Single Polymer Composite Yarns and Films Prepared from Heat Bondable Poly(lactic acid) Core-shell Fibres with Submicron Fibre Diameters

Kriel H., Sanderson R. D., Smit E.

Fibres & Textiles in Eastern Europe

2013

Vol. 21, no. 4 (100)

44--47

Mats of core-shell fibres of semi-crystalline poly(L-lactic acid) (core) and amorphous poly(D,L-lactic acid) (shell) produced through coaxial electrospinning were used to prepare fibre reinforced single polymer composite yarns and films. The internal molecular arrangement (fine structure) within the fibres and the potential to enhance the crystallinity of the core and heat-bond neighbouring fibres within the thermal operating window, between where the shell components fused and the melting point of the core components, were investigated. Thermal treatments were shown to increase the crystallinity and mechanical strength of the composite yarns.

Za pomocą współosiowego elektroprzędzenia wyprodukowano runa z włókien typu rdzeń-otoczka o strukturze składającej się z półkrystalicznego i amorficznego kwasu polimlekowego, które następnie wykorzystano do produkcji kompozytu. Badano wewnętrzną strukturę cząsteczkową włókien i zdolność do polepszenia krystaliczności rdzenia oraz możliwości termicznego łączenia sąsiednich włókien przez zmianę właściwości otoczki. Stwierdzono, że obróbka termiczna powoduje wzrost krystaliczności i wytrzymałości mechanicznej przędz kompozytowych.

Coaxial Electrospinning of Miscible PLLA-Core and PDLLA-Shell Solutions and Indirect Visualisation of the Core-Shell Fibres Obtained

Kriel H., Sanderson R. D., Smit E.

Fibres & Textiles in Eastern Europe

2012

Vol. 20, no. 2 (91)

28-33

Core-shell fibres of semi-crystalline poly(L-lactic acid) (PLLA) (core) and amorphous poly(D,L-lactic acid) (PDLLA) (shell) were produced through the coaxial electrospinning of two miscible solutions. Due to the poor contrast between the PDLLA and PLLA, the core-shell structure of the resulting fibres could not be elucidated using TEM. An indirect visualisation method was devised consisting of a combination of SEM, selective dissolution, polarimetry and DSC. The method is evaluated here and applied in the investigation of the effect of spin solution concentration and flow rate on the morphology of the resulting fibers.

W procesie współosiowego elektroprzędzenia uzyskiwano włókna typu rdzeń-otoczka stosując roztwory ulegające mieszaniu. Na rdzeń stosowano roztwory częściowo krystalicznego poli-(L-kwasu mlekowego), a na otoczkę roztwory amorficzne poli-(D,L-kwasu mlekowego). W wyniku nieznacznych różnic pomiędzy dwoma roztworami nie można było dokonać oceny techniką TEM. Zastosowano pośrednia metodę identyfikacji przy użyciu SEM, selektywnej rozpuszczalności, polarymetrii, różnicowej kalorymetrii skaningowej (DSC). Badano wpływ stężenia roztworów i szybkości ich podawania na morfologię otrzymywanych włókien.