The Effect of Gas Pressure on Powder Size and Morphology in The Production of AZ91 Powder by Gas Atomization Method

Akkaş M., Çetin T., Boz M.

Archives of Metallurgy and Materials

2018

Vol. 63, iss. 4

1587--1594

In this study, the effect of gas pressure on the shape and size of the AZ91 alloy powder produced by using the gas atomization method was investigated experimentally. Experiments were carried out at 820°C constant temperature in 2-mm nozzle diameter and by applying 4 different gas pressures (0.5, 1.5, 2.5 and 3.5 MPa). Argon gas was used to atomize the melt. Scanning electron microscope (SEM) to determine the shape of produced AZ91 powders, XRD, XRF and SEM-EDX analysis to determine the phases forming in the internal structures of the produced powders and the percentages of these phases and a laser measuring device for powder size analysis were used. Hardness tests were carried out to determine the mechanical properties of the produced powders. The general appearances of AZ91 alloy powders produced had general appearances of ligament, acicular, droplet, flake and spherical shape, but depending on the increase in gas pressure, the shape of the powders is seen to change mostly towards flake and spherical. It is determined that the finest powder was obtained at 820°C with 2 mm nozzle diameter at 3.5 MPa gas pressure and the powders had complex shapes in general.

Effect of boron on micro structure and microhardness properties of Mo-Si-B based coatings produced viatig process

Islak S., Özorak C., Sezgin C. T., Akkaş M.

Archives of Metallurgy and Materials

2016

Vol. 61, iss. 3

1515--1520

In this study, Mo-Si-B based coatings were produced using tungsten inert gas (TIG) process on the medium carbon steel because the physical, chemical, and mechanical properties of these alloys are particularly favourable for high-temperature structural applications. It is aimed to investigate of microstructure and microhardness properties of Mo-Si-B based coatings. Optical microscopy (OM), X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to characterize the microstructures of Mo-Si-B based coatings. The XRD results showed that microstructure of Mo-Si-B coating consists of α-Mo, α-Fe, Mo2B, Mo3Si and Mo5SiB2 phases. It was reported that the grains in the niicrostructure were finer with increasing amounts of boron which caused to occur phase precipitations in the grain boundary. Besides, the average microhardness of coatings changed between 735 HV0.3 and 1140 HV0.3 depending on boron content.