The effect of tri(1-chloro-3-etoxy-propane-2-ol) borate on the properties of rigid polyurethane-polyisocyanurate foams

Czupruński B., Paciorek-Sadowska J., Liszkowska J.

Polimery

2002

T. 47, nr 10

727-729

Tri(1-chloro-3-etoxy-propane-2-ol) borate (1) was obtained by reaction of tri(hydroxyethyl) borate and epichlorohydrin. Reaction product was applied as fire retardant for preparation of rigid polyurethane-polyisocyanurate foams. As the W content was increased from 0.1 to 0.4 of the chemical equivalent, the compressive strength, oxygen index, residue after combustionand content of closed cells rose but brittleness, softening point and water absorption decreased. However, W presence does not influence explicitly on the foam apparent density. The results of our studies showed that chloroboroorganic compound [ChBOC, (I)] is generally useful as an additive to improve the properties of rigid PUR-PIR foams.

Boran tri(2[3-chloro-2-hydroksy-l-propoksy]etylul (I) o wzorze B(OCH2CH2OCH2CHOHCH2C1)3 otrzymano w wyniku reakcji boranu tris(hydroksyetylowego) z epichlorohyd-ryną i zastosowano go jako środek uniepalniający w syntezie sztywnych pianek PUR-PIR (tabela 1). Zwiększenie zawartości 1 w wyjściowej kompozycji z 0,1 do 0,4 równoważnika chemicznego powoduje wzrost wytrzymałości na ściskanie (rys. 1), wskaźnika tlenowego, pozostałości po spaleniu i zawartości komórek zamkniętych (tabela 1) oraz spadek kruchości (rys. 1), temperatury mięknienia i chłonności wody (tabela 1). Obecność I nie wpływa natomiast w sposób jednoznaczny na gęstość pozorną pianek (tabela 1). Wyniki badań wskazują na przydatność I jako dodatku polepszającego właściwości sztywnych pianek PUR-PIR.

The effect of tri(2-hydroxypropyl) borate on the properties of rigi polyurethane-polyisocyanurate foams

Czupruński B., Paciorek J.

Polimery

1999

T. 44, nr 7-8

552-554

Tri(2-hydroxypropyl) borate was prepared from boric acid and 1,2-propanediol and its properties were determined by IR and NMR techniques; density, viscosity, hydroxy number, and molecular weight were also measured. The compound was used as a flame retardant for rigid polyurethane-polyisocyanurate foams (Tables 1, 2). As the borate content was increased from 0.1 to 0.4 of the chemical equivalent, the compressive strength and retention rose but the softening point and brittleness fell; the oxygen index increased but slightly. The borate is generally useful as an addition to improve the properties of the foams examined.

Boran tri-(hydroksypropylu) otrzymano w wyniku reakcji kwasu borowego z 1,2-propanodiolem. Produkt zastosowano w sztywnych piankach poliuretanowo-poliizocyjanuranowych (tabele l i 2). Zwiększanie dodatku boranu od 0,1 do 0,4 równoważnika chemicznego powoduje wzrost wytrzymałości pianek na ściskanie i zwiększenie masy pozostałości po spalaniu (tabela 2), oraz spadek temperatury topnienia i kruchości; indeks tlenowy prawie nie ulega przy tym zmianie. Ogólnie biorąc, wpływ boranu jako dodatku na właściwości pianek okazał się pozytywny.