Primary and secondary crystallization of modified hypoeutectic chromium cast iron

Studnicki A., Kilarski J.

Archives of Foundry Engineering

|

2010

|

Vol. 10, iss. 2

163--168

EN

The paper presents investigations of crystallization of modified hypoeutectic wear resistant chromium cast iron which contains carbon about 2% and chromium on three levels (12%, 18% and 25%). Three substances were applied to the modification (boron carbide (B4C), ferroniobium (FeNb) and mixture of ferroniobium and mischmetal (RE)). The investigations of crystallization were conducted the DTA method in DTA-C and DTA-Is testers. The influence on the course of the process of primary and secondary crystallization was observed.

2

Struktura żeliwa nadeutektycznego modyfikowanego kompleksowo dodatkami zawierającymi bizmut i cer.

Warchala T., Soiński M.S.

Archiwum Nauki o Materiałach

|

2001

|

T. 22, nr 2

145-157

PL

W artykule omówiono wyniki badań nad wpływem małych dodatków bizmutu (od 0,0006% do 0,0017%) i ceru (od 0,010% do 0,043%), wprowadzonych jako modyfikatory do żeliwa nadeutektycznego (Sc od 1,02 do 1,09), na charakterystyki grafitu oraz udział ferrytu w osnowie. Stwierdzono, że następuje zmniejszenie udziału grafitu, obwodu i liczby jego wydzieleń oraz zmiana postaci z płatkowej na zwartą. Udział ferrytu w osnowie wzrasta z udziału śladowego do ponad 80%. Optymalny pozimo zawartości bizmutu wynosi od 0,0007% do 0,0010%. Udział ceru powinien odpowiadać stosunkowi Ce/Bi w granicach 25-50.

EN

The paper discusses results of investigation concerning the influence of small additions of bismuth (from 0,0006% to 0,0017%) and cerium (from 0,010% to 0,043%) introduced as modifiers into the hypereutectic cast iron (Sc from 1,02 to 1,09) on the graphite characteristics and the fraction of ferrite in the matrix. Having performed the statistic analysis of experimental results, the authors have graphically determined the relationships between the bismuth and cerium content and the examined structure parameters. It has been found that the graphite percentage has decreased, as well as the total perimeter, the number of its precipitates, and the shape of graphite changes from flake to compact ones. The ferrite in the matrix increases from trace amounts to over 80%. It has been also noticed that for the hypereutectic cast iron the advantageous changes in the parameters of structure are related to the proportion of cerium to bismuth content. The optimum level of bismuth content falls within in range from 0,0007% to 0,0010%. The cerium should correspond to the Ce/Bi proportion equal to 25-50.

3

Wpływ zawartości bizmutu i ceru po modyfikacji kompleksowej na właściwości mechaniczne żeliwa nadeutektycznego

Warchala T., Soiński M. S.

Krzepnięcie Metali i Stopów

|

2000

|

R. 2, nr 43

517--522

PL

Żeliwo nadeutektyczne (Sc=1,05) poddano jednoczesnej modyfikacji dodatkami FeSiCaBi (rozchód od 0,2% do 0,5%) oraz FeSiMZR (rozchód od 0,14% do 0,36%). Otrzymane żeliwo wykazywało osnowę ferrytyczną i ferrytyczno-perlityczną ze zwartymi wydzieleniami grafitu - od wermikularnego do kulkowego włącznie. Stwierdzono ponad sześciokrotny wzrost wytrzymałości na rozciąganie i umownej granicy plastyczności oraz ponad pięciokrotny wzrost wydłużenia względnego. Jedynie twardość Brinella zwiększyła się zaledwie o około 20 jednostek, nie przekraczając poziomu 170 HBS. Analiza statystyczna wykazała istnienie wyraźnych zależności między zawartością bizmutu i ceru w osnowie a wymienionymi wcześniej właściwościami mechanicznymi. Ustalone relacje mają charakter zbliżony do funkcji parabolicznych z tym, że w przypadku bizmutu występuje maksimum właściwości przy zawartości 0,0008% do 0,0010% Bi. Optymalna zawartość śladowych ilości Bi i Ce powinna odpowiadać stosunkowi ilościowemu ceru do bizmutu w granicach 30-45.