Dynamic Mechanical Analysis of Nylon 66 Cord Yarns

Demšar A., Bukošek V., Kljun A.

Fibres & Textiles in Eastern Europe

2010

Vol. 18, no. 4 (81)

29--34

The viscoelastic properties of three different nylon cord yarns were analysed, and the dependence on the temperature of the annealing process was examined with the use of dynamic mechanical analysis (DMA). The research showed that the initial moduli of temperature-treated nylon cord yarns in a clamped state decrease after temperature treatment. The results also demonstrated that it is recommended to perform the vulcanisation of rubber composites at temperatures between 160 °C and 180 °C, where segmental motion is at minima. Likewise, it is not recommended to mechanically load cord yarns between 90 °C to 130 °C. This study demonstrated that DMA can be used to analyse the viscoelastic properties of cord yarns, which enables us to detect subtle differences between different materials and to interpret changes in the material at a supermolecular level. DMA can aid in determining optimal process conditions and materials.

Przeprowadzono analizę właściwości lepko-sprężystych trzech różnych rodzajów przędz nylonowych oraz zbadano zależności temperaturowe procesu wygrzewania stosując dynamiczną analizę parametrów mechanicznych. Na podstawie uzyskanych Wyników można zasugerować, że proces wulkanizacji kompozytów kauczukowych należy przeprowadzać w temperaturze 160 °C – 180 °C. Jednocześnie nie powinno się obciążać kordów poliamidowych w temperaturach 90 °C – 130 °C. Badania wykazały, że metoda ta może być stosowana do analizy lepko-sprężystych właściwości przędz kordowych i pozwala na wykrywanie nieznacznych różnic pomiędzy materiałami.

The Behaviour of Fabric with Elastane Yarn During Stretching

Gorjanc D. Š., Bukošek V.

Fibres & Textiles in Eastern Europe

2008

Vol. 16, no. 3 (68)

63--68

This paper presents an investigation into the behaviour of fabric with elastane yarn during stretching. The aim of the research was to study the viscoelastic part of the stress-extension curve and behaviour of fabrics with elastane yarn after one hour stretching above the yield point. Research results of the viscoelastic part of the stress-extension curve show low values of stress and extension in the yield point (extension at the yield point is from 0.25% to 0.75%), which means a larger area of the viscoelastic behaviour of the fabrics was analysed. The results of research into the viscoelastic properties of fabrics with elastane yarn also show greater differences in viscoelastic properties on the stress-extension curve above the yield point, which means that the elastane in the yarn had started to affect the viscoelastic properties, with an extension which is higher than the one at the yield point. The results of the research also show that elastic extension after one hour of stretching the fabric to the specified extension of 25% is higher than the extension at the yield point, which moves between 22.2% and 24.1%. This figure is considered to be very high.

Opisano badania nad zachowaniem się tkanin z udziałem przędz elastomerowych podczas rozciągania. Celem badań było określenie lepko-sprężystej części krzywej naprężeniewydłużenie oraz zachowanie się tkanin z udziałem elastomerowych przędz po jednej godzinie rozciągu powyżej punktu mięknięcia. Wyniki badań krzywych rozciągania pokazały małe wartości naprężeń i wydłużeń w punkcie mięknięcia (wydłużenie w punkcie mięknięcia wynosiło od 0,25% do 0,75%), co oznacza duży obszar lepko-sprężystego zachowania się tkanin. Zaobserwowano również duże różnice właściwości lepko-sprężystych w obszarze krzywej rozciągania powyżej punktu mięknięcia, co oznacza, że udział elastomeru w przędzy wpływa wydatnie na krzywą rozciągu powodując osiągnięcie rozciągów znacznie większych od odpowiadających punktowi mięknięcia. Wyniki badań wskazują również, że sprężyste wydłużenie po jednej godzinie rozciągu tkaniny do określonej wartości 25% jest większe, niż wydłużenie odpowiadające punktowi mięknięcia, które jest zawarte pomiędzy 22,2% i 24,1%