The effect of preparation method on pigmentary properties of manganese doped cassiterite pigments

Karolová L., Dohnalová Ż., Luxová J.

Materiały Ceramiczne

2016

T. 68, nr 3

199--203

The presented work deals with the possibility of synthesis of blue-violet cassiterite pigments, in which a part of tin ions was substituted by cobalt and manganese ions. In this case, phosphorous is used as a charge-compensating element. The compounds with the formula Sn0.752Co0.08P0.16Mn0.008O2 were prepared by solid state reaction, using the classical ceramic method, and also the method of mechanical activation. The goal was to develop conditions for synthesis and the most suitable preparation method of these pigments. The temperature range was chosen from 1350 °C to 1500 °C. The synthesised pigments were characterised in terms of colour properties after their application into the transparent ceramic glaze P 074 91 and into the organic binder. They were also studied with respect to their phase composition as well as the particle size distribution.

Prezentowana praca poświecona jest możliwości syntezy niebieskofioletowago pigmentu kaserytowego, w którym część jonów cynowych podstawiono jonami kobaltu i manganu. W tym przypadku fosfor użyto jako pierwiastek kompensujący ładunek. Związki o wzorze Sn0,752Co0,08P0,16Mn0,008O2 przygotowano w drodze reakcji w fazie stałej, wykorzystując klasyczną metodę ceramiczną, a także metodę mechanicznej aktywacji. Cele było opracowanie warunków syntezy i najbardziej odpowiedniej metod wytwarzania tych pigmentów. Wybrano zakres temperatury od 1350 °C do 1500 °C. Pigmenty scharakteryzowano w odniesieniu do właściwości barwnych po zastosowaniu ich w przezroczystym ceramicznym szkliwie P 074 91 i organicznym lepiszczu. Zbadano również ich skład fazowy i rozkład wielkości cząstek.

Study of ceramic pigments with perovskite structure

Dohnalová Ż., Sulcová P., Gorodylova N.

Materiały Ceramiczne

2016

T. 68, nr 3

188--192

Our attention was focused on preparation of inorganic pigments based on the perovskite structure of SrSnO3, in which part of tin ions was substituted by ions of terbium and titanium or terbium and cerium. The particle size (d50) of all pigments is between 2-3 μm. Powders with the general formula SrSn0.6-xTixTb0.4O3, where x = 0.1-0.6, provide an intensive yellow colour hue in application into an organic binder, and white glossy surfaces in application into a ceramic glaze. A SrSn0.4Ti0.2Tb0.4O3 sample offers the best colour parameters in application into the organic binder: the highest amount of yellow hue (b* = 58.95) and the highest saturation (C = 59.05). Powders with the general formula SrSn0.6-xCexTb0.4O3, where x = 0.1-0.6, also provide an intensive yellow colour hue in application into the organic binder and dark yellow-orange glossy surfaces in application into the ceramic glaze. The most interesting yellow colour hue has powder SrSn0.4Ce0.2Tb0.4O3 applied into the organic binder. In application into the ceramic glaze, an increase of cerium ions content in pigment shifts the hue from yellow to dark orange.

Uwagę skupiono na przygotowaniu nieorganicznych pigmentów opartych na perowskitowej strukturze SrSnO3, w której część jonów cyny podstawiono jonami terbu i tytanu lub terbu i ceru. Rozmiar cząstek (d50) wszystkich pigmentów mieścił sie pomiędzy 2-3 μm. Proszki o wzorze ogólnym SrSn0.6-xTixTb0.4O3, gdzie x = 0.1-0.6, dostarczają intensywny odcień koloru żółtego w zastosowaniu do spoiwa organicznego i białe połyskujące powierzchnie w zastosowaniu do szkliwa ceramicznego. Próbka SrSn0.4Ti0.2Tb0.4O3 oferuje najlepsze parametr barwne w zastosowaniu do spoiwa organicznego: największy udział odcienia żółtego (b* = 58.95) i największe nasycenie (C = 59.05). Proszki o wzorze ogólnym SrSn0.6-xCexTb0.4O3, gdzie x = 0.1-0.6, również dostarczają intensywny odcień koloru żółtego w zastosowaniu do spoiwa organicznego i ciemne żółto-pomarańczowe powierzchnie w zastosowaniu do szkliwa ceramicznego. Najbardziej interesujący odcień koloru żółtego ma proszek SrSn0.4Ce0.2Tb0.4O3 zastosowany do spoiwa organicznego. W zastosowaniu do szkliwa ceramicznego wzrost stężenia jonów ceru w pigmencie przesuwa odcień żółty do ciemnopomarańczowego.