókien, z wykorzystaniem innowacyjnej maszyny sortującej i pompującej, zbudowanej wg własnej koncepcji, w celu rozdzielenia masy na frakcję długowłóknistą i krótkowłóknistą.

EN

Multi-layer beverage packagings were shredded to intensify edgewise H₂O penetration and slushed in a pulper with helical rotor to produce a fibre stock with concn. 10%. An increase in av. fiber length from 1.55 mm up to 1.95 mm was achieved after fractionation of the stock.

4

Recykling materiałowy odpadów TETRA-PAKU

Korniejenko K., Kuciel S., Mikuła J.

Czasopismo Techniczne. Mechanika

|

2009

|

R. 106, z. 1-M

181-185

PL

Artykuł opisuje możliwości recyklingu odpadów z Tetra Paku. Opisana jest możliwość wytwarzania materiału kompozytowego z odpadów z Tetra Paku. Artykuł prezentuje rezultaty próby wytrzymałościowej dla próbek z wytworzonego kompozytu, jest omówiony wpływ ciśnienia, temperatury i dodatku polietylenu na własności mechaniczne próbek.

EN

This paper describes one of the possibilities of recycling waste from Tetra Pak. It presents the results of strength tests conducted on Tetra-Pak waste samples. The most important influence on mechanical properties of this composite had pressure, temperature and polyethylene addition.