This article presents joining methods (welding and sealing) of single-polymer composite materials in a hot air stream. The research material was created using the film-stacking method, which involves pressing successive fractions of polyethylene terephthalate-modified with glycol (PET-G) at defined technological conditions, such as pressure, temperature, and time. Joining method analysis was carried out based on the tensile test results. Analysis of the obtained results showed that the properties of the overlapped weld joint were the best because they were closest to the original materials. In contrast, PET-G welded joint properties were the worst because the PET-G welded joint does not contain fibers, which enhanced the weld; therefore, the fastest breakage of the material was observed at the welding location. For the overlapped weld, the weld itself is more resistant because the joint surface is influenced by friction forces between joined materials.
W pracy przedstawiono proces recyklingu materiałowego odpadowej folii z poli(tereftalanu etylenu) modyfikowanej glikolem (PET-G) do postaci regranulatu. Po zmyciu nadruku i wysuszeniu, folia została poddana procesowi wytłaczania w warunkach laboratoryjnych, co pozwoliło na uzyskanie jednorodnego regranulatu. Zbadano stabilność termiczną przy zastosowaniu analizy termograwimetrycznej TGA, a także temperaturę zeszklenia metodą skaningowej kalorymetrii różnicowej DSC. Zaobserwowano, iż niezmycie nadruku obniża stabilność termiczną folii, która to jest również niższa dla regranulatów, w odniesieniu do bazowego granulatu PET-G. Lepkosprężyste właściwości materiałów zostały zbadane przy użyciu reometru oscylacyjnego. Lepkość folii odpadowej była nieznacznie niższa niż dla regranulatów z kolei zależność ich modułu zachowawczego i stratności była identyczna jak dla wyjściowego PET-G.
EN
In this paper, a recycling process of post-consumer poly(ethylene terephthalate) modified with ethylene glycol (PET-G) towards regranulate pellets was described. After prints washing and drying, foil was extruded in a lab conditions what allows to obtain uniform regranulate pellets. The thermal stability and glass transition temperature were examined using thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC), respectively. It was found that thermal stability is decreased in the presence of prints and also lower for PET-G regranulates than for starting PET-G. Viscoelastic properties were analyzed by an oscillatory rheometer. The viscosity of post-consumer foil was slightly lower than for regranulates while their dependence between storage and loss modulus was the same as for starting PET-G.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.